Plasticizing carbon paper softening processing method and softening composite conductive carbon paper prepared by the method

A technique of plasticizing conductive paper and its processing method, which is applied in the fields of fiber raw material processing, paper, papermaking, etc., and can solve problems such as the influence of conductive performance, large thickness of conductive paper, and reduced service life, and achieve stable conductive performance and increased tear strength , the effect of improving the service life

Inactive Publication Date: 2016-02-17
SHANXI XUYAO ELECTRONICS TECH CO LTD
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the problems of existing conductive papers such as large thickness, high hardness, low tear strength, easy tearing, reduced service life, and affected conductive performance, the present invention provides a softening treatment method for plasticized carbon paper and its preparation Softening Composite Conductive Carbon Paper

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Embodiment 1: a kind of plasticizing treatment method of plasticized conductive paper, comprises the following steps:

[0015] (1) Preparation of conductive paper by wet forming: fully disperse pure wood pulp and carbon fiber with 5% weight of pure wood pulp in water, copy into paper, and dry to obtain conductive paper;

[0016] (2) Preparation of hydrophobic SBR styrene-butadiene latex: based on the total weight of the prepared styrene-butadiene latex as 100%, it is prepared by mixing 40% butadiene, 20% styrene, 25% acrylic acid and 15% methacrylic acid;

[0017] (3) Plasticized conductive paper: The hydrophobic SBR styrene-butadiene latex prepared in step (2) is mixed with water evenly according to the glue ratio of 1:6, and then the mixed glue solution is sprayed on the conductive paper prepared in step (1). On paper, let it dry naturally.

[0018] The thickness of the conductive paper prepared in step (1) is 50g / m 2 . The spraying amount of the mixed glue aqueous...

Embodiment 2

[0021] Embodiment 2: a kind of plasticizing treatment method of plasticized conductive paper, comprises the following steps:

[0022] (1) Preparation of conductive paper by wet forming: fully disperse pure wood pulp and carbon fiber with 15% weight of pure wood pulp in water, copy into paper, and dry to obtain conductive paper;

[0023] (2) Preparation of hydrophobic SBR styrene-butadiene latex: According to the total weight of the prepared hydrophobic SBR styrene-butadiene latex as 100%, mix 30% butadiene, 25% styrene, 30% acrylic acid and 15% methacrylic acid , prepared into hydrophobic SBR styrene-butadiene latex;

[0024] (3) Plasticized conductive paper: The hydrophobic SBR styrene-butadiene latex prepared in step (2) is mixed with water evenly according to the glue ratio of 1:6, and then the mixed glue solution is sprayed on the conductive paper prepared in step (1). On paper, let it dry naturally.

[0025] The thickness of the conductive paper prepared in step (1) is ...

Embodiment 3

[0028] Embodiment 3: a kind of plasticizing treatment method of plasticized conductive paper, comprises the following steps:

[0029] (1) Preparation of conductive paper by wet forming: fully disperse pure wood pulp and carbon fiber with 25% weight of pure wood pulp in water, copy into paper, and dry to obtain conductive paper;

[0030] (2) Preparation of hydrophobic SBR styrene-butadiene latex: According to the total weight of the prepared hydrophobic SBR styrene-butadiene latex as 100%, mix 50% butadiene, 15% styrene, 25% acrylic acid and 10% methacrylic acid , prepared into hydrophobic SBR styrene-butadiene latex;

[0031] (3) Plasticized conductive paper: The hydrophobic SBR styrene-butadiene latex prepared in step (2) is mixed with water evenly according to the glue ratio of 1:6, and then the mixed glue solution is sprayed on the conductive paper prepared in step (1). On paper, let it dry naturally.

[0032] The thickness of the conductive paper prepared in step (1) is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention belongs to the technical field of a conductive material, solves the problems that conventional conductive paper is large in thickness and hardness, low in tear strength and easy to tear, the service life is reduced, conductive performance is affected, and the like, and provides a plasticizing carbon paper softening processing method and softening composite conductive carbon paper prepared by the method. Conductive paper is prepared by wet molding, hydrophobic SBR styrene-butadiene rubber is prepared, and the conductive paper is plasticizing by the styrene-butadiene rubber. The method is simple, and suitable for industrial production; the conductive paper is ultra-thin, loose, soften and high in tear strength, the service life is increased, thermal conductivity is uniform, power stability, electrical conductivity is stable, temperature is kept stable, the indoor can be evenly heated, price is low, the service life is long, power consumption is low, the product is waterproof, fire retardant, and small in space occupation, can be freely wound, can be made into invisibly-heated walls, floors and furniture, can be used in insulation works, belongs to an energy saving, environmental-friendly, safe, easy-to-maintain new generation electric heating product, and is convenient to transport, transportation-cost-saving and durable.

Description

technical field [0001] The invention belongs to the technical field of conductive material production, and in particular relates to a softening treatment method for plasticized carbon paper and the prepared softened composite conductive carbon paper. Background technique [0002] Conductive paper is a kind of conductive functional paper, which can be widely used in anti-static packaging, electromagnetic shielding, surface heating, heat-resistant and flame-retardant, new energy, electrochemistry, biomedicine and other materials. Carbon fiber conductive paper is obtained by fully dispersing carbon fiber and other fibers or powder materials in a solvent, and drying them into paper. In order to make the fibers interweave more fully, organic compounds, such as polyvinyl alcohol, polyimide and other binders and cationic reinforcing agents, are usually added to increase the bonding force between fibers; at the same time, the content of carbon fibers can also be adjusted at Adjusta...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D21H27/18D21H23/50D21H19/14
CPCD21H27/18D21H19/14D21H23/50
Inventor 程学礼
Owner SHANXI XUYAO ELECTRONICS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap