Corrosion-preventing treating agent for surface of alloy casting
An anti-corrosion treatment and alloy casting technology, applied in the field of alloy casting surface anti-corrosion treatment agent, can solve problems such as difficulty in meeting requirements, environmental hazards, inability to clean and remove aluminum alloy die-casting coatings, etc. good antiseptic effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0015] Example one
[0016] The surface anticorrosive treatment agent for alloy castings is prepared according to a method known in the art, and the following components are all calculated in parts by weight:
[0017] 100 parts of oxalic acid, 20 parts of silane coupling agent, 20 parts of isopropanol, 10 parts of aluminum sulfate, 6 parts of corrosion inhibitor, 80 parts of distilled water, at room temperature, first add oxalic acid and soluble aluminum salt sequentially to the mixture of isopropanol and distilled water In the mixed solution, stir evenly, and then add the γ-ureidopropyltriethoxysilane coupling agent and benzotriazole into the above solution.
[0018] Preferably, the corrosion inhibitor is a mixture of benzotriazole and octadecyltrichlorosilane in a mass ratio of 1:0.1.
[0019] Spray the above treatment agent on the surface of the casting. After coating, the anti-corrosion and anti-rust properties of the casting are increased by 2 times, and the coating adhesion rea...
Example Embodiment
[0020] Example two
[0021] Prepare alloy casting surface anticorrosion treatment agent according to the following components (all in parts by weight)
[0022] 100 parts of oxalic acid, 20 parts of silane coupling agent, 25 parts of isopropanol, 15 parts of aluminum chloride, 8 parts of corrosion inhibitor, 100 parts of distilled water. At room temperature, first add oxalic acid and soluble aluminum salt sequentially to the mixed solution of isopropanol and distilled water, stir evenly, and then add the aniline methyl triethoxy silane coupling agent and the corrosion inhibitor to the above solution.
[0023] The above-mentioned corrosion inhibitor is a mixture of benzotriazole and octadecyltrichlorosilane in a mass ratio of 1:0.2.
[0024] Spray the above treatment agent on the surface of the casting. After coating, the anti-corrosion and anti-rust properties of the casting are increased by 3 times, and the coating adhesion reaches the first level.
Example Embodiment
[0025] Example three
[0026] 100 parts of oxalic acid, 25 parts of silane coupling agent, 30 parts of isopropanol, 12 parts of aluminum chloride, 6 parts of corrosion inhibitor, 120 parts of distilled water. At room temperature, first add oxalic acid and soluble aluminum salt to the mixed solution of isopropanol and distilled water in sequence, stir uniformly, and then add hexamethylenediaminomethyltriethoxysilane coupling agent and corrosion inhibitor to the above solution.
[0027] The above-mentioned corrosion inhibitor is a mixture of benzotriazole and octadecyltrichlorosilane in a mass ratio of 1:0.3.
[0028] Spray the above treatment agent on the surface of the casting. The anti-corrosion and anti-rust properties of the casting are increased by 3 times, and the coating adhesion reaches the first level.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap