A fireproof electromagnetic shielding anti-radiation cloth

An electromagnetic shielding and anti-radiation technology, which is applied in textiles and papermaking, fiber treatment, plant fibers, etc., can solve the problems of poor flexibility, easy peeling off of coatings, and easy corrosion of metals, and achieve good flexibility, good fire performance, and high The effect of shielding effectiveness

Active Publication Date: 2018-01-23
LINYI ZHONGRUI RADIATION PROTECTION TECH CO LTD
View PDF9 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the existing electromagnetic shielding cloths on the market are mainly made by adding metal wires or conductive fibers when weaving. In this method, the metal wires are easy to break during the production process, and the flexibility is poor, and the shielding effect is not ideal; Shielding cloth is a metal-coated fabric, which generally has problems such as metal corrosion, oxidation, high temperature resistance, coating easy to fall off, poor fire resistance, etc., which is far from being suitable for some explosion-proof and military special environments.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A fireproof electromagnetic shielding anti-radiation cloth

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A fire-proof electromagnetic shielding radiation-proof cloth, which sequentially includes a base layer, a composite metal coating, a high-temperature resistant layer, a fire-proof layer and an anti-oxidation layer from bottom to top.

[0023] Its specific preparation method is as follows:

[0024] 1) Choose cotton, linen, silk, polyester, nylon, acrylic or their blended woven, knitted, warp-knitted fabric layer or non-woven fabric layer as the substrate layer fabric;

[0025] 2) Evenly disperse 30g of nano-silver with a particle size of 20-30nm in 70g of 5% sodium carboxymethylcellulose solution to make a mixed solution, then immerse the matrix layer cloth in it, take it out and dry it after it is completely soaked;

[0026] 3) On the substrate layer after drying, metal nickel, metal copper, and metal nickel are uniformly plated on the surface according to the thickness ratio of 1:2:1 according to the conventional metallization coating method to form a composite metal c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses fireproof electromagnetic shielding and radiation protection cloth. The fireproof electromagnetic shielding and radiation protection cloth comprises a substrate layer, a composite metal plating, a high-temperature resisting layer, an oxidation-resisting layer and a fireproof layer, wherein the substrate layer is formed by uniformly soaking cloth of the substrate layer into a mixed solution of 30% nanosilver and a 70% binder and drying the cloth; the composite metal plating is located above the substrate layer; the fireproof layer is arranged above the composite metal plating; the high-temperature resisting layer is arranged between the fireproof layer and the composite metal plating; the oxidation-resisting layer is arranged above the fireproof layer. The radiation protection cloth has the higher electromagnetic shielding efficacy in a wider range and has excellent fireproof, oxidation-resisting and high-temperature resisting properties.

Description

technical field [0001] The invention relates to an electromagnetic shielding radiation-proof cloth, in particular to a fire-proof electromagnetic shielding radiation-proof cloth. Background technique [0002] With the rapid development of modern electronic and electrical equipment industry, the number of various wireless communication systems and electronic devices has increased sharply, resulting in increasingly serious electromagnetic interference and electromagnetic compatibility, and the problem of electromagnetic radiation pollution has become increasingly prominent. Therefore, electromagnetic radiation pollution has become more and more popular. focus on. The electromagnetic interference generated by electromagnetic radiation not only affects the performance of electronic products, but also the electromagnetic pollution caused by it will cause serious harm to humans and other organisms. Shielding is the use of shields (materials with specific properties) to prevent or...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M15/09D06M11/83D06M15/643D06M11/71D06M13/364D06M15/55D06M11/79D06M13/148D06M11/74D06M101/06D06M101/10D06M101/32D06M101/34D06M101/28
CPCD06M11/71D06M11/74D06M11/79D06M11/83D06M13/148D06M13/364D06M15/09D06M15/55D06M15/643D06M2101/06D06M2101/10D06M2101/28D06M2101/32D06M2101/34D06M2200/30
Inventor 刘原麟
Owner LINYI ZHONGRUI RADIATION PROTECTION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products