Glass cutting fluid
A cutting fluid and glass technology, applied in the petroleum industry, lubricating compositions, etc., can solve the problems of poor glass powder settling, poor grinding-assistance durability, poor lubrication and cooling effect, etc., to achieve good lubricity, prolonged The effect of improving the service life and cutting force
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0046] The present invention also provides a method for preparing glass cutting fluid. In a preferred embodiment, the method for preparing glass cutting fluid includes the following steps:
[0047] Provide the ratio of the glass cutting fluid of the above-mentioned preferred embodiment;
[0048] Add C4-C12 organic carboxylic acid rust inhibitor, synthetic lubricant, polymer surface penetrant, dipropylene glycol wetting agent, PH stabilizer, strong alkali and weak acid salt, and foam suppression in the reactor filled with pure water in turn And glass powder settling agent to prepare a mixed liquid;
[0049] The mixture is heated to 60℃~70℃, and stirred for 2~3h, and then filtered and packaged with a 5um filter bag.
Example Embodiment
[0051] Example 1
[0052] The ratio of glass cutting fluid is as follows:
[0053] C4~C12 organic carboxylate 7.5%, PH stabilizer 10%, polymer surface penetrant 12%, dipropylene glycol 12%, synthetic lubricant 12.5%, strong alkali weak acid salt 3%, foam inhibitor 0.1%, Glass powder settling agent 3% and the balance is water;
[0054] The preparation process of the glass cutting fluid is as follows:
[0055] Add the above-mentioned components in the above-mentioned order to the reaction kettle containing water to prepare a mixed liquid;
[0056] Heat the mixture to 60°C and stir to react for 2 to 3 hours;
[0057] Sampling and testing all indicators, filter and package after qualified.
[0058] The product specifications of the glass cutting fluid are as follows:
[0059] Appearance is light yellow transparent liquid; almost odorless; good physical stability, no delamination or crystal precipitation at 5±2℃, no delamination phenomenon at 60±2℃; effective content of 40%±1%; specific gravit...
Example Embodiment
[0060] Example 2
[0061] The ratio of cutting fluid is as follows:
[0062] C4~C12 organic carboxylate 6.5%, pH stabilizer 10%, polymer surface penetrant 10%, dipropylene glycol 6%, synthetic lubricant 8%, strong alkali and weak acid salt 3%, foam inhibitor 0.1%, Glass powder settling agent 3% and the balance is water;
[0063] The preparation process of the glass cutting fluid is as follows:
[0064] Add the above-mentioned components in the above-mentioned order to the reaction kettle containing water to prepare a mixed liquid;
[0065] Heat the mixture to 60°C and stir to react for 2 to 3 hours;
[0066] Sampling and testing all indicators, filter and package after qualified.
[0067] The product specifications of the glass cutting fluid are as follows:
[0068] Appearance is light yellow transparent liquid; almost odorless; good physical stability, no delamination or crystal precipitation at 5±2℃, no delamination phenomenon at 60±2℃; effective content of 40%±1%; specific gravity of 1...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology