Mosquito-repellent incense preparation method

A mosquito coil and sludge carbon technology is applied in the fields of botanical equipment and methods, preservation of human or animal bodies, resistance to vector-borne diseases, etc., to achieve the effects of being conducive to environmental protection, smooth appearance, and reducing difficulty

Inactive Publication Date: 2016-06-15
庞用
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] The invention provides a preparation method of mosquito-repellent incense to solve the problem of deforestation according to the ingredients of existing mosquito-repellent incense and the large amount of deforestation in the preparation process, as well as the use of a large amount of adhesives such as carboxymethyl cellulose and polyacrylamide to bring a lot of environmental protection and health problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0036] In an embodiment, the preparation method of mosquito-repellent incense, comprises the following steps:

[0037] S1: After the sludge is dried at 106-110°C for 20-23h, under the protection of nitrogen or carbon dioxide, the temperature is raised to 500-600°C at a rate of 20-25°C / min, carbonized for 0.6-1h, and cooled to obtain Sludge carbon, after the sludge carbon is crushed through a 60-80 mesh sieve, sludge carbon powder is obtained;

[0038] S2: Take 100-200 parts of sludge carbon powder prepared in step S1, 4-8 parts of anthracite, 16-32 parts of binder, 4-6 parts of mica powder, and 350-500 parts of water, at a temperature of 60-70 °C, stirring at a speed of 200-300r / min for 1-2h to obtain a paste;

[0039] S3: Put the paste prepared in step S2 into a mold, compact and demould, and then dry at 45-55°C until the water content is ≤10%, to obtain a dry mosquito coil;

[0040] S4: Spray the mosquito coil lotion evenly on the surface of the dried mosquito coil prepare...

Embodiment 1

[0049] A preparation method for mosquito-repellent incense, comprising the following steps:

[0050] S1: After drying the sludge at 106°C for 23 hours, under the protection of nitrogen, raise the temperature to 500°C at a heating rate of 20°C / min, carbonize for 1 hour, obtain sludge carbon after cooling, and pulverize the sludge carbon Sludge carbon powder is obtained after passing through a 60-mesh sieve;

[0051] S2: Take 100 parts of sludge carbon powder, 4 parts of anthracite, 16 parts of binder, 4 parts of mica powder, and 350 parts of water prepared in step S1, and stir for 2 hours at a temperature of 60 °C and a speed of 200 r / min to prepare get a paste;

[0052] S3: Put the paste prepared in step S2 into a mold, compact and demould, and then dry at 45°C until the water content is 10%, to obtain a dry mosquito coil;

[0053] S4: Spray the mosquito-repellent incense potion evenly on the surface of the dried mosquito-repellent coil prepared in step S3, and dry at 30° C....

Embodiment 2

[0061] A preparation method for mosquito-repellent incense, comprising the following steps:

[0062] S1: After the sludge was dried at 110°C for 20 hours, under the protection of nitrogen or carbon dioxide, the temperature was raised to 600°C at a heating rate of 25°C / min, carbonized for 0.6h, and sludge carbon was obtained after cooling. Carbon pulverized through 80 mesh sieve to obtain sludge carbon powder;

[0063] S2: Take 200 parts of sludge carbon powder, 8 parts of anthracite, 32 parts of binder, 6 parts of mica powder, and 500 parts of water prepared in step S1, and stir for 1 hour at a temperature of 70 °C and a speed of 300 r / min to prepare get a paste;

[0064] S3: Put the paste prepared in step S2 into a mold, compact and demould, and then dry at 55°C until the moisture content is 8%, so as to obtain a dry mosquito coil;

[0065] S4: Spray the mosquito coil lotion evenly on the surface of the dried mosquito coil prepared in step S3 and dry at 35° C. with a water ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a mosquito-repellent incense preparation method and belongs to the technical field of mosquito-repellent incense preparation. Mosquito-repellent incense is prepared according to the steps of preparing sludge carbon powder, preparing paste, molding the paste prior to drying, subjecting mosquito-repellent incense dry bodies to chemical spraying and the like. The mosquito-repellent incense preparation method has the advantages that sludge carbon serves as a combustion agent, inorganic substances in the sludge carbon serve as a fire retardant, and accordingly a novel approach is provided for resource utilization of the sludge carbon, a great quantity of deforestation in the mosquito-repellent incense industry is avoided, and environmental protection is benefited. The mosquito-repellent incense prepared by the preparation method has the advantages that the mosquito-repellent incense is poisonless and harmless, thereby being capable of meeting the requirements of environmental protection; after being combusted, the mosquito-repellent incense cannot cause asthma, neurotoxicity and cancers after being absorbed by human bodies; the mosquito-repellent incense is smooth in appearance and free of fracture and mildew spots, fracture resistance reaches 423-456g, combustion point time reaches 8.81-9.23 hours, a smoke-free combustion process is achieved, and 'end broken' extinction when the mosquito-repellent incense passes by an iron-tooth tray is avoided.

Description

technical field [0001] The invention belongs to the technical field of mosquito-repellent incense preparation, and in particular relates to a preparation method of mosquito-repellent incense. Background technique [0002] Municipal sludge is the solid matter separated during the treatment of domestic sewage. These solid substances may already exist in sewage, such as suspended substances intercepted in various natural sedimentation tanks; they may also be transformed during sewage treatment, such as biological treatment and chemical treatment, from the original dissolved substances and colloids Biological flocs and suspended matter derived from material transformation. But generally speaking, the sludge of urban sewage treatment plants belongs to organic sludge, which is characterized by high organic matter content (60%-80%), fine particles (0.02-0.2mm), and low density (1.002-1.006g / cm 3 ), into a colloidal structure, accounting for about 0.3%-0.5% of the total treated wa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A01N25/20A01N65/22A01N53/10A01N31/02A01P7/04A01P17/00
CPCA01N25/20A01N31/02A01N53/00A01N65/00A01N65/22A01N2300/00Y02A50/30
Inventor 庞用
Owner 庞用
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com