Sound insulation and adsorption material for indoor decoration and preparation method thereof

A technology for adsorption materials and interior decoration, applied in the field of sound insulation adsorption materials and its preparation, can solve the problems of poor performance of sound insulation materials, hidden dangers of privacy protection, etc., and achieve the effect of improving purification efficiency

Inactive Publication Date: 2016-01-27
SUZHOU FAST INFORMATION TECH CO LTD
View PDF6 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the lack of sound insulation materials or the poor performance of sound insulation materials in houses, the sound of walking on the floor upstairs, the crying of babies in the neighbors, and the quarrel between husband and wife can be introduced into our houses; more importantly, It is your own voice that can also be transmitted to other families, which brings hidden dangers to privacy protection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sound insulation and adsorption material for indoor decoration and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A preparation method for a sound-insulating adsorption material for interior decoration, comprising the following steps:

[0019] S1: Preparation of modified montmorillonite: immerse montmorillonite in aluminum chloride solution, stir and reflux at 80°C for 5 hours, filter, wash with deionized water, and dry to obtain modified montmorillonite;

[0020] S2: Add 25 parts of the modified montmorillonite, 40 parts of molecular sieves, 15 parts of D-mannitol and 38 parts of water-soluble polyurethane emulsion in step S1 into the reactor, and stir and react at 40°C for 2 hours; 10 parts of boronite, 8 parts of anatase and 4 parts of zirconium silicate were ground to 30-60 mesh and added to the reactor, and the stirring was continued for 3.5 hours to obtain the mixed solution A;

[0021] S3: Add 5 parts of carboxymethylcellulose ammonium salt, 4 parts of antimony pentoxide sol and 8 parts of silane coupling agent to the mixed liquid A in step S2 in sequence, raise the temperat...

Embodiment 2

[0027] A preparation method for a sound-insulating adsorption material for interior decoration, comprising the following steps:

[0028] S1: Preparation of modified montmorillonite: immerse montmorillonite in ferric chloride solution, stir and reflux at 100°C for 6 hours, filter, wash with deionized water, and dry to obtain modified montmorillonite;

[0029] S2: Add 35 parts of modified montmorillonite, 65 parts of molecular sieve, 28 parts of D-mannitol and 45 parts of water-soluble polyurethane emulsion in step S1 into the reactor, and stir and react at 60°C for 1 hour; 15 parts of boronite, 18 parts of anatase and 10 parts of zirconium silicate were ground to 30-60 mesh, then added into the reactor, and continued to stir for 3 hours to obtain a mixed solution A;

[0030] S3: Add 10 parts of carboxymethyl cellulose ammonium salt, 8 parts of antimony pentoxide sol and 15 parts of silane coupling agent to the mixed liquid A in step S2 in sequence, raise the temperature of the ...

Embodiment 3

[0036] A preparation method for a sound-insulating adsorption material for interior decoration, comprising the following steps:

[0037] S1: Preparation of modified montmorillonite: immerse montmorillonite in ferric chloride solution, stir and reflux at 100°C for 6 hours, filter, wash with deionized water, and dry to obtain modified montmorillonite;

[0038] S2: Add 30 parts of modified montmorillonite, 58 parts of molecular sieves, 20 parts of D-mannitol and 42 parts of water-soluble polyurethane emulsion in step S1 into the reactor, and stir and react at 60°C for 1 hour; 12 parts of boronite, 10 parts of anatase and 6 parts of zirconium silicate were ground to 30-60 mesh, then added to the reactor, and continued to stir for 3 hours to obtain a mixed solution A;

[0039] S3: Add 8 parts of carboxymethyl cellulose ammonium salt, 5 parts of antimony pentoxide sol and 10 parts of silane coupling agent to the mixed liquid A in step S2 in sequence, raise the temperature of the rea...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a sound insulation and adsorption material for indoor decoration and a preparation method thereof. The method includes: firstly preparing modified montmorillonite; then taking 25-35 parts of modified montmorillonite, 40-65 parts of a molecular sieve, 15-28 parts of D-mannitol and 38-45 parts of a water soluble polyurethane emulsion, and adding them into a reactor to carry out stirring reaction; then grinding 10-15 parts of ascharite, 8-18 parts of anatase and 4-10 parts of zirconium silicate, then adding the grinding product into the reactor to conduct further stirring; adding 5-10 parts of a carboxymethyl cellulose ammonium salt, 4-8 parts of antimony pentoxide sol and 8-15 parts of a silane coupling agent into the reactor in order, heating the reaction liquid to 80-120DEG C, and carrying out reaction under continuous stirring; and finally adding the mixture into a double-screw extruder to conduct extrusion molding, thus obtaining the sound insulation and adsorption material. The sound insulation and adsorption material provided by the invention has good adsorption performance and sound insulation effect at the same time, and can reach the purposes of purifying indoor air and obstructing noise.

Description

technical field [0001] The invention belongs to the field of building materials, and relates to a sound-insulating and absorbing material for interior decoration and a preparation method thereof. Background technique [0002] Clothing, food, housing and transportation are the basic needs of people's life, and the most important thing is housing. However, due to the lack of sound insulation materials or the poor performance of sound insulation materials in houses, the sound of walking on the floor upstairs, the crying of babies in the neighbors, and the quarrel between husband and wife can be introduced into our houses; more importantly, The voice of one's own family can also be transmitted to other families, which brings hidden dangers to the protection of privacy. There are many meals, restaurants, and barbecue restaurants gathered around today's residential areas. The resulting pollution and pollution from automobile exhaust will enter the room through the windows. If our...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/16
Inventor 彭孝茹
Owner SUZHOU FAST INFORMATION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products