Diamond glaze for ceramic tiles

A diamond glaze and ceramic tile technology, applied in the field of glaze, can solve the problems of light-reflecting "water ripples, increase production costs, weak three-dimensional effect of patterns, etc., achieve the improvement of water ripple phenomenon, the improvement of wear resistance and thermal shock resistance, Eliminate the effect of later cracking

Inactive Publication Date: 2016-07-13
XIANGYANG GAOMING MINING IND CO LTD
View PDF4 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Ceramic tiles are widely used in the field of construction. While being widely used, various technological improvements promote product optimization. However, existing ceramic tiles generally have light-reflecting "water ripples", poor wear resistance, and weak three-dimensional patterns. It is difficult to solve defects such as polishing and glaze penetration during production. In order to solve this defect, existing enterprises focus on the research and development of super-flat diamond glaze, that is, thicken the glaze before polishing, so as to solve the existing defects. However, this The solution has the problems of wasting raw materials and increasing production costs, so that the existing defects cannot be fundamentally solved technically

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] 1) Formula in weight percentage:

[0016] Spodumene powder 40%, frit powder 10%, potash feldspar powder 10%, burnt talc powder 5%, barium carbonate powder 8%, wollastonite powder 10%, kaolin powder 5%, white corundum powder 1%, zinc oxide 5 %,

[0017] Two) Preparation method:

[0018] Step 1. First prepare the frit powder. The formula for the weight percentage of the frit powder is as follows: potassium feldspar 30%, wollastonite 4%, raw talc 5%, barium carbonate 5%, calcite 16%, quartz 20%, coarse oxidation Aluminum 10%, 95 zinc oxide 2%, potassium carbonate 1%, strontium carbonate 1%,

[0019] Preparation of frit powder:

[0020] 1) Put all the ingredients into the melting furnace and heat to 1500℃ to obtain the frit;

[0021] 2) After the frit is taken out and cooled to room temperature, it is crushed with a pulverizer, and then sieved with a 100-mesh sieve for use. If it is unqualified, it is crushed and sieved to pass;

[0022] Step 2. Put all the formula materials in a) we...

Embodiment 2

[0024] 1) Formula of weight percentage:

[0025] Spodumene powder 27%, frit powder 13%, potash feldspar powder 13%, burnt talc powder 10%, barium carbonate powder 12%, wollastonite powder 13%, kaolin powder 7%, white corundum powder 3%, zinc oxide 6 %,

[0026] Two) Preparation method:

[0027] Step 1. First prepare the frit powder. The formula of the frit powder is as follows: 25% potash feldspar, 5% wollastonite, 6% raw talc, 7% barium carbonate, 18% calcite, 21% quartz, and coarse oxidation Aluminum 12%, 95 zinc oxide 3%, potassium carbonate 2%, strontium carbonate 1.5%,

[0028] Preparation of frit powder:

[0029] 1) Put all the ingredients into the melting furnace and heat to 1500℃ to obtain the frit;

[0030] 2) After the frit is taken out and cooled to room temperature, it is crushed with a crusher, and then sieved with a 100-mesh screen for use. If it is unqualified, it is crushed and sieved to pass;

[0031] Step 2. Put all the formula materials in a) weight percentage into a ...

Embodiment 3

[0033] 1) Formula in weight percentage:

[0034] Spodumene powder 15%, frit powder 15%, potash feldspar powder 15%, burnt talc powder 15%, barium carbonate powder 15%, wollastonite powder 15%, kaolin powder 8%, white corundum powder 5%, zinc oxide 7 %,

[0035] Two) Preparation method:

[0036] Step 1. First prepare the frit powder. The formula for the weight percentage of the frit powder is as follows: potassium feldspar 20%, wollastonite 6%, raw talc 8%, barium carbonate 8%, calcite 20%, quartz 22%, coarse oxidation Aluminum 14%, 95 zinc oxide 4%, potassium carbonate 3%, strontium carbonate 2%,

[0037] Preparation of frit powder:

[0038] 1) Put all the ingredients into the melting furnace and heat to 1500℃ to obtain the frit;

[0039] 2) After the frit is taken out and cooled to room temperature, it is crushed with a crusher, and then sieved with a 100-mesh screen for use. If it is unqualified, it is crushed and sieved to pass;

[0040] Step 2. Put all the formula materials in a) we...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a diamond glaze for ceramic tiles.One), a formula comprises: spodumene powder, frit powder, potassium feldspar powder, calcined talc powder, barium carbonate powder, wollastonite powder, kaolin powder, white alundum powder, and zinc oxide; two), a preparation method comprises the steps: 1, preparing the frit powder, potassium feldspar, wollastonite, raw talc, barium carbonate, calcite, quartz, crude aluminum oxide, 95 zinc oxide, potassium carbonate and strontium carbonate, 1), placing all materials in a melting furnace, and heating to 1500 DEG C to obtain frit; 2), taking out for cooling to normal temperature, crushing, screening with a 100-mesh screen for use, and if disqualification occurs, crushing and screening until qualification; 2, placing all materials of formula one) into a stirrer, and stirring well to obtain the diamond glaze.The method has a simple process, the diamond glaze has high glaze, can prevent cracking, cut facture and the like, has excellent wear resistance and is useful in the production of polished tiles closer to nature and richer in color.

Description

Technical field [0001] The invention relates to a glaze used in the production of ceramic tiles, in particular to a diamond glaze for ceramic tiles. Background technique [0002] Ceramic tiles are widely used in the construction field. At the same time as they are widely used, various technical improvements have led to continuous product optimization. However, the existing ceramic tiles have light reflection "water ripples", poor wear resistance, and weak three-dimensional pattern. In order to solve this defect, the existing enterprises focus on the research and development of diamond glaze super flat glaze, which is to thicken the glaze and then polish it to solve the existing defects. The solution has the problem of wasting raw materials and increasing production costs, so that the existing defects cannot be fundamentally solved technically. Summary of the invention [0003] The invention provides a diamond glaze for ceramic tiles, which adopts scientific formula and simple tec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/14C03C8/04
CPCC03C8/14C03C8/04
Inventor 高世明
Owner XIANGYANG GAOMING MINING IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap