A technology of welding wire and forging billet, which is applied in the field of steel ingot and its smelting, and the preparation of solid welding wire for gas shielded arc welding, which can solve the problems of alloy steel plasticity and toughness decrease and process difficulties

Inactive Publication Date: 2016-07-06
天津冶金集团天材科技发展有限公司
View PDF7 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0014] The welding wire in this case is an innovation based on the existing H1Cr21Ni10Mn6 welding wire, including adding an appropriate amount of Mo and increasing the content of Mn correspondingly. The problem is that the change of the material composition will bring technical difficulties to the later production. It is generally known that, When the content of molybdenum in alloy s

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Forging method for producing 21-10Mn7Mo welding wire and blank forged by same
  • Forging method for producing 21-10Mn7Mo welding wire and blank forged by same
  • Forging method for producing 21-10Mn7Mo welding wire and blank forged by same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0092] Below in conjunction with preferred embodiments, the specific implementation, features and effects provided by the present invention are described in detail as follows; for the purpose of simplicity and clarity, the description of known technologies is appropriately omitted below to avoid unnecessary details Affect the description of this technical solution.

[0093] A forging method of 21-10Mn7Mo welding wire and a forging blank prepared by the method. The quoted unit of material composition is mass %. Quantities and value units that are not specifically described are in line with the general regulations and customary usage of the industry, and will not be repeated.

[0094] 1. The forging method of the 21-10Mn7Mo welding wire, wherein the chemical composition mass % of the 21-10Mn7Mo steel ingot should satisfy: carbon C≤0.10, silicon Si≤0.8, manganese Mn5.5-8.0, phosphorus P≤0.030, sulfur S ≤0.020, nickel Ni9.0-11.0, chromium Cr19.0-22.0, molybdenum Mo0.5-2.0, or / an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A forging method for producing a 21-10Mn7Mo welding wire and a blank forged by the method belong to the technical field of welding, relate to the production of a solid welding wire used for gas-shielded arc welding, a forging method, a component forged by the method and a hot-rolling technology and further relate to a steel ingot and the smelting thereof. The forged blank comprises the following chemical components in a percent by mass: smaller than or equal to 0.10 of C, smaller than or equal to 0.8 of Si, 5.5-8.0 of Mn, smaller than or equal to 0.030 of P, smaller than or equal to 0.020 of S, 9.0-11.0 of Ni, 19.0-22.0 of Cr and 0.5-2.0 of Mo, wherein the ratio of Mn to Mo is controlled between 7 and 7.5. The forging step adopted for producing the forged blank comprises the step of heating a blank, and forging temperature is controlled in a way that initial forging temperature is higher than or equal to 1180 DEG C and final forging temperature is higher than or equal to 850 DEG C. The smelting step of a forged steel ingot comprises the technical step of using an electric-arc furnace return oxygen blowing process to smelt an electroslag re-melted electrode.

Description

technical field [0001] This case belongs to the field of welding technology, and involves the preparation method of solid wire for gas-shielded arc welding, its intermediate and finished products, and its process equipment. It involves a forging method and its forged parts, as well as a hot rolling process, and also involves a steel ingot and its smelting. Background technique [0002] Stainless steel welding wire and welding rod are used more and more in automation technology, but the common quality problems of stainless steel welding wire prepared by existing technologies are that the appearance of the welding wire is not good, and the wire feeding is not stable enough, so it is difficult to meet the requirements of high-automation welding equipment. [0003] It is generally known that the quality of welding wire is closely related to the subtle changes in chemical composition caused by steelmaking, and has a close relationship with the impurity content of material compone...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B21J5/00B21B1/16C22C38/58C22C33/04
Inventor 于庆莲韩萍薛玉宝蔡玉丽张永泉厉海艳于湘
Owner 天津冶金集团天材科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap