Hydrotalcite-dimer acid lanthanum composite environmental protection stabilizer for PVC, and preparation method thereof

An environmentally friendly stabilizer, lanthanum dimer acid technology, applied in the field of PVC additives, can solve the problems of not being the main stabilizer, poor coloring, low thermal stability, etc., to reduce the balance torque, low cost, and good thermal stability. and processing performance

Inactive Publication Date: 2016-02-03
HWASU
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Rare earth heat stabilizers have good thermal stability, but the early thermal stability is not high, and the initial coloring is poor, so they cannot be the main stabilizer alone, so their application and promotion are limited. The application of a single rare earth heat stabilizer is often difficult to meet the needs of PVC processing. Composite and multi-functional rare earth heat stabilizers have become the development trend according to the requirements of application performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] A PVC hydrotalcite dimer lanthanum acid composite environmental stabilizer, which is prepared from the following component raw materials by weight (kg): modified magnesium aluminum hydrotalcite 25, dibutyltin oxide 11, dimer lanthanum acid 8, Triphenyl phosphite 2, zinc stearate 5, epoxidized soybean oil 3, β-diketone 6, 2,2'-thiobis(4-tert-octylphenoxy)nickel 3, acetyl citrate tri Ethyl ester 13, montan wax 2, attapulgite 14,

[0018] The preparation method is as follows:

[0019] (1) Preparation of modified hydrotalcite:

[0020] a. Add a certain amount of Mg(NO3)2·6H2O and Al(NO3)3·9H2O into water to form a salt solution with a total molar concentration of 0.6mol / L, and add a certain amount of NaOH and Na2CO3 into deionized water to form The total molar concentration is 0.6mol / L alkali solution, drop the alkali solution into the salt solution at a speed of 1-2 drops / s, N 2 Stir vigorously under protection, keep the temperature at 38-42°C, keep the pH value between...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
timeaaaaaaaaaa
timeaaaaaaaaaa
Login to View More

Abstract

The present invention provides a hydrotalcite-dimer acid lanthanum composite environmental protection stabilizer for PVC, wherein the hydrotalcite-dimer acid lanthanum composite environmental protection stabilizer is prepared from the following raw materials by weight: 20-30 parts of modified magnesium aluminum hydrotalcite, 10-12 parts of dibutyl tin oxide, 6-9 parts of dimer acid lanthanum, 1-3 parts of triphenyl phosphite, 3-6 parts of zinc stearate, 2-4 parts of epoxidized soybean oil, 5-6 parts of beta-diketone, 2-4 parts of 2,2'-thiobis(4-tert-octylphenoloxy)nickel, 12-15 parts of triethyl acetyl citrate, 1-2 parts of montan wax, and 10-15 parts of attapulgite. According to the present invention, the PVC stabilizer has characteristics of good thermal stability, good processing performance, environmental protection, no toxicity, low cost, good plasticity and balance torque reducing during the PVC processing process, and low cost.

Description

technical field [0001] The invention relates to the field of PVC additives, in particular to a PVC hydrotalcite dimer lanthanum acid composite environmental stabilizer and a preparation method thereof. Background technique [0002] With its superior physical properties and low cost, PVC is widely used in chemical industry, materials, machinery, agriculture, daily necessities and other fields, especially in the field of plastics, and is known as one of the five general-purpose plastics. However, PVC has a very important defect, that is, it is easy to decompose and generate HCl gas during thermal processing, and self-catalysis leads to severe degradation of PVC, which affects various properties of PVC products, such as discoloring PVC products or reducing its mechanical properties. In order to overcome this defect of PVC, it is mainly to add an appropriate amount of stabilizer during the thermal processing of PVC. [0003] The only heat stabilizers that are generally industri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08K13/06C08K9/02C08K9/04C08K3/26C08K5/57C08K5/526C08K5/098C08K5/11
Inventor 王圣茂丘永桂宋开生高旭李毅徐明肖独山孙荣兴
Owner HWASU
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com