Method for preparing cerium dioxide/two-dimensional layered titanium carbide composite material through hydrothermal process

A ceria, two-dimensional layered technology, applied in the field of hydrothermal preparation of ceria/two-dimensional layered titanium carbide composite materials, can solve the problems of small specific surface area, low performance, narrow application, etc., and achieve good light Simple and effective effect of catalytic performance, loading method

Active Publication Date: 2016-05-04
SHAANXI UNIV OF SCI & TECH
View PDF5 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Existing single MXene-Ti 3 C 2 , the specific surface area is small, the characteristics are very single, the performance is low, and the application is relatively narrow

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing cerium dioxide/two-dimensional layered titanium carbide composite material through hydrothermal process
  • Method for preparing cerium dioxide/two-dimensional layered titanium carbide composite material through hydrothermal process
  • Method for preparing cerium dioxide/two-dimensional layered titanium carbide composite material through hydrothermal process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Step 1, refine the powder

[0029] Refinement of ternary layered Ti with a purity greater than 97 wt% by high energy ball milling 3 AlC 2 Ceramic powder, ball milling conditions: the mass ratio of ball stone, mixing material and absolute ethanol is 10:1:1, the ball milling speed is 350r / min, the high energy ball milling time is 2h, and then the obtained solid-liquid mixture is baked at 40°C Dry, get Ti 3 AlC 2 ceramic powder;

[0030] Step 2, two-dimensional layered nanomaterial MXene-Ti 3 C 2 preparation of

[0031] Ti obtained in step 1 3 AlC 2 The ceramic powder is immersed in HF acid solution, in which 5gTi 3 AlC 2 The powder was immersed in 80ml mass concentration of 40wt% HF acid solution and reacted for 24h; magnetic stirring, the Ti 3 AlC 2 After the powder was corroded, it was centrifugally washed with deionized water until the pH was 6, and the obtained solid sample was dried at room temperature to obtain the two-dimensional layered nanomaterial MX...

Embodiment 2

[0037] Step 1, refine the powder

[0038] Refinement of ternary layered Ti with a purity greater than 97% by high energy ball milling 3 AlC 2 Ceramic powder, ball milling conditions: the mass ratio of ball stone, mixing material and absolute ethanol is 10:1:1, the ball milling speed is 350r / min, the high energy ball milling time is 2h, and then the obtained solid-liquid mixture is baked at 40°C Dry, get Ti 3 AlC 2 ceramic powder;

[0039] Step 2, two-dimensional layered nanomaterial MXene-Ti 3 C 2 preparation of

[0040] Ti obtained in step 1 3 AlC 2 The ceramic powder is immersed in HF acid solution, in which 5gTi 3 AlC 2 The powder was immersed in 80ml mass concentration of 40wt% HF acid solution and reacted for 24h; magnetic stirring, the Ti 3 AlC 2 After the powder was corroded, it was centrifugally washed with deionized water until the pH was 6, and the obtained solid sample was dried at room temperature to obtain the two-dimensional layered nanomaterial MXene-T...

Embodiment 3

[0046] Step 1, refine the powder

[0047] Refinement of ternary layered Ti with a purity greater than 97 wt% by high energy ball milling 3 AlC 2 Ceramic powder, ball milling conditions: the mass ratio of ball stone, mixing material and ball milling medium is 10:1:1, the ball milling speed is 350r / min, the high energy ball milling time is 2h, and then the obtained solid-liquid mixture is dried at 40°C , get Ti 3 AlC 2 ceramic powder;

[0048] Step 2, two-dimensional layered nanomaterial MXene-Ti 3 C 2 preparation of

[0049] Ti obtained in step 1 3 AlC 2 The ceramic powder is immersed in HF acid solution, in which 5gTi 3 AlC 2 The powder was immersed in 80ml mass concentration of 40wt% HF acid solution and reacted for 24h; magnetic stirring, the Ti 3 AlC 2 After the powder was corroded, it was centrifugally washed with deionized water until the pH was 6, and the obtained solid sample was dried at room temperature to obtain the two-dimensional layered nanomaterial MX...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a method for preparing a cerium dioxide / two-dimensional layered titanium carbide composite material through a hydrothermal process. The method comprises the following steps: high-energy ball milling and crystal grain refinement so as to obtain high-purity three-component layered Ti3AlC2 powder; preparation of two-dimensional layered nano-material MXene-Ti3C2 through hydrofluoric acid corrosion; and formation of CeO2 on the surface and interlayers of MXene-Ti3C2 through the hydrothermal process so as to allow CeO2 to be loaded with MX3ne-Ti3C2, thereby obtaining the CeO2 / MXene-Ti3C2 nanocomposite material. The method has the advantages of simple process, controllable technology and low cost; and the prepared nanocomposite material has the characteristics of uniform lamellas of the two-dimensional layered MXene-Ti3C2, uniform distribution of CeO2 and the like and the advantages of a large specific surface area, good conductivity and good photocatalysis performance, which facilitates application of the nanocomposite material in fields like photocatalysis, lithium ion batteries and supercapacitors.

Description

technical field [0001] The invention belongs to the technical field of inorganic nanocomposite materials, in particular to a method for preparing ceria / two-dimensional layered titanium carbide composite materials by a hydrothermal method. Background technique [0002] Ternary layered ceramic material Ti 3 AlC 2 It belongs to layered hexagonal crystal structure. at Ti 3 AlC 2 In the crystal structure, Ti and C atoms form Ti 6 The C octahedron is separated by the Al layer, and the C atom is located in the center of the octahedron. The combination of C and Ti atoms is a strong covalent bond, while Ti-Ti, and between Ti and Al are weakly bonded, similar to the bond between graphite Van der Waals weak bonds. [0003] Ti 3 AlC 2 It has both the properties of metal and ceramics. At room temperature, it has thermal conductivity and electrical conductivity, as well as low Vickers microhardness and high elastic modulus. It can be machined like metal, and can be processed at hi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J27/22B01J37/03B01J37/10B82Y30/00B82Y40/00
CPCB01J27/22B01J37/035B01J37/10B82Y30/00B82Y40/00
Inventor 朱建锋周文静汤祎曹敏娟吕文静任莹莹鹿萧
Owner SHAANXI UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com