Glass cleaning anti-fogging agent and preparation method thereof

An anti-fogging and cleaning technology, applied in chemical instruments and methods, detergent compounding agents, other chemical processes, etc., can solve the problems of poor functionality of anti-fogging cleaning agents, etc., and is suitable for large-scale industrial production applications, The effect of low price of raw materials and simple preparation process

Inactive Publication Date: 2016-07-06
HENAN UNIV OF URBAN CONSTR
View PDF7 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the functionality of the anti-fog cleaners in the above two patents is still not good enough, and the anti-fog and cleaning effects need to be further improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] In this embodiment, the glass cleaning antifogging agent is made from the following raw materials by mass fraction: 8 parts of Sapindus japonica, 5 parts of saponin, 0.5 part of sodium lauryl sulfate, fatty alcohol polyoxyethylene ether (C 12 , AEO-9) 0.2 part, alkyl glycoside 0.1 part, cocamidopropyl hydroxysulfobetaine 0.1 part, water 65 parts.

[0024] The preparation steps of the glass cleaning antifogging agent are as follows:

[0025] 1) Accurately take each raw material according to the parts by mass, pulverize the dried (80°C) Sapindus bark and saponin, then sieve (10 mesh sieve), add water to soak and extract for 1 hour, filter, and take the filtrate for later use, the filtrate is plant extract;

[0026] 2) The remaining raw materials are added to the filtrate and mixed evenly to obtain a glass cleaning and antifogging agent.

Embodiment 2

[0028] In this embodiment, the glass cleaning antifogging agent is made from the following raw materials by mass fraction: 11 parts of Sapindus japonica, 9 parts of saponin, 0.3 part of sodium dodecylbenzenesulfonate, fatty alcohol polyoxyethylene ether (C 16 , AEO-9) 0.4 parts, coco acid diethanolamide 0.5 parts, alkyl glycosides 0.3 parts, lauramidopropyl hydroxysulfobetaine 0.3 parts, polyethylene glycol 0.4 parts, anhydrous ethanol 3 parts, water 75 parts share.

[0029] The preparation steps of the glass cleaning antifogging agent are as follows:

[0030] 1) Accurately take each raw material according to the parts by mass, pulverize the dried (100°C) Sapindus japonica and saponin, and then sieve (20 mesh sieve), add in water, soak and extract for 1.5 hours, filter, and take the filtrate for later use. The filtrate is It is plant extract;

[0031] 2) The remaining raw materials are added to the filtrate and mixed evenly to obtain a glass cleaning and antifogging agent. ...

Embodiment 3

[0033] In this embodiment, the glass cleaning antifogging agent is made from the following raw materials by mass: 15 parts of Sapindus japonica, 12 parts of saponin, 0.3 parts of sodium dodecylbenzenesulfonate, and 0.3 parts of sodium lauryl sulfate , fatty alcohol polyoxyethylene ether (C 12 , AEO-9) 2 parts, 0.1 part of lauramidopropyl hydroxysulfobetaine, 0.1 part of lauramidopropyl betaine, 0.5 part of polyethylene glycol, 5 parts of absolute ethanol, and 85 parts of water.

[0034] The preparation method of the glass cleaning antifogging agent is the same as that in Example 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a glass cleaning anti-fogging agent and a preparation method thereof, and belongs to the technical field of fine chemical engineering. The cleaning anti-fogging agent is prepared from, by mass, 8-15 parts of peels of Chinese soapberry fruit, 5-12 parts of Chinese honeylocust fruit, 0.5-1 part of anionic surfactant, 0.5-2 parts of non-ionic surfactant, 0.1-0.4 part of zwitterionic surfactant, 0-0.8 part of thickening agent, 0-5 parts of quick-drying agent and 65-85 parts of water. According to the glass cleaning anti-fogging agent and the preparation method thereof, peels of Chinese soapberry fruit and an extraction solution of Chinese honeylocust fruit are compounded with the anionic surfactant, the non-ionic surfactant and the zwitterionic surfactant, all the materials can synergistically exert the anti-fogging and cleaning and decontamination functions, and the glass cleaning anti-fogging agent has a significant anti-fogging effect on the glass surface, can effectively remove dirt attached to the surface and is safe, environmentally friendly and harmless to human bodies; meanwhile, the raw materials are low in price, the production cost is low, and the glass cleaning anti-fogging agent is suitable for large-scale industrial production and application.

Description

technical field [0001] The invention relates to a glass cleaning antifogging agent, and also relates to a preparation method of the cleaning antifogging agent, belonging to the technical field of fine chemicals. Background technique [0002] Glass has a wide range of uses in industrial production and daily life. However, glass often suffers from fogging, that is, a layer of water droplets adheres to its surface and loses transparency. For example, the fogging of building glass windows, bathroom mirrors, spectacle lenses, car windshields, camera lenses, etc., will bring great inconvenience to people's lives, and some even cause safety hazards. [0003] Generally, when the room temperature is below the dew point, tiny water droplets will form on the glass surface, and these water droplets will scatter the light and cause the glass to devitrify. At present, glass anti-fogging methods mainly include the following: 1) Keep the temperature of the glass surface above the dew point...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C11D1/94C11D3/382C11D3/37C11D3/20C11D3/60C09K3/18
CPCC09K3/18C11D1/22C11D1/66C11D1/662C11D1/721C11D1/92C11D1/94C11D3/00C11D3/201C11D3/3707C11D3/382
Inventor 任海波任泳豪王要令李晓燕李翔张艳花
Owner HENAN UNIV OF URBAN CONSTR
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com