Preparation method for heat insulating coating for improving heat resistance of automobile

A heat-insulating coating and heat-resistant technology, applied in the field of preparation of heat-insulating coatings, can solve the problems of loss, thermal conductivity occupant discomfort, easy to cause accidents, etc., so as to improve heat resistance, avoid high-temperature accidents, isolate good thermal performance

Inactive Publication Date: 2016-02-24
韩登鹤
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the improvement of people's living standards, cars have become more and more common means of transportation, and car covers are one of the most important parts of cars, including car roof covers, car engine covers, car tail covers, etc. Because the profile used in the car cover is a good conductor of heat, in the face of high temperature environments such as the summer heat, good thermal conductivity often makes passengers feel uncomfortable. At the same time, excessive temperature can easily cause accidents and cause losses.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A preparation method of a thermal insulation coating for improving the heat resistance of an automobile cover plate, the preparation method is as follows:

[0019] (1) Put 22 parts of triethanolamine and 19 parts of triglycerol into the stirring tank in terms of parts by mass, control the stirring rate to 120r / min, and the stirring temperature at 45°C, stir once for 12 minutes, and then put in 13 parts of polyether Polyol 835, the stirring rate is controlled at 150r / min, the stirring temperature is 55°C, and the second stirring is carried out for 22 minutes, and then 8 parts of polyether polyol 4410 are added, the stirring rate is controlled at 150r / min, the stirring temperature is 65°C, and three times Stir for 22min to obtain Polymer A;

[0020] (2) Put 21 parts of polyimide resin, 13 parts of polyethylene glycol dimethacrylate and 6 parts of polyvinyl chloride resin into the stirring tank in order by mass parts, control the stirring rate to 60r / min, stir The tempera...

Embodiment 2

[0024] A preparation method of a thermal insulation coating for improving the heat resistance of an automobile cover plate, the preparation method is as follows:

[0025] (1) Put 23 parts of triethanolamine and 16 parts of tripolyglycerol into the stirring tank by mass parts, control the stirring rate to 120r / min, and the stirring temperature at 55°C, stir once for 14min, and then put in 11 parts of polyether Polyol 835, the stirring rate is controlled at 140 / min, the stirring temperature is 40-55°C, and the second stirring is carried out for 18 minutes, and then 7 parts of polyether polyol 4410 are added, the stirring rate is controlled at 160r / min, and the stirring temperature is 65°C. Stir three times for 25min to obtain Polymer A;

[0026] (2) Put 21 parts of polyimide resin, 13 parts of polyethylene glycol dimethacrylate and 7 parts of polyvinyl chloride resin into the stirring tank in order by mass parts, control the stirring rate to 60r / min, stir The temperature was 50...

Embodiment 3

[0030] A preparation method of a thermal insulation coating for improving the heat resistance of an automobile cover plate, the preparation method is as follows:

[0031] (1) Put 32 parts of triethanolamine and 21 parts of tripolyglycerol into the stirring tank by mass parts, control the stirring rate to 135r / min, and the stirring temperature at 55°C, stir once for 15min, and then put in 14 parts of polyether Polyol 835, the stirring rate is controlled at 150r / min, the stirring temperature is 45°C, and the second stirring is carried out for 24 minutes, and then 8 parts of polyether polyol 4410 are added, the stirring rate is controlled at 160r / min, the stirring temperature is 65°C, and three times Stir for 20min to obtain Polymer A;

[0032] (2) Put 22 parts of polyimide resin, 16 parts of polyethylene glycol dimethacrylate and 7 parts of polyvinyl chloride resin into the stirring tank in order by mass parts, control the stirring rate to 60r / min, stir The temperature was 50°C...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a preparation method for a heat insulating coating for improving the heat resistance of an automobile cover plate. The preparation method comprises the following steps: (1) preparing a polymer A, wherein the polymer A comprises a polyol a, a polyol b, a polyether polyol a and a polyether polyol b; (2) preparing a polymer B, wherein the polymer B comprises polyimide resin, polyethylene glycol dimethyl acrylate and polyvinyl chloride resin; (3) preparing an inorganic mixture, wherein the inorganic mixture comprises silicon dioxide, graphite powder and inorganic fiber; (4) preparing the heat insulating coating. The heat insulating coating can coat the outer surface of the automobile cover plate, so that the heat resistance of the automobile can be improved, the passenger comfort degree can be improved, and high-temperature accidents can be avoided.

Description

technical field [0001] The invention relates to a coating, in particular to a method for preparing a thermal insulation coating for improving the heat resistance of an automobile cover plate. Background technique [0002] With the improvement of people's living standards, cars have become more and more common means of transportation, and car covers are one of the most important parts of cars, including car roof covers, car engine covers, car tail covers, etc. Because the profile used in the car cover is a good conductor of heat, in the face of high temperature environments such as the summer heat, good thermal conductivity often makes occupants feel uncomfortable. At the same time, excessively high temperatures are likely to cause accidents and cause losses. Contents of the invention [0003] The purpose of the present invention is to address the defects of the prior art and provide a preparation method for improving the heat resistance of the automobile cover. The prepare...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D179/08C09D171/00C09D127/06C09D7/12
CPCC09D179/08C08L2201/02C08L2201/08C08L2205/035C09D7/61C09D7/63C09D7/70
Inventor 韩璐季璠韩登鹤
Owner 韩登鹤
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap