High-blackness Huizhou ink stick and preparation method thereof

A technology of blackness and Hui ink, which is applied in the field of Hui ink with high blackness and its preparation, can solve problems such as uneven blackness, insufficient color and brightness, and complex production techniques of Hui ink, and achieve long storage life, bright color and uniform handwriting Effect

Inactive Publication Date: 2016-06-08
HUANGSHAN GUCHENG SHEZHOU INKSTONE CO LTD
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The production techniques of Hui ink are complicated, and different genres have their own unique production techniques, which cannot be passed on to the outside world.
[0003] When traditional Hui ink is written on some paper, the blackness will appear uneven, and after a period of time, the color and brightness will not be enough

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] In the embodiment of the present invention, a kind of Hui ink with high blackness is composed of the following raw materials in parts by weight: 26 parts of tobacco, 2.9 parts of olive oil, 0.15 parts of kettle navel ink, 1.2 parts of Myrobalan extract, 1 part of Luokui extract parts, 0.6 parts of juniper berry extract, and 27 parts of peach gum.

[0019] The preparation method is as follows:

[0020] 1) Preparation of myrobalan extract: dry and grind myrobalan under constant temperature and reduced pressure, and then sieve with 85 meshes to obtain dried myrobalan powder for later use; add water with 4 times the mass of myrobalan dry powder, and then add 12% of myrobalan dry powder pectinase was stirred at 45°C for 2 hours to obtain an enzymatic hydrolysis solution, and then the enzymolysis solution was subjected to ultrasonic treatment, the ultrasonic treatment power was 1000W, the ultrasonic treatment time was 58min, and the centrifugation treatment was performed 3 ti...

Embodiment 2

[0025] In the embodiment of the present invention, a Hui ink with high blackness is composed of the following raw materials in parts by weight: 24 parts of pine smoke, 2 parts of olive oil, 0.123 parts of kettle navel ink, 1.1 parts of myrobalan extract, and Luo Kui extract 0.6 parts, 0.5 parts of juniper berry extract, 28 parts of peach gum.

[0026] Example 1 of the preparation method of Hui ink with high blackness.

Embodiment 3

[0028] In the embodiment of the present invention, a kind of Hui ink with high blackness is composed of the following raw materials in parts by weight: 28 parts of pine smoke, 3.7 parts of olive oil, 0.15 parts of kettle navel ink, 1 part of Myrobalan extract, and Luo Kui extract 0.8 parts, 0.9 parts of juniper berry extract, 27 parts of peach gum.

[0029] Example 1 of the preparation method of Hui ink with high blackness.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses high-blackness a Huizhou ink stick and a preparation method thereof. The Huizhou ink stick is composed of, by weight, 22-28 parts of pine soot, 1-5 parts of olive oil, 0,12-0.18 part of pot soot, 1-1.6 parts of Fructus chebulae extract, 0.5-1.6 parts of Basella rubra extract, 0.4-1.1 parts of juniper berry extract and 22-30 parts of peach gum. The high-blackness Huizhou ink has the advantages of high hardness, less proneness to breaking, bright color, high blackness, high stability, high light resistance and quickness in drying after writing, and is convenient to grind, smooth in writing and wielding, uniform in writing trace and long in storage life.

Description

technical field [0001] The invention relates to the technical field of ink, in particular to Hui ink with high blackness and a preparation method thereof. Background technique [0002] Ink is an ink ingot used in ancient Chinese writing and painting. The main raw materials of ink are carbon black, pine smoke, glue, etc., and the carbon element exists in an amorphous form. The ink used for brush writing can be produced by grinding the inkstone with water, which exists as a colloidal solution in water. Among them, Hui ink is a treasure in the ink-making skills of the Han nationality in China, and it is also one of the "Four Treasures of the Study" well-known both at home and abroad. It got its name because it was produced in the ancient Huizhou Prefecture. Hui ink is a kind of special pigment mainly used in traditional calligraphy and painting, which is made of pine smoke, tung oil smoke, lacquer smoke and glue as the main raw materials. It is refined through the processes...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D11/16
CPCC09D11/16
Inventor 胡秋生
Owner HUANGSHAN GUCHENG SHEZHOU INKSTONE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com