Polyester fabric foamed flame-retardant coating adhesive

A technology of flame-retardant coating and polyester fabric, which is applied in the direction of flame-retardant fibers, textiles, papermaking, fiber types, etc., can solve the problems that cannot meet the requirements of foaming finishing process, and achieve low production cost, wide application range, high efficiency effect

Inactive Publication Date: 2016-04-20
HANGZHOU FUYANG HONGXIANG TECH SERVICES CO LTD
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Chinese patent application number 93115328.X discloses a kind of flame retardant coating that can be used for fabric primer, and Chinese patent application number CN200480025533.X discloses a kind of flame retardant composition that is used for general fabric coating, but they can't satisfy foaming finishing process requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A foaming flame-retardant coating adhesive for polyester fabrics, characterized in that it comprises the following components by weight: 100 parts of matrix emulsion composed of 50 parts of vinyl acetate polymer and 50 parts of ethylene-vinyl acetate copolymer resin, three 10 parts of (2,3-dibromopropyl) isocyanurate, 5 parts of tri-(chloroisopropyl) phosphate, 1 part of associative water-based polyurethane emulsion, 5 parts of polyacrylate emulsion, gas phase two 2 parts of silicon oxide, 0.5 parts of silicone emulsion, 0.5 parts of linear alcohol sulfate, 1 part of sulfosuccinate, 0.3 parts of sulfosuccinamide, 6 parts of silicon nitrogen compound, ethylene oxide / propylene oxide block 5 parts of copolymer, 12 parts of modifying agent; 20 parts of wood fiber powder; 1 part of aluminate; Described modifying agent is made up of the raw material of following weight part:

[0022] Succinate 0.5, citric acid 0.5, ethylene glycol 4, glass fiber 4, jute fiber 2, wheat straw 2...

Embodiment 2

[0025] A foaming flame-retardant coating glue for polyester fabric, which comprises the following components by weight: 100 parts of matrix emulsion composed of 20 parts of vinyl acetate polymer and 80 parts of ethylene-vinyl acetate copolymer resin, three (2,3 -23 parts of dibromopropyl) isocyanurate, 8 parts of tri-(chloroisopropyl) phosphate, 3 parts of associative water-based polyurethane emulsion, 10 parts of polyacrylate emulsion, 4 parts of fumed silica , 1.0 parts of silicone emulsion, 2 parts of linear alcohol sulfate, 1.5 parts of sulfosuccinate, 0.8 parts of sulfosuccinamide, 16 parts of silicon nitrogen compound, 13 parts of ethylene oxide / propylene oxide block copolymer , 20 parts of modifying agent; 35 parts of wood fiber powder; 10 parts of aluminate; described modifying agent is made up of the raw material of following weight part:

[0026] Succinate 1, citric acid 1, ethylene glycol 8, glass fiber 8, jute fiber 4, wheat straw 4, silane coupling agent KH5500.5,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a polyester fabric foamed flame-retardant coating adhesive which comprises 100 parts of matrix emulsion composed of 20-50 parts of vinyl acetate polymer and 50-80 parts of ethylene-vinyl acetate copolymer resin, 10-23 parts of tri(2, 3-dibromopropyl) isocyanuric acid ester, 5-8 parts of tri(isopropyl chloride) phosphate, 1-3 parts of associative waterborne polyurethane emulsion, 5-10 parts of polyacrylate emulsion, 2-4 parts of fumed silica, 0.5-1.0 part of organic silicone emulsion and 0.5-2 parts of straight chain alcohol sulfate. The polyester fabric foamed flame-retardant coating adhesive has the advantages that a composite foamed flame-retardant coating adhesive system which has good flame-retardant effect is provided, and washing durability and mechanical resistance of the flame-retardant coating adhesive on fabric are improved.

Description

technical field [0001] The invention relates to a finishing agent for textiles, in particular to a foaming flame-retardant coating adhesive for polyester fabrics. Background technique [0002] With the continuous development of the textile industry, industrial and civil textiles have grown rapidly, and fires caused by textiles have also increased, threatening the safety of human life and property at all times. Therefore, the flame retardant function of textiles is extremely important to eliminate fire hazards, delay the spread of fire, and reduce the loss of human life and property. At present, industrially developed countries have formulated corresponding textile flame retardant standards and test methods, and some countries also combine textile flame retardant performance standards with relevant laws for enforcement. This has promoted the industrial departments and research departments of various countries to be engaged in textile flame retardant research in the past 20 y...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M23/04D06M15/333D06M15/564D06M15/263D06M15/53D06M15/643D06M11/79D06M11/78D06M13/256D06M13/364D06M13/298D06M13/262D06M15/01D06M101/32
CPCD06M23/04D06M11/78D06M11/79D06M13/256D06M13/262D06M13/298D06M13/364D06M15/01D06M15/263D06M15/333D06M15/53D06M15/564D06M15/643D06M2101/32D06M2200/30
Inventor 李程伟
Owner HANGZHOU FUYANG HONGXIANG TECH SERVICES CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com