A kind of vulcanization-resistant LED encapsulation silicone with high refractive index and high toughness

A technology of LED encapsulation and high refractive index, used in adhesives, polymer adhesive additives, non-polymer adhesive additives, etc., can solve the problem of low relative content of silicone resin, unsatisfactory bonding effect, and easy bonding interface. Damage and other problems, to achieve the effects of excellent substrate adhesion, increased hardness, and increased crosslinking density

Active Publication Date: 2018-02-06
YANTAI DARBOND TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, although the refractive index of domestic high-refractive index LED packaging silica gel can reach between 1.50 and 1.55, due to the common use of silicone resin, vinyl silicone oil, hydrogen-containing silicone oil, etc. in formula design, the relative content of silicone resin is low, and the crosslinking density Low, and the bonding effect is not ideal, so it leads to poor vulcanization resistance, easy to damage the bonding interface, etc., while high silicone resin content, high cross-linking density LED packaging silicone has improved vulcanization resistance, but because of its high internal stress , will lead to the reduction of the toughness of the material, and the phenomenon of dead light, cracking of the packaging material, and failure of the bonding interface will occur during the use of high and low temperature cold and heat shocks.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of vulcanization-resistant LED encapsulation silicone with high refractive index and high toughness
  • A kind of vulcanization-resistant LED encapsulation silicone with high refractive index and high toughness
  • A kind of vulcanization-resistant LED encapsulation silicone with high refractive index and high toughness

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] 1. Raw material

[0038] Methylphenyl vinyl silicone resin: (ViMe 2 SiO 1 / 2 ) (PhSiO 3 / 2 ) 5 ;

[0039] Vinyl dimethyl diphenyl polysiloxane: (ViMe 2 SiO 1 / 2 ) 10 (ViMePh 2 SiO 1 / 2 ) 10 ;

[0040] The platinum series catalyst is a platinum-methylphenyl polysiloxane complex;

[0041] Methylphenyl hydrogen silicone resin: (HMe 2 SiO 1 / 2 ) 3 (MePhSiO 1 / 2 ) 5 (PhSiO 3 / 2 ) 4 ;

[0042] Hydrogen-terminated diphenyl polysiloxane: (HMe 2 SiO 1 / 2 ) 1 (Ph 2 SiO 1 / 2 ) 4 ;

[0043] The inhibitor is ethynylcyclohexanol.

[0044] 2. Preparation method

[0045]Preparation of component A: Weigh 80 parts of methylphenyl vinyl silicone resin, 18 parts of vinyl dimethyl diphenyl polysiloxane, 0.1 part of platinum catalyst, and 2.9 parts of adhesive, and add them into the mixer in turn for mixing Stir evenly for 3 hours to obtain the A component;

[0046] Preparation of component B: Weigh 40 parts of dimethyl diphenyl hydrogen-containing silicone resin, 59.8 pa...

Embodiment 2

[0049] 1. Raw material

[0050] Methylphenyl vinyl silicone resin: (ViMe 2 SiO 1 / 2 ) (PhSiO 3 / 2 ) 3.5 ;

[0051] Vinyl dimethyl diphenyl polysiloxane: (ViMe 2 SiO 1 / 2 ) 70 (ViMePh 2 SiO 1 / 2 ) 70 ;

[0052] The platinum series catalyst is a platinum-olefin complex;

[0053] Methylphenyl hydrogen silicone resin: (HMe 2 SiO 1 / 2 ) 3 (MePhSiO 1 / 2 ) 4 (PhSiO 3 / 2 ) 4 ;

[0054] Hydrogen-terminated diphenyl polysiloxane: (HMe 2 SiO 1 / 2 ) 1 (Ph 2 SiO 1 / 2 ) 5 ;

[0055] The inhibitor is 1,1,3-triphenyl-2-propyn-1-ol.

[0056] 2. Preparation method

[0057] Preparation of component A: Weigh 90 parts of methylphenyl vinyl silicone resin, 8 parts of vinyl dimethyl diphenyl polysiloxane, 0.3 parts of platinum catalyst, and 1.0 parts of adhesive, and add them to the mixer in turn and mix them Stir evenly for 5 hours to obtain the A component;

[0058] Preparation of component B: Weigh 60 parts of dimethyl diphenyl hydrogen-containing silicone resin, 39.7 parts of...

Embodiment 3

[0061] 1. Raw material

[0062] Methylphenyl vinyl silicone resin: (ViMe 2 SiO 1 / 2 ) 2 (PhSiO 3 / 2 ) 8 ;

[0063] Vinyl dimethyl diphenyl polysiloxane: (ViMe 2 SiO 1 / 2 ) 40 (ViMePh 2 SiO 1 / 2 ) 40 ;

[0064] The platinum series catalyst is a platinum-methylphenylpolysiloxane complex;

[0065] Methylphenyl hydrogen silicone resin: (HMe 2 SiO 1 / 2 ) 3 (MePhSiO 1 / 2 ) 6 (PhSiO 3 / 2 ) 4 ;

[0066] Hydrogen-terminated diphenyl polysiloxane: (HMe 2 SiO 1 / 2 ) 1 (Ph 2 SiO 1 / 2 ) 6 ;

[0067] The inhibitor is 1,1,3-triphenyl-2-propyn-1-ol.

[0068] 2. Preparation method

[0069] Preparation of component A: Weigh 85 parts of methylphenyl vinyl silicone resin, 9.8 parts of vinyl dimethyl diphenyl polysiloxane, 0.2 parts of platinum catalyst, and 5 parts of adhesive into the mixer in sequence, Mix for 4 hours and stir evenly to obtain the A component;

[0070] Preparation of component B: Weigh 50 parts of dimethyl diphenyl hydrogen-containing silicone resin, 49.9 p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
refractive indexaaaaaaaaaa
Login to View More

Abstract

The invention relates to LED packaging silica gel, in particular to LED packaging silica gel with high refractive index, and belongs to the technical field of adhesives. The high refractive index LED encapsulating silica gel of the present invention includes A component and B component, and the weight ratio of the A component to the B component is 10:1; wherein, the A component includes the following raw materials in parts by weight Components: 80-90 parts of methylphenyl vinyl silicone resin, 8-18 parts of vinyl dimethyl diphenyl polysiloxane, 0.1-0.3 parts of platinum catalyst, 1-5 parts of adhesive; The B component includes the following raw material components in parts by weight: 40-60 parts of methylphenyl hydrogen-containing silicone resin, 40-60 parts of terminal hydrogen-containing diphenyl polysiloxane, and 0.1-0.3 parts of inhibitor. The high-refractive-index LED packaging silica gel of the present invention has beneficial effects such as high hardness, vulcanization resistance, excellent adhesion, and excellent resistance to cold and heat shock.

Description

technical field [0001] The invention relates to LED packaging silica gel with high refractive index, in particular to LED packaging silica gel with high refractive index, vulcanization resistance and thermal shock resistance, and belongs to the technical field of adhesives. Background technique [0002] As LEDs become more and more widely used, the requirements for LED packaging materials are also getting higher and higher. At present, the packaging materials used in LED mainly include epoxy resin and organic silicon materials. Epoxy resin has excessive internal stress, yellowing, poor high and low temperature resistance, and poor aging resistance, while organic silicon materials have small internal stress and high and low temperature resistance. Good, non-yellowing, comprehensive performance is obviously better than epoxy resin, so it quickly replaces epoxy resin and is widely used in the field of LED packaging. The use of high-refractive silicone silica gel with a refract...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J183/07C09J183/05C09J11/08C09J11/06H01L33/56
Inventor 陈维庄恒冬王建斌陈田安
Owner YANTAI DARBOND TECH