Preparation method for synergetic reinforcing and toughening polypropylene composite material

A composite material and polypropylene-based technology, which is applied in the preparation of synergistically reinforced and toughened polypropylene-based composite materials and the reinforcement and toughening process of extrusion-molded polypropylene-based composite materials, can solve the problems of decreased strength and rigidity, complex process, The problem of high cost is to achieve the effect of balancing excellent toughness and rigidity, simple preparation process and remarkable effect.

Active Publication Date: 2016-03-16
SICHUAN UNIV
View PDF5 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the method of chemical modification can also produce a certain effect on improving the impact strength of polypropylene, the process of this method is complicated, the cost is high, and it is n

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method for synergetic reinforcing and toughening polypropylene composite material
  • Preparation method for synergetic reinforcing and toughening polypropylene composite material
  • Preparation method for synergetic reinforcing and toughening polypropylene composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] (1) Polypropylene (PP, 1300, Maoming Petrochemical) and polyolefin elastomer (POE, 8150, DuPont-Dow Chemical) were selected as experimental raw materials, and the melt indices of the two were 2.5g / 10min (215°C, 2.16 Kg) and 0.8g / 10min (230°C, 5Kg). The blend of polypropylene and polyolefin elastomer with a mass ratio of 80 / 20 is mixed and granulated by twin-screw extrusion, and vacuum-dried before use. The temperature of each stage of twin-screw extrusion granulation is set at 165-190- 200-195°C;

[0036] (2) Put the dried blend masterbatch into a multi-stage stretching device consisting of a single-screw extruder (1), a confluence (2), a force assembly unit (3), and a cooling roll (4) (see figure 1 ) in a single-screw extruder. Through the continuous splitting and shearing action of four one-two-force assembly units, it flows out from the discharge port, and after traction, calendering and cooling, a polypropylene-based sheet with a thickness of about 1.8mm is obtain...

Embodiment 2

[0040] (1) Polypropylene (PP, 1300, Maoming Petrochemical) and polyolefin elastomer (POE, 8150, DuPont-Dow Chemical) were selected as experimental raw materials, and the melt indices of the two were 2.5g / 10min (215°C, 2.16 Kg) and 0.8g / 10min (230°C, 5Kg). The blend of polypropylene and polyolefin elastomer with a mass ratio of 80 / 20 is mixed and granulated by twin-screw extrusion, and vacuum-dried before use. The temperature of each stage of twin-screw extrusion granulation is set at 165-190- 200-195°C;

[0041] (2) Put the dried blend masterbatch into a multi-stage stretching device consisting of a single-screw extruder (1), a confluence (2), a force assembly unit (3), and a cooling roll (4) (see figure 1 ) in a single-screw extruder. After 6 assembling units divided into two, it flows out from the discharge port, and after being drawn and calendered by a traction cooling roller, a polypropylene-based sheet with a thickness of about 1.8mm is obtained. The temperatures of t...

Embodiment 3

[0048] (1) Polypropylene (PP, K1001, Yanshan Petrochemical) and polyolefin elastomer (POE, 8200, Dow Chemical) were selected as experimental raw materials, and the melt indices of the two were 1.0g / 10min (215°C, 2.16Kg) and 5.0g / 10min (215°C, 2.16Kg). The blend of polypropylene and polyolefin elastomer with a mass ratio of 80 / 20 is subjected to twin-screw extrusion, mixing, granulation, and vacuum drying before use. The temperature of each stage of twin-screw extrusion granulation is set at 175-195- 210-205°C;

[0049] (2) Put the dried blend masterbatch into a multi-stage stretching device consisting of a single-screw extruder (1), a confluence (2), a force assembly unit (3), and a cooling roll (4) (see figure 1 ) in a single-screw extruder. After three assembling units divided into two, it flows out from the discharge port, and after traction, calendering and cooling, a PP / POE composite material with a thickness of about 0.6mm is obtained. The temperatures of the feeding ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Melt indexaaaaaaaaaa
Thicknessaaaaaaaaaa
Tensile yield strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method for a synergetic reinforcing and toughening polypropylene composite material. The preparation method is characterized in that in the extrusion molding machining process, under the stimulation effect of an external stress field, the crystal habit of a polypropylene base is evolved into shish-kebab structures tightly arranged in a high orientation manner, and the intensity of the polypropylene material can be obviously improved through formation of the shish-kebab structures; and a flexibilizer dispersion phase form is evolved into the fiber shape and sheet shape from the sphere shape or ellipsoidal shape under the effects of a stretching force field and a rolling force field, and the toughness of the polypropylene material can be obviously improved through formation of the fiber or sheet-shaped dispersion phase form. By means of the preparation method, a force assembling unit is additionally arranged on a traditional extrusion device, operation is simple, continuous production can be achieved, control is convenient, the quality is stable, the production efficiency is high, the good industrialization and the good market prospect are achieved, and the preparation method can be widely applied to preparation of high strength and high toughness polypropylene base panels, sheets and film materials.

Description

technical field [0001] The invention relates to a method for preparing a synergistically reinforced and toughened polypropylene-based composite material, in particular to a reinforced and toughened process for extruding a polypropylene-based composite material, and belongs to the technical field of polymer material processing. Background technique [0002] Polypropylene has excellent comprehensive properties, such as chemical stability, non-toxic, odorless, tasteless, good formability, low relative density, and excellent mechanical properties. Therefore, polypropylene is widely used in automobiles, construction, home furnishing, and home appliances. In the large and small fields of daily life such as packaging and printing industry, its production capacity and consumption in the field of general plastic applications are second only to polyethylene. From 2010 to 2014, in just four years, my country's polypropylene production capacity increased from 9.68 million tons / year at t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B29C69/02C08L23/12C08L23/08C08L53/02
Inventor 吴宏王建峰郭少云夏立超
Owner SICHUAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap