Composite for manufacturing automobile seat cover and preparation method of composite

A technology for composite materials and car seats, which is applied in the field of manufacturing composite materials for car seat covers and its preparation, can solve the problems of no odor absorption, wear resistance, poor dirt resistance and elasticity, and achieves anti-aging wear and good dirt resistance. , good protection effect

Inactive Publication Date: 2016-07-13
SUZHOU NETABHAPE COMPOSITE MATERIALS
View PDF12 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Technical issues solved: Aiming at the shortcomings of existing car seat covers that have no function of absorbing peculiar smell, and poor performances such as wear resistance, dirt resistance, and elasticity, the present invention provides a composite material for manufacturing car seat covers and a preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A composite material for manufacturing car seat covers, which contains the following components in parts by mass: 50 parts of butadiene rubber, 15 parts of silicon carbide fiber, 10 parts of polyacrylate fiber, 15 parts of diatomaceous earth, 2 parts of aluminum oxide, azo 1 part of diformamide, 2 parts of phenyl o-hydroxybenzoate, 3 parts of aluminum borate whiskers, 0.1 part of unsaturated polyester resin, 0.5 part of titanium dioxide, 0.1 part of epoxy resin, 1 part of masterbatch, 2,4 - 1 part of dihydroxybenzophenone.

[0019] A preparation method for manufacturing a composite material for a car seat cover, the steps of the preparation method are as follows:

[0020] The first step: add butadiene rubber, silicon carbide fiber, polyacrylate fiber, diatomaceous earth, alumina, azodicarbonamide, phenyl o-hydroxybenzoate, and aluminum borate whiskers into the internal mixer for internal mixing , wherein the banburying temperature is 200°C, and the time is 40min;

[0...

Embodiment 2

[0024] A composite material for manufacturing car seat covers, containing the following components in parts by mass: 70 parts of butadiene rubber, 30 parts of silicon carbide fiber, 25 parts of polyacrylate fiber, 30 parts of diatomaceous earth, 9 parts of aluminum oxide, azo 7 parts of diformamide, 7 parts of phenyl o-hydroxybenzoate, 9 parts of aluminum borate whiskers, 0.5 parts of unsaturated polyester resin, 1.8 parts of titanium dioxide, 0.5 parts of epoxy resin, 3 parts of masterbatch, 2,4 - 2 parts of dihydroxybenzophenone.

[0025] A preparation method for manufacturing a composite material for a car seat cover, the steps of the preparation method are as follows:

[0026] The first step: add butadiene rubber, silicon carbide fiber, polyacrylate fiber, diatomaceous earth, alumina, azodicarbonamide, phenyl o-hydroxybenzoate, and aluminum borate whiskers into the internal mixer for internal mixing , wherein the banburying temperature is 250°C and the time is 60min;

[...

Embodiment 3

[0030] A composite material for manufacturing car seat covers, containing the following components in parts by mass: 65 parts of butadiene rubber, 26 parts of silicon carbide fiber, 22 parts of polyacrylate fiber, 25 parts of diatomaceous earth, 8 parts of aluminum oxide, azo 6 parts of diformamide, 6 parts of phenyl o-hydroxybenzoate, 7 parts of aluminum borate whiskers, 0.4 parts of unsaturated polyester resin, 1.4 parts of titanium dioxide, 0.4 parts of epoxy resin, 2.5 parts of masterbatch, 2,4 - 1.7 parts of dihydroxybenzophenone.

[0031] A preparation method for manufacturing a composite material for a car seat cover, the steps of the preparation method are as follows:

[0032] The first step: add butadiene rubber, silicon carbide fiber, polyacrylate fiber, diatomaceous earth, alumina, azodicarbonamide, phenyl o-hydroxybenzoate, and aluminum borate whiskers into the internal mixer for internal mixing , wherein the banburying temperature is 225°C and the time is 50min; ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a composite for manufacturing an automobile seat cover and a preparation method of the composite. The composite is prepared from the following constituents in parts by mass: 50-70 parts of butadiene rubber, 15-30 parts of silicon carbide fibers, 10-25 parts of polyacrylate fibers, 15-30 parts of diatomite, 2-9 parts of aluminum oxide, 1-7 parts of azodicarbonamide, 2-7 parts of phenyl salicylate, 3-9 parts of aluminum borate whiskers, 0.1-0.5 parts of unsaturated polyester resin, 0.5-1.8 parts of titanium dioxide, 0.1-0.5 parts of epoxy resin, 1-3 parts of color master batch and 1-2 parts of 2,4-dihydroxybenzophenone. The automobile seat cover manufactured from the composite provided by the invention has excellent performance of breathability, static resistance, ultraviolet resistance and pressure resistance, is good in elasticity, abrasion resistance and dirt resistance, and can also effectively absorb peculiar smell in an automobile.

Description

technical field [0001] The invention relates to the technical field of composite materials, in particular to a composite material for manufacturing automobile seat covers and a preparation method thereof. Background technique [0002] As the transportation industry continues to evolve, cars are becoming more common. Moreover, many car seats are made of genuine leather materials. Although the genuine leather materials have the advantages of being beautiful, if no protective measures are taken, they are still prone to mildew, wear and tear, and are prone to cracking after a long time. At present, the more direct protection method is to put a layer of seat cover on the seat to protect the cleanliness of the seat and prevent the leather from aging. [0003] Existing seat covers are made of ice silk, flax, gold velvet, jeanette, sandwiches, etc., but each has its own shortcomings. In addition, seat covers are generally required when a new car is new. If the seat cover can absor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/00C08L33/04C08L67/06C08L63/00C08K13/04C08K7/10C08K7/08C08K3/34C08K3/22C08J9/10
CPCC08J9/103C08J2203/04C08J2309/00C08J2433/04C08L9/00C08L2201/04C08L2201/08C08L2203/14C08L2205/035C08L2205/16C08L33/04C08L67/06C08L63/00C08K13/04C08K7/10C08K7/08C08K3/34C08K2003/2227
Inventor 刘莉王爽邱晶
Owner SUZHOU NETABHAPE COMPOSITE MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com