A low-grade talc chemical fertilizer anti-caking agent and its preparation method and application
An anti-caking agent, low-grade technology, applied in the direction of application, fertilization device, fertilizer mixture, etc., to achieve the effect of less dosage, wide application range and simple preparation process
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0026] Weigh 100g of inorganic powder B and 1100ml of water to prepare a slurry with a slurry concentration of 8.33%. Dissolve 1g of stearic acid in 15mL of absolute ethanol, put it into the SMA-0.75 basket mill together with the pulp, the ball-to-material ratio is 66:1, carry out the integrated operation of ultrafine pulverization and surface modification, and grind for 3 hours , take out the pulp, dehydrate it with a vacuum filter, dry it in an electric blast drying oven at 80°C, and grind it finely with a high-speed pulverizer to obtain a fertilizer anti-caking agent. The whiteness of the product obtained is 90%. d 50 is 2.91 μm.
Embodiment 2
[0027] Example 2: Weigh 100g of inorganic powder B and 1100ml of water to prepare a slurry with a slurry concentration of 8.33%. Dissolve 2g of stearic acid in 30mL of absolute ethanol, put it into the SMA-0.75 basket mill together with the pulp, the ball-to-material ratio is 66:1, carry out the integrated operation of ultrafine pulverization and surface modification, and grind for 3 hours , take out the pulp, dehydrate it with a vacuum filter, dry it in an electric blast drying oven at 80°C, and grind it with a high-speed pulverizer to obtain a fertilizer anti-caking agent. The whiteness of the obtained product is 90.2%. d 50 is 2.85 μm.
Embodiment 3
[0028] Embodiment 3: Weigh 100g of inorganic powder B and 1100ml of water to prepare a slurry with a slurry concentration of 8.33%. Dissolve 3g of stearic acid in 45mL of absolute ethanol, put it into the SMA-0.75 basket mill together with the pulp, the ball-to-material ratio is 66:1, carry out the integrated operation of ultra-fine pulverization and surface modification, and grind for 3 hours , take out the pulp, dehydrate it with a vacuum filter, dry it in an electric blast drying oven at 80°C, and grind it with a high-speed pulverizer to obtain a fertilizer anti-caking agent. The whiteness of the obtained product is 90.85%. d 50 is 2.86 μm.
PUM
Property | Measurement | Unit |
---|---|---|
whiteness | aaaaa | aaaaa |
whiteness | aaaaa | aaaaa |
whiteness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com