Polishing paste for modifying and processing plastic product

A technology of plastic products and polishing paste, which is applied in the field of plastic product processing, can solve the problems of affecting product appearance, increasing scrap rate, excessive polishing, etc., and achieve the effects of improving polishing effect, preventing excessive polishing, and protecting dimensional accuracy

Active Publication Date: 2016-01-06
YINGSHANG LONGYUYANG IND & TRADE
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Generally, a polishing machine is used for polishing. Since the polishing wheel is in direct contact with the surface of the plastic product, it is prone to over-polishing or insufficient polishing.
Excessive polishing will directly affect the appearance of the product and waste raw materials, while insufficient polishing will increase the scrap rate, thereby increasing input costs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] (1) Firstly put 80 parts of modified bentonite, 25 parts of zeolite powder and 15 parts of fly ash in an oven at 70-75°C to dry for 12 hours, then calcined at 350°C for 3 hours, and then calcined at 550°C for 2 hours , to obtain the mixed powder;

[0017] (2) Add 30 parts of soap powder and 18 parts of tea seed powder to 50 parts of ethanol, then ultrasonically treat for 20 minutes at an ultrasonic frequency of 22kHz and a power of 100W, then add 12 parts of tung oil, 10 parts of modified microcrystalline paraffin, and 7 parts of vaseline and 5 parts of beef tallow, the mixture was heated to 60-65 ° C and stirred for 15 minutes to obtain material I;

[0018] (3) Add 15 parts of rapeseed cake powder, 8 parts of activated carbon and 8 parts of silicon micropowder mixed powder into 300 parts of water, add material I after standing for 15 minutes, transfer to ball mill after mixing evenly, and ball mill until the fineness is less than 0.1mm, Finally, heat and concentrate u...

Embodiment 2

[0022] (1) Firstly put 85 parts of modified bentonite, 30 parts of zeolite powder and 18 parts of fly ash in an oven at 75-80°C to dry for 12 hours, then calcined at 350°C for 3 hours, and then calcined at 500°C for 2 hours , to obtain the mixed powder;

[0023] (2) Add 35 parts of soap powder and 15 parts of tea seed powder to 55 parts of ethanol, then ultrasonically treat for 20 minutes at an ultrasonic frequency of 22kHz and a power of 100W, then add 15 parts of tung oil, 12 parts of modified microcrystalline paraffin, and 8 parts of vaseline and 7 parts of tallow, the mixture was heated to 60-65 ° C and stirred for 15 minutes to obtain material I;

[0024] (3) Add 18 parts of rapeseed cake powder, 10 parts of activated carbon and 8 parts of silicon micropowder mixed powder into 350 parts of water, add material I after standing for 15 minutes, transfer to ball mill after mixing evenly, and ball mill until the fineness is less than 0.1mm, Finally, heat and concentrate until...

Embodiment 3

[0028] (1) First, put 90 parts of modified bentonite, 30 parts of zeolite powder and 20 parts of fly ash in an oven at 75-80°C to dry for 12 hours, then calcined at 350°C for 3 hours, and then calcined at 550°C for 2 hours , to obtain the mixed powder;

[0029] (2) Add 35 parts of soap powder and 18 parts of tea seed powder to 60 parts of ethanol, then ultrasonically treat at 22kHz and power of 100W for 20min, then add 16 parts of tung oil, 15 parts of modified microcrystalline paraffin, and 10 parts of vaseline and 8 parts of tallow, the mixture was heated to 60-65 ° C and stirred for 15 minutes to obtain material I;

[0030] (3) Add 20 parts of rapeseed cake powder, 12 parts of activated carbon and 8 parts of silicon micropowder mixed powder into 350 parts of water, add material I after standing for 15 minutes, transfer to ball mill after mixing evenly, and ball mill until the fineness is less than 0.1mm, Finally, heat and concentrate until the water content is 12-15%.

[...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a polishing paste for modifying and processing a plastic product, and relates to the technical field of processing a plastic product. The polishing paste is prepared from the following raw materials, by weight: 80-90 parts of modified bentonite, 30-35 parts of soap powder, 25-30 parts of zeolite powder, 15-20 parts of fly ash, 15-20 parts of rape seed cake powder, 13-18 parts of tea seed powder, 12-16 parts of tung oil, 10-15 parts of modified microcrystalline wax, 8-12 parts of active carbon, 8-12 parts of silica powder, 6-10 parts of vaseline, 5-8 parts of tallow, 50-60 parts of ethanol, and 300-350 parts of water. According to the invention, the polishing paste for modifying and processing a plastic product is prepared by taking modified bentonite as a main raw material, and can be directly coat the surface of the plastic product. The polishing effect can be effectively improved; the dimension accuracy of the plastic product can be furthest protected; and over polishing is prevented.

Description

Technical field: [0001] The invention relates to the technical field of plastic product processing, in particular to a polishing paste for plastic product modification and processing. Background technique: [0002] Plastic products are a general term for daily necessities and industrial products processed with plastic as the main raw material. Including plastic as raw material for injection molding, blister and other products of all processes. The production of plastic products generally includes plastic ingredients, molding, machining, joining, modification and assembly. The last four processes are carried out after the plastic has been formed into finished products or semi-finished products, also known as plastic secondary processing. In the finishing process, it is necessary to remove cold scars, spots and trace waste edges on the surface of plastic products by polishing. Generally, a polishing machine is used for polishing. Since the polishing wheel is in direct conta...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09G1/08
Inventor 李传云
Owner YINGSHANG LONGYUYANG IND & TRADE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap