Steel slag permeable building material and manufacturing method thereof

A technology of building materials and manufacturing methods, applied in the direction of sustainable waste treatment, solid waste management, climate sustainability, etc., can solve the problems of waste of resources, comprehensive utilization rate of less than 10%, poor utilization, etc., to achieve utilization and water permeability good performance effect

Inactive Publication Date: 2016-04-20
赵建林
View PDF3 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Except for a small part of the steel slag sold to the cement factory, most of the steel slag is piled up in an unorganized manner, causing environmental pollution, land occupation and waste of resources
Steel slag tailings are one of the worst bulk solid wastes used by iron and steel enterprises. Last year, the amount of steel slag produced in my country reached more than 100 million tons. At present, the cumulative stock of steel slag in the country has reached as much as 1 billion tons, and the comprehensive utilization rate is less than 10%.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Steel slag permeable building material and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] This embodiment provides a building material with unique water permeability and water permeability made of steel slag, including: steel slag with a polymer coating layer and an adhesive, and the steel slag with a polymer coating layer is mixed through the adhesive Bonding and curing; wherein, the particle diameter of the steel slag is 0.01-20mm, and the polymer coating is one or more of epoxy resin adhesive, acrylic resin adhesive and polyurethane adhesive; the adhesive is One or more of epoxy resin adhesive, acrylic resin adhesive and polyurethane adhesive. Use steel slag with a particle diameter of 0.01-20mm and a polymer to make particles with a polymer coating, and then use an adhesive to bond the steel slag with a polymer coating to form a building material with good water permeability. It can be applied to the production of building materials, realizing the recycling and utilization of steel slag. The polymer coating layer can significantly improve the interface ...

Embodiment 2

[0041] This embodiment provides a method for preparing a water-permeable functional brick, which includes mixing, molding and curing the steel slag according to the present invention and a polymer.

[0042] Specific steps include:

[0043] Step S1: performing particle size screening on the steel slag, and selecting steel slag with a particle diameter of 0.01-20 mm;

[0044] Step S2: processing the screened steel slag with a polymer coating;

[0045] Step S3: mixing the steel slag with the polymer coating layer and the adhesive;

[0046] Step S4: Pour the steel slag mixture in step S3 into a brick mold for molding;

[0047] The polymer coating is one or more of epoxy resin adhesive, acrylic resin adhesive and polyurethane adhesive; the adhesive is one or more of epoxy resin adhesive, acrylic resin adhesive and polyurethane adhesive kind.

[0048] Taking functional bricks as an example, in one embodiment, the adhesive is an epoxy resin adhesive. According to the preparation ...

Embodiment 3

[0057] (1) Preparation of steel slag that meets the particle size

[0058] According to the special physical and chemical characteristics of the steel slag, the steel slag is pre-crushed, baked and dried, magnetically separated and sieved, ground and crushed and classified, wet magnetic separation and classified, and the preferred grades are classified according to the particle size, and then passed through Special surface treatment activates the steel slag. The surface treatment can be ground or the chemical activator can be used to change the structure and shape of the tailing slag particles. The chemical activator can be prepared with acidic substances, and the surface of the steel slag can be treated with acidic substances to increase the surface area of ​​the steel slag. .

[0059] (2) Preparation of steel slag with polymer coating

[0060] 24g epoxy adhesive (18g is NPEL-127 epoxy resin, epoxy equivalent is 176-184g / eq; 2g is NPPN-431A70 epoxy resin; 4g is T31 curing ag...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a steel slag permeable building material and a manufacturing method thereof. The steel slag permeable building material comprises steel slag provided with a polymer coated layer and an adhesion agent, and the steel slag provided with the polymer coated layer is bonded in a mixed mode and solidified through the adhesion agent; the diameter of particles of the steel slag is 0.01-20 mm, and the polymer coated layer is one or more of epoxy resin, acrylic resin and polyurethane; the adhesion agent is one or more of an epoxy resin adhesion agent, an acrylic resin adhesion agent and a polyurethane adhesion agent. The steel slag with the particle diameter being 0.01-20 mm is in cooperation with polymer to be made into particles provided with the polymer coated layer, the steel slag provided with the polymer coated layer is bonded through the adhesion agent to form the building material which is good in water permeability, and recycling and utilization of the steel slag are achieved.

Description

technical field [0001] The invention relates to the technical field of environmental protection application of steel slag, and more specifically relates to a steel slag permeable building material and a manufacturing method thereof. Background technique [0002] At present, the global freshwater resources are becoming increasingly scarce, and scientifically and rationally obtaining and utilizing water resources is becoming an increasingly important research topic. Rainwater is one of the important ways for human beings to obtain fresh water resources. However, the cities where human beings live are mainly paved with impermeable materials such as granite, marble, glazed bricks, cement and asphalt, such as city squares, commercial streets, sidewalks, community activities and Occupied by hardened ground such as parking lots. When it rains, the hardened ground completely prevents rainwater from infiltrating directly into the ground, resulting in water accumulation on the road, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B26/16C04B20/10C04B18/14
CPCC04B20/1037C04B26/16C04B2111/00284C04B2201/50C04B18/142C04B24/281C04B24/28Y02W30/91
Inventor 赵建林徐社阳陆平韩建军
Owner 赵建林
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com