High-strength asphalt mixture and preparation method thereof

A technology of asphalt mixture and asphalt binder, applied in the field of asphalt, can solve the problems of reducing the service life of pavement, low hardness of limestone, low intensity of asphalt, etc., and achieve the effects of prolonging the service life, improving the waterproofness of the pavement, and improving the quality of the pavement

Inactive Publication Date: 2016-05-11
SICHUAN GUOXING POLYMER RESIN CO LTD
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The currently commonly used asphalt has low strength. After years of use, the road surface is prone to ruts, dents, cracks and even breaks, causing traffic hazards and greatly reducing the service life of the road surface. At the same time, the asphalt pavement is exposed to moisture. Under the repeated action of traffic load and temperature expansion and contraction, water intrusion, the asphalt film gradually peels off from the aggreg

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0059] Example 1

[0060] (1) Aggregate treatment: the limestone and alkaline granite are respectively processed by a crusher, and coarse aggregates with a particle size of 20-35mm are selected, and part of the crushed limestone is crushed by a sand making machine, and the particle size is 1 -4.5mm fine aggregate spare;

[0061] (2) Material preparation: weigh 18.35% of elastic resin, asbestos lint 3.20%, waste rubber 36.00%, rosin 14.00%, water reducing agent 0.20%, paraffin 1.85%, diacetone alcohol 7.10%, stearamide 0.30 % After mixing thoroughly, heat up to 100-120 degrees Celsius;

[0062] (3) Add 0.30% emulsifier and 0.40% palmitic acid to the mixture obtained in step (2), and mix and react for 10-30 minutes;

[0063] (4) Weigh 0.60% fiber stabilizer, mix it with 0.25% silica with a fineness of 400-450 mesh, heat the material obtained in step (3) to 195 degrees Celsius, add silica-mixed fiber stabilizer Mix well;

[0064] (5) Reduce the temperature of the mixture obtained in ste...

Example Embodiment

[0066] Example 2

[0067] (1) Aggregate treatment: the limestone and alkaline granite are respectively processed by a crusher, and coarse aggregates with a particle size of 20-35mm are selected, and part of the crushed limestone is crushed by a sand making machine, and the particle size is 1 -4.5mm fine aggregate spare;

[0068] (2) Material preparation: weigh 20.00% of elastic resin, 4.50% of asbestos wool, 32.00% of waste rubber, 15.00% of rosin, 0.52% of water reducing agent, 3.20% of paraffin, 7.05% of diacetone alcohol, and 0.45 of stearamide % After mixing thoroughly, heat up to 100-120 degrees Celsius;

[0069] (3) Add 0.42% emulsifier and 0.48% palmitic acid to the mixture obtained in step (2), and mix and react for 10-30 minutes;

[0070] (4) Weigh 0.85% fiber stabilizer, mix it with 0.40% silica with a fineness of 400-450 mesh, heat the material obtained in step (3) to 195 degrees Celsius, add silica-mixed fiber stabilizer Mix well;

[0071] (5) The temperature of the mixtu...

Example Embodiment

[0073] Example 3

[0074] (1) Aggregate treatment: the limestone and alkaline granite are respectively processed by a crusher, and coarse aggregates with a particle size of 20-35mm are selected, and part of the crushed limestone is crushed by a sand making machine, and the particle size is 1 -4.5mm fine aggregate spare;

[0075] (2) Material preparation: weigh 21.40% of elastic resin, asbestos lint 5.00%, waste rubber 28.00%, rosin 17.00%, water reducing agent 0.50%, paraffin wax 3.00%, diacetone alcohol 7.20%, stearamide 0.80 % After mixing thoroughly, heat up to 100-120 degrees Celsius;

[0076] (3) Add 0.70% emulsifier and 0.80% palmitic acid to the mixture obtained in step (2), and mix and react for 10-30 minutes;

[0077] (4) Weigh 1.20% fiber stabilizer, mix it with 0.50% silica with a fineness of 400-450 mesh, heat the material obtained in step (3) to 195 degrees Celsius, add the fiber stabilized with silica Mix well;

[0078] (5) Reduce the temperature of the mixture obtained...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-strength asphalt mixture and a preparation method thereof. The asphalt mixture comprises the components of elastic resin, waste rubber, rosin, diacetone alcohol, asbestos wool, a water reducer, paraffin, epoxy resin, stearamide, a curing agent, palmitic acid, an emulsifier, a fiber stabilizer, and silicon dioxide. The main method of a preparation process comprises: crushing and heating limestone and alkali granite, and then mixing the crushed materials with a premixed and preheated asphalt binding material for full reaction. The asphalt mixture has the characteristics of good toughness, high strength, water resistance, corrosion resistance, low toxicity and environmental friendliness, and can effectively prolong the service life of an asphalt pavement.

Description

technical field [0001] The invention relates to the field of asphalt, in particular to a high-strength asphalt mixture and a preparation method thereof. Background technique [0002] Asphalt is widely used in highway pavement structure due to its excellent adhesion and thermoplasticity. At present, the asphalt used in highway pavement is mostly a mixture of asphalt and concrete, which is mixed, paved and solidified at high temperature or normal temperature. The currently commonly used asphalt has low strength. After years of use, the road surface is prone to ruts, dents, cracks and even breaks, causing traffic hazards and greatly reducing the service life of the road surface. At the same time, the asphalt pavement is exposed to moisture. Under the repeated action of traffic load and temperature expansion and contraction, water intrusion, the asphalt film gradually peels off from the aggregate surface and is damaged, and the conventional asphalt raw materials often contain t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B26/26C04B14/28C04B14/04C04B20/00C04B16/02C04B24/02C04B24/12C04B24/08
CPCC04B26/26C04B2111/0075
Inventor 王洪魏道新陈景郭朝阳
Owner SICHUAN GUOXING POLYMER RESIN CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap