Modified diaphragm special for Li-S battery, preparation method of modified diaphragm and Li-S battery

A lithium-sulfur battery and separator technology, which is applied in the field of lithium-sulfur batteries, can solve the problems of limited adsorption capacity and achieve the effects of simple preparation method, improved capacity and cycle life, and enhanced adsorption capacity

Active Publication Date: 2016-01-27
CHANGSHA RES INST OF MINING & METALLURGY
View PDF7 Cites 27 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the adsorption of these conductive polymer materials and porous carbon materials on lithium polysu

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified diaphragm special for Li-S battery, preparation method of modified diaphragm and Li-S battery
  • Modified diaphragm special for Li-S battery, preparation method of modified diaphragm and Li-S battery
  • Modified diaphragm special for Li-S battery, preparation method of modified diaphragm and Li-S battery

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A special modified diaphragm for lithium-sulfur batteries of the present invention, comprising commercial diaphragm Celgard2400 and a modified coating coated on the surface of the commercial diaphragm Celgard2400 near the positive electrode, the modified coating is Ketjen black coated with Ketjen black-oxidized Manganese coating; the conductive agent Super-P is added to the modified coating; the thickness of the modified coating is 100 μm; the mass ratio of Ketjen black to metal oxide in the modified coating is about 5:1.

[0036] The preparation method of the special modified diaphragm for lithium-sulfur battery in this embodiment includes the following steps:

[0037] (1) 0.3g manganese sulfate is dissolved in 100mL ultrapure water to form solution A;

[0038] (2) Add 1 g of Ketjen Black to Solution A, and ultrasonically disperse for 2 hours with 500W of ultrasonic power;

[0039] (3) Suction filter the solution obtained in step (2) and dry in an oven at 80° C. for 2...

Embodiment 2

[0050] A special modified diaphragm for lithium-sulfur batteries of the present invention, comprising commercial diaphragm Celgard2400 and a modified coating coated on the surface of the commercial diaphragm Celgard2400 near the positive electrode, the modified coating is Ketjen black coated with Ketjen black-oxidized Manganese coating; the conductive agent Super-P is added to the modified coating; the thickness of the modified coating is 100 μm; the mass ratio of Ketjen black to metal oxide in the modified coating is about 4:1.

[0051] The preparation method of the special modified diaphragm for lithium-sulfur battery in this embodiment comprises the following steps:

[0052] (1) 0.4g manganese nitrate is dissolved in 100mL ultrapure water to form solution A;

[0053] (2) Add 1 g of Ketjen Black to Solution A, and ultrasonically disperse for 2 hours with 500W of ultrasonic power;

[0054] (3) Suction filter the solution obtained in step (2) and dry in an oven at 80° C. for ...

Embodiment 3

[0064] A special modified diaphragm for lithium-sulfur batteries of the present invention, comprising commercial diaphragm Celgard2400 and a modified coating coated on the surface of the commercial diaphragm Celgard2400 near the positive electrode, the modified coating is Ketjen black coated with Ketjen black-oxidized Lanthanum coating; the conductive agent Super-P is added to the modified coating; the thickness of the modified coating is 100 μm; the mass ratio of Ketjen black to metal oxide in the modified coating is about 3:1.

[0065] The preparation method of the special modified diaphragm for lithium-sulfur battery in this embodiment comprises the following steps:

[0066] (1) 0.4g lanthanum nitrate is dissolved in 100mL ultrapure water to form solution A;

[0067] (2) Add 1 g of Ketjen Black to Solution A, and ultrasonically disperse for 2 hours with 500W of ultrasonic power;

[0068] (3) Suction filter the solution obtained in step (2) and dry in an oven at 80° C. for ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
First discharge specific capacityaaaaaaaaaa
Login to view more

Abstract

In a modified diaphragm special for a Li-S battery, the surface at one side, close to a positive electrode, of a general diaphragm is coated with a Ketjen black coated metal oxide modified coating layer added with a conductive agent. A preparation method of the modified diaphragm special for the Li-S battery comprises the following steps of sequentially mixing Ketjen black and an aqueous solution of a metal oxide inorganic salt, carrying out dispersion, drying and calcinations to prepare a paste, and applying the paste at one side, close to the positive electrode, of a commercial diaphragm to obtain the modified diaphragm. The invention also discloses the Li-S battery applying the modified diaphragm special for the Li-S battery. The Li-S battery is prepared by taking metal lithium as a negative electrode, applying a Ketjen balck-sulfur composite material onto an aluminum foil to serve as the positive electrode, taking a mixture of LiTFSI, lithium nitrate, 1,3-dioxolane and glycol dimethyl ether as an electrolyte and assembling the modified diaphragm special for the Li-S battery. With the modified diaphragm disclosed by the invention, a "shuttle effect" of polysulfide lithium in the Li-S battery can be prevented, the electrochemical performance and the capacity of the Li-S battery are improved, the cycle lifetime of the Li-S battery is prolonged, and the modified diaphragm is suitably used for production at a large scale.

Description

technical field [0001] The invention relates to the field of lithium-ion batteries, in particular to a modified diaphragm specially used for lithium-sulfur batteries, a preparation method thereof and a lithium-sulfur battery composed of the same. Background technique [0002] Lithium-sulfur (Li-S) battery is a new type of electrochemical energy storage system with lithium as the negative electrode (theoretical specific capacity 3860mAh / g) and sulfur as the positive electrode (theoretical specific capacity 1675mAh / g). The theoretical specific energy can reach 2600Wh / g. kg, which is much larger than the commercial lithium-ion batteries at this stage, and the characteristics of sulfur, which are abundant, cheap, and low-toxic or non-toxic, make this system extremely commercially valuable. However, there are many serious problems in the electrochemistry of lithium-sulfur batteries that need to be solved urgently. First of all, the conductivity of the active substance sulfur and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01M2/16H01M2/14H01M10/0525H01M50/40H01M50/403H01M50/431
CPCH01M10/0525H01M50/403H01M50/446Y02E60/10
Inventor 钱昕晔沈湘黔赵迪杨晓龙王善文姚山山饶德伟周友元习小明
Owner CHANGSHA RES INST OF MINING & METALLURGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap