A kind of uv mixing powder glue and its preparation method and application

A technology of powder-mixing glue and light-curing monomer, which is applied in the direction of adhesives, etc., can solve the problems of high-temperature yellowing resistance, poor weather resistance, insufficient toughness, and low light transmittance, achieve high refractive index, improve toughness, and solve The effect of high energy consumption

Active Publication Date: 2017-03-29
SUMDA MATERIAL TECH CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing UV adhesives currently on the market have defects such as high-temperature yellowing resistance, poor weather resistance, low light transmittance, and insufficient toughness, which cannot fully meet the requirements of LED packaging adhesives.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0056] Preparation of main body UV resin:

[0057] According to the formula shown in Table 1, add isocyanate, polymerization inhibitor and catalyst into the reaction vessel, add cyclohexanedimethanol, control the reaction temperature at 50°C, and the reaction time is 4h. The measured NCO% reaches the theoretical value of 4%-11 %, add hydroxypivalate hydroxypivalate, react at 60°C for 3 hours, measure NCO% and reach the theoretical value of 2%-8%, then add hydroxyethyl acrylate, react at 50°C for 3 hours, and detect After the NCO% is less than 1%, the material is discharged, and the main UV resin is obtained;

[0058] Table 1 A 1 ~ A6, C1-C3 main body UV resin (parts by weight)

[0059] A1 A2 A3 A4 A5 A6 C1 C2 HDI 20 50 60 80 50 IPDI 40 70 40 BHT 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 Organic Bismuth Catalyst 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 Cyclohexanedimethanol 20 40 50 60 70 80 hydroxyp...

Embodiment 1-5 and comparative example 1-2

[0065] According to the formula shown in Table 3, add the photocurable monomer and the silicon-modified photocurable monomer obtained above into the reactor, stir and add the photoinitiator at the same time, heat to 50 ° C, stir for 1 hour, and then add the main body obtained above Continue to stir the UV resin for 2 hours, remove the air bubbles in a vacuum, filter with a 400-mesh filter cloth, and centrifuge to obtain the UV powder mixing glue. The obtained UV powder mixing glue was applied according to the traditional silica gel dispensing method, and after UV curing, the packaged LED lamp beads were obtained, and its various properties were tested. The results are shown in Table 3.

[0066] Table 3 The composition and performance results of each component of the embodiment and the comparative example

[0067] Example 1 Example 2 Example 3 Example 4 Example 5 Comparative example 1 Comparative example 2 Main body UV resin A1 30 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
refractive indexaaaaaaaaaa
transmittivityaaaaaaaaaa
Login to view more

Abstract

The invention discloses UV powder mixed silica gel and a preparation method and application thereof. The UV powder mixed silica gel comprises 30-50 parts of UV resin serving as a main body, 25-40 parts of silicon-modified photocuring monomer, 25-40 parts of photocuring monomer and 1-8 parts of photoinitiator. The UV powder mixed silica gel can be resistant to the high temperature of 280 degrees without yellowing, the high refractive index is achieved, furthermore, quite good toughness and air-tightness are achieved, and the problem that due to raising of the refractive index of traditional powder mixed silica gel, an adhesive layer is hardened, so that chalking occurs easily in the using process is effectively avoided; energy consumption is greatly lowered, the curing time is only 1 / 1800 that of the traditional powder mixed silica gel, the defects that the traditional powder mixed silica gel is high in energy consumption, long in curing time and the like are effectively overcome, and productivity is greatly improved.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a UV powder mixing glue and its preparation method and application. Background technique [0002] LED packaging glue is a kind of glue that covers the LED lamp bead. Its function is to protect the LED lamp bead. At present, the powder mixing glue for LED lamp bead packaging is basically two-component silica gel or two-component epoxy glue. Their curing conditions are generally baked in a high-power electric oven at 150°C for 5 hours, which consumes a lot of energy. At the same time, each batch of lamp beads needs to be baked for about 5 hours, and its efficiency is very low. In addition, the refractive index of the traditional powder-mixed silica gel is relatively low, and the increase of the refractive index usually causes the hardening of the adhesive layer, which makes it easy to pulverize during use. [0003] UV glue is mainly composed of base resin, active monomer...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08F299/06C09J153/00C08F220/28C08F220/18C08F220/06C08G18/32C08G18/67
CPCC08F220/18C08F220/28C08F299/06C08G18/3212C08G18/3221C08G18/672C09J153/00C08F220/06
Inventor 赵东理
Owner SUMDA MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap