Novel antistatic fabric special for infant clothes and preparation method of novel antistatic fabric

An antistatic, baby technology, applied in the field of textile materials, to achieve the effect of improving wear resistance, good water solubility, and excellent antistatic properties

Active Publication Date: 2016-01-06
浙江三德纺织服饰有限公司
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] It can be seen from the above-mentioned prior art that the antistatic clothing currently on the market is finished by antistatic agents or given by antistatic raw materials, but there are few special antistatic baby clothing fabrics, and baby clothing fabrics require higher requirements than conventional fabrics. Therefore, it is necessary to design a special antistatic fabric for baby clothing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel antistatic fabric special for infant clothes and preparation method of novel antistatic fabric
  • Novel antistatic fabric special for infant clothes and preparation method of novel antistatic fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] (1) Chitosan-N-acetyl-glucosaminid hydrolase is dissolved in distilled water to form 1-2% enzyme solution, and powdered chitosan with a mass ratio of 1:1 is placed in the enzyme solution, Stir and degrade to obtain a degraded chitosan solution.

[0031] (2) Prepare the degraded chitosan solution prepared in step (1) into a chitosan solution with a concentration of 0.3%, immerse the cotton fiber in the chitosan solution with a bath ratio of 1:20, and shake at 65°C for 2h , taken out, placed in an oven at 60° C. for drying, washed with water, and dried to obtain chitosan-modified cotton fibers.

[0032] (3) The chitosan-modified cotton fiber and chitin fiber prepared in the step (2) with a raw material ratio of 2:1 were used as raw materials, and the knitted baby fabric was prepared through a knitting process.

[0033] (4) Treat the knitted baby fabric prepared in step (3) with air or oxygen as an atmosphere, after low-temperature plasma treatment under 200W power for 30...

Embodiment 2

[0035] (1) Chitosan-N-acetyl-glucosaminid hydrolase is dissolved in distilled water to form a 2% enzyme solution, and powdered chitosan with a mass ratio of 1:3 is placed in the enzyme solution, stirred and degraded , to obtain a degraded chitosan solution.

[0036] (2) Prepare the degraded chitosan solution prepared in step (1) into a chitosan solution with a concentration of 0.8%, immerse the cotton fiber in the chitosan solution with a bath ratio of 1:30, and shake at 70°C for 3h , taken out, placed in an oven at 60° C. for drying, washed with water, and dried to obtain chitosan-modified cotton fibers.

[0037] (3) The chitosan-modified cotton fiber and chitin fiber prepared in the step (2) with a raw material ratio of 4:1 were used as raw materials, and the knitted baby fabric was prepared through a knitting process.

[0038] (4) Treat the knitted baby fabric prepared in step (3) with air or oxygen as an atmosphere, after low-temperature plasma treatment at a power of 250...

Embodiment 3

[0040] (1) Chitosan-N-acetyl-glucosaminid hydrolase is dissolved in distilled water to form 1.5% enzyme solution, and powdered chitosan with a mass ratio of 1:2 is placed in the enzyme solution, stirred and degraded , to obtain a degraded chitosan solution.

[0041] (2) The degraded chitosan solution prepared in step (1) is formulated into a chitosan solution with a concentration of 0.5%, and the cotton fiber is soaked in the chitosan solution with a bath ratio of 1:25 and shaken at 68°C for 2.5 h, take it out, place it in an oven at 60° C. for drying, wash it with water, and dry it to obtain the cotton fiber modified with chitosan.

[0042] (3) The chitosan-modified cotton fiber and chitin fiber prepared in the step (2) with a raw material ratio of 3:1 were used as raw materials, and the knitted baby fabric was prepared through a knitting process.

[0043] (4) Treat the knitted baby fabric prepared in step (3) with air or oxygen as an atmosphere, and then immerse it in 4% silk...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides novel antistatic fabric special for infant clothes and a preparation method of the novel antistatic fabric. The preparation method comprises the following specific steps: (1) dissolving chitosan-N-acetyl-amino glucoside hydrolase into water to form a 1-2% enzyme solution, placing powdered chitosan in the enzyme solution, and stirring for degradation, so as to obtain a degraded chitosan solution; (2) preparing the degraded chitosan solution into a chitosan solution with the concentration of 0.3-0.8%, dipping cotton fibers in the chitosan solution, oscillating for 2-3 h at the temperature of 65-70 DEG C, taking out the cotton fibers, placing the cotton fibers into a drying oven with the temperature of 60 DEG C to be dried, washing with water, and drying, so as to obtain the cotton fibers modified by chitosan; (3) taking the cotton fibers modified by chitosan and chitin fibers as raw materials, and carrying out the knitting process, so as to obtain knitted infant fabric; (4) performing low-temperature plasma treatment on the knitted infant fabric, dipping the knitted infant fabric subjected to the low-temperature plasma treatment in a silk fibroin solution, taking out the knitted infant fabric, removing the residual silk fibroin solution on the surface of the knitted infant fabric, and drying, so as to obtain the antistatic fabric special for infant clothes.

Description

Technical field: [0001] The invention belongs to the technical field of textile materials, and in particular relates to a special antistatic fabric for baby clothes and a preparation method thereof. Background technique: [0002] In recent years, with the relaxation of the birth policy, my country will usher in a new round of birth peak, accompanied by a huge increase in baby clothing, and with the enhancement of green environmental protection awareness, young parents not only meet the needs of baby clothing Instead of the needs of the body, more requirements are put forward for the health and hygiene safety of baby clothing. [0003] Infancy refers to children aged 0-1. The biggest physiological characteristics of infancy are that the body is not yet fully developed, the bones are soft, the skin is delicate and sensitive, sweating and excrement, poor resistance, behavioral ability is not self-help, self-protection ability Difference. These factors determine that the safety...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine