Heatproof and moisture-proof cigarette capsule material and applications thereof

A technology for capsules and cigarettes, which can be used in applications, microcapsule preparations, tobacco, etc. It can solve the problems that the glue cannot be completely uniform, affects the stability of dripping molding, capsule size, uneven skin thickness, etc., and achieves compatibility. The effect of excellent, uniform size and simple manufacturing process

Active Publication Date: 2016-03-16
CHINA TOBACCO GUIZHOU IND
View PDF11 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are certain limitations in this method: the curing of capsules is divided into two steps of low-temperature gel and divalent ion curing. The proportion of gellan gum that is easier to gel in the formula is relatively large, and it is easy to block the dripper during dripping, resulting in uneven dripping, resulting in uneven capsule size and skin thickness, and low yield
In addition, the Chinese patent app

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Heatproof and moisture-proof cigarette capsule material and applications thereof
  • Heatproof and moisture-proof cigarette capsule material and applications thereof
  • Heatproof and moisture-proof cigarette capsule material and applications thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0055] Example 1

[0056] Example 1 is used to illustrate the temperature and moisture-resistant tobacco capsule of the present invention and its preparation method.

[0057] 1. Raw materials

[0058] Material name

[0059] 2. Preparation method

[0060] Weigh 10kg of deionized water, 50g of gum arabic, 0.5kg of sorbitol and 1kg of maltodextrin, respectively, and add them to the gel tank, stir and heat to 65°C, after the mixture is completely dissolved, add 5kg of gelatin, continue stirring until the gelatin is completely dissolved, add 5g bright blue, stir for 30 minutes until the bright blue is completely dissolved, stop stirring, reduce the heating temperature of the glue tank to 60 °C, let it stand for 4 hours to remove air bubbles, pass through an 80-mesh sieve, and obtain a glue solution. The viscosity at 70 °C is 916.8mPa.s.

[0061] Using a co-extrusion dropping equipment with a coaxial double-layer dripper, the glue liquid and the capsule content (flavor...

Example Embodiment

[0069] Experimental example 1

[0070] The purchased capsule and the capsule of Example 1 gained are put into the environment of temperature 22 ℃, humidity 60%, take out and weigh at intervals, investigate the moisture absorption rate of finished product capsule, the capsule moisture absorption curve is as follows: figure 1 shown. Depend on figure 1 It can be seen that the moisture absorption rate of the capsules obtained in Example 1 is significantly lower than that of the purchased capsules, indicating that the capsules obtained in Example 1 have strong temperature and humidity resistance.

Example Embodiment

[0071] Example 2

[0072] Example 2 is used to illustrate the temperature and moisture resistant tobacco capsule of the present invention and its preparation method.

[0073] 1. Raw materials

[0074] Material name

[0075] 2. Preparation method

[0076] Weigh 10kg of deionized water, 0.6kg of citric acid, 0.3kg of chitosan, 0.15kg of glycerol, 0.2kg of sorbitol and 1.3kg of maltodextrin respectively, add them to the glue tank, stir and heat to 65°C, and after the mixture is completely dissolved, Add 5kg of gelatin, continue to stir until the gelatin is completely dissolved, add 5g of bright blue, and stir for 30 minutes until the bright blue is completely dissolved, stop stirring, reduce the heating temperature of the glue tank to 60 ° C, let stand for 4 hours to remove air bubbles, and pass 80 mesh. A mesh screen was used to obtain a glue solution. The glue solution viscosity was 993.4 mPa.s at 70°C. Capsule dropping, oil rubbing, drying, coating and pill selec...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Strengthaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to view more

Abstract

The invention relates to the cigarette technology field, and concretely discloses a heatproof and moisture-proof cigarette capsule material and applications thereof. The capsule material comprises the following components, by weight, 40-60 parts of gelatinizing agent, 4-30 parts of filler, 1-12 parts of plasticizer and 100 parts of deionized water. The capsule material formula and the preparation technology of the capsule material are researched through a lot of tests, and a cigarette brittle capsule material is provided. The compatibility performance is excellent, the manufacturing process is simple, and the capsule material can be widely suitable for coating of various cigarette additives such as essence, perfume and the like. The prepared capsule is round, has a uniform size, has a particle size range of 2.0-4.0mm, has an adjustable and controllable content loading range of 10-25mg, and can meet usage requirements of cigarettes with different specifications. The capsule crushing intensity is 3-15N, the capsule can be crushed by fingers easily with rattle, and the capsule still has brittleness in a humid environment.

Description

technical field [0001] The invention relates to the technical field of cigarettes, in particular to a temperature-resistant and moisture-resistant cigarette capsule material and its application. Background technique [0002] As a "small container", capsules are used in the field of tobacco. They can be used to load additives that improve tobacco quality such as tobacco flavors, flavors, and condiments. They can be made into brittle capsules for cigarettes and added to cigarette filter rods. When consumers smoke The capsules are ruptured by external force to release the fragrance substances. In this way, not only the retention period of flavors and fragrances is prolonged, but also the disadvantages of traditional tobacco additive addition methods such as volatile flavors and fragrances, difficulty in application, poor solubility of additives, ineffective application, and contamination of equipment by additive residues can be effectively avoided. [0003] Capsule preparation...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L89/00C08L5/00C08L5/12C08L5/08C08L5/04C08L3/02C08K5/053A24D3/06B01J13/02B65D81/18
CPCA24D3/061B01J13/02B65D81/18C08K2201/014C08L89/00C08L2205/02C08L2205/03C08L2205/035C08L5/00C08L3/02C08K5/053C08L5/08C08L5/12
Inventor 彭黔荣徐龙泉罗光杰韩慧杰刘娜吴艾璟叶世著张进胡世龙
Owner CHINA TOBACCO GUIZHOU IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap