TPE (thermoplastic elastomer) foamed master batch and preparation method thereof

A thermoplastic elastomer and foaming masterbatch technology, applied in the field of thermoplastic elastomer TPE foaming masterbatch and its preparation, can solve the problems of poor slip resistance, inability to recycle, insufficient adhesion, etc., and achieve high elasticity to absorb and wrap oil, Good absorption and wrapping oil, improve strength and toughness effect

Inactive Publication Date: 2016-06-22
FUZHOU HAOWANG MATERIALS TECH CO LTD
View PDF4 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0014] However, the shoe material made of the thermoplastic elastomer shoe material masterbatch has insufficient tensile strength, insufficient adhesion, poor tensile strength, insufficient wear resistance, poor anti-slip performance, high hardness, poor resilience, and no rubber texture. In terms of usage, it is only suitable for insoles, not for outsoles
[0015] The thermoplastic elastomer is actually a kind of EVA modified body. Its compression is high, its elastic performance is not even as good as EVA, and its application range is narrow. become worse, and the production process is complicated, and the product is a disposable material that cannot be recycled

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • TPE (thermoplastic elastomer) foamed master batch and preparation method thereof
  • TPE (thermoplastic elastomer) foamed master batch and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0060] A thermoplastic elastomer TPE foaming masterbatch, prepared from the following raw materials according to the following weight ratio:

[0061] Styrene butadiene block copolymer SBS20 parts

[0062] Ethylene octene block copolymer POE20 parts

[0063] 55 parts of white oil

[0064] Microsphere foaming agent 50 parts

[0065] 30 parts of chemical foaming agent

[0066] 2 parts lubricant

[0067] 2 parts of dispersant.

[0068] A method for preparing thermoplastic elastomer TPE foam masterbatch, the process is as follows:

[0069] First weigh the styrene butadiene block copolymer SBS according to the above ratio and put it in the mixer, slowly add white oil, stir for 25 minutes, add ethylene octene block copolymer POE, stir for another 5 minutes, then add Microsphere foaming agent, chemical foaming agent, lubricant and dispersant, stirred for 20 minutes, discharged, and then granulated by a double-stage extruder at an extrusion temperature of 110°C to obtain a TPE foam...

Embodiment 2

[0071] A thermoplastic elastomer TPE foaming masterbatch, prepared from the following raw materials according to the following weight ratio:

[0072] Styrene butadiene block copolymer SBS10 parts

[0073] Ethylene octene block copolymer POE30 parts

[0074] 30 parts white oil

[0075] Microsphere foaming agent 80 parts

[0076] 50 parts of chemical foaming agent

[0077] 3 parts lubricant

[0078] 3 parts of dispersant.

[0079] A method for preparing thermoplastic elastomer TPE foam masterbatch, the process is as follows:

[0080] First weigh the styrene butadiene block copolymer SBS according to the above ratio and put it in the mixer, slowly add white oil, stir for 15 minutes, add ethylene octene block copolymer POE, stir for another 4 minutes, then add Microsphere foaming agent, chemical foaming agent, lubricant and dispersant, stirred for 15 minutes, discharged, and then granulated by a double-stage extruder at an extrusion temperature of 70°C to obtain a TPE foam m...

Embodiment 3

[0082] A thermoplastic elastomer TPE foaming masterbatch, prepared from the following raw materials according to the following weight ratio:

[0083] Styrene butadiene block copolymer SBS30 parts

[0084] Ethylene octene block copolymer POE10 parts

[0085] 80 parts white oil

[0086] Microsphere foaming agent 20 parts

[0087] 10 parts chemical blowing agent

[0088] 1 part lubricant

[0089] 3 parts of dispersant.

[0090] A method for preparing thermoplastic elastomer TPE foam masterbatch, the process is as follows:

[0091] First weigh the styrene butadiene block copolymer SBS according to the above ratio and place it in the mixer, slowly add white oil, stir for 30 minutes, add ethylene octene block copolymer POE, stir for another 6 minutes, then add Microsphere foaming agent, chemical foaming agent, lubricant and dispersant, stirred for 30 minutes, discharged, and then granulated by a double-stage extruder at an extrusion temperature of 120°C to obtain a TPE foam ma...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to TPE (thermoplastic elastomer) foamed master batch and a preparation method thereof and belongs to the field of new chemical materials. The TPE foamed master batch is prepared from raw materials in parts by weight as follows: 10-30 parts of a styrene-butadiene block copolymer, 10-30 parts of an ethylene-octylene block copolymer, 30-80 parts of white oil, 20-80 parts of a microsphere foaming agent, 10-50 parts of a chemical foaming agent, 1-3 parts of a lubricating agent and 1-3 parts of a dispersing agent. The prepared TPE foamed master batch has high modulus, fine and uniform foam holes and adjustable density.

Description

technical field [0001] The invention relates to a thermoplastic elastomer TPE foam masterbatch and a preparation method thereof, belonging to the field of new chemical materials. Background technique [0002] Thermoplastic elastomer (Thermoplasticlastomer, TPE) is usually an elastic material with a low elastic modulus, which can be repeatedly stretched to more than twice its original length at room temperature, and has the ability to almost completely return to its original length after stress relief. ability. [0003] Thermoplastic elastomer TPE is a kind of rubber with high elasticity, high strength, high resilience, and has the characteristics of injection molding processing. It is environmentally friendly, non-toxic and safe, with a wide range of hardness, soft touch, weather resistance, fatigue resistance and temperature resistance. It can be re-injected, coated and bonded with PP, PE, PC, PS, ABS and other base materials, or molded separately. At present, thermoplast...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L91/00C08L23/08C08L53/02C08L91/06C08K13/02C08K3/22C08K3/34C08K5/098C08K5/20C08J9/32C08J9/10
CPCC08J9/103C08J9/32C08J2323/08C08J2391/00C08L23/0815C08L91/00C08L2205/03C08L2205/035C08L53/02C08K13/02C08K5/09C08K2003/2241C08K3/34C08K5/098C08K5/20C08L91/06
Inventor 张伙生
Owner FUZHOU HAOWANG MATERIALS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com