Preparation method of olefin resin composition

A manufacturing method and technology of olefin resin, applied in the field of polyolefin products, can solve the problems of environmental pollution, urgency of flame retardant modification, etc., and achieve the effects of low cost, good flame retardant effect, and increased mixing affinity

Inactive Publication Date: 2015-12-30
LIAONING UNIVERSITY OF PETROLEUM AND CHEMICAL TECHNOLOGY
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, polyolefin resins are extremely flammable, so it is urgent to modify them with flame retardancy. The existing halogen flame retardants will cause serious environmental pollution. A new environmentally friendly flame retardant olefin resin composition The manufacturing method is subject to further research and development

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A kind of manufacture method of olefin resin composition of the present embodiment, comprises the following steps:

[0021] (1) the oxide of iron and the oxide of Mo are loaded on montmorillonite to prepare flame retardant;

[0022] (2) Blend the following components:

[0023] Polyethylene resin 100 parts

[0024] 4 parts of flame retardants that step (1) makes

[0025] 1 part of silane coupling agent

[0026] Under the condition of 80-100°C, mix at 1800 rpm and high speed for 15 minutes;

[0027] (3) After the materials are mixed and melted, they are extruded and granulated.

Embodiment 2

[0029] A kind of manufacture method of olefin resin composition of the present embodiment, comprises the following steps:

[0030] (1) loading iron oxide and Mo oxide on clay to prepare flame retardant;

[0031] (2) Blend the following components:

[0032] 100 parts of polypropylene resin

[0033] 8 parts of flame retardants that step (1) makes

[0034] Silane coupling agent 2 parts

[0035] Under the condition of 80-100°C, mix at 2000 rpm for 10 minutes at high speed;

[0036] (3) After the materials are mixed and melted, they are extruded and granulated.

Embodiment 3

[0038] A kind of manufacture method of olefin resin composition of the present embodiment, comprises the following steps:

[0039] (1) The oxides of iron and Mo are supported on aluminum oxide to prepare a flame retardant;

[0040] (2) Blend the following components:

[0041] 100 parts of poly-1-butene resin

[0042] 5 parts of flame retardants that step (1) makes

[0043] 1.5 parts of silane coupling agent

[0044] Under the condition of 80-100°C, mix at 2000 rpm for 10 minutes at high speed;

[0045] (3) After the materials are mixed and melted, they are extruded and granulated.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a preparation method of olefin resin composition. The preparation method comprises steps as follows: (1), an oxide of iron and an oxide of Mo are supported on a carrier, and a flame retardant is prepared; (2), 100 parts of polyolefin resin, 4-8 parts of the flame retardant prepared in the step (1) and 0.1-2 parts of a silicone coupling agent are mixed at a high speed of 1,800-2,000 r / m at the temperature ranging from 80 DEG C to 100 DEG C for 10-15 minutes; (3), the materials are mixed, melted, extruded and pelletized. The preparation method has the benefits that the olefin resin composition has good flame retardancy and is environment-friendly.

Description

technical field [0001] The invention belongs to the technical field of polyolefin products, in particular to a method for manufacturing an olefin resin composition. Background technique [0002] Polyolefin is a polymer compound formed by polyaddition reaction of olefin. Such organic polymers are usually composed of many identical or different simple olefin molecules (such as ethylene, propylene, 1-butene, 1-pentene, 1-hexene, 1-octene, 4-methyl-1-pentene Such as α-olefins and certain cycloolefins) are formed by polymerization. Common polyolefins include polyethylene and poly-1-butene. Polyolefins are mainly produced by high-pressure polymerization, low-pressure polymerization (including solution method, slurry method, bulk method, gas phase method) and other methods. [0003] Polyolefin resin has the characteristics of low relative density, good chemical resistance and water resistance; good mechanical strength and electrical insulation. It can be used in films, pipes, p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L23/12C08L23/20C08K9/12C08K3/22
CPCC08K9/12C08K3/22C08K5/54C08K2003/2255C08K2003/2265C08L2201/02C08L2201/22C08L2205/025C08L23/06C08L23/12C08L23/20
Inventor 刘姝王晓宁
Owner LIAONING UNIVERSITY OF PETROLEUM AND CHEMICAL TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com