tizrcraln multi-component composite wear-resistant coating tool and preparation method thereof

A wear-resistant coating and multi-component compounding technology, which is applied in the field of metal cutting tools, can solve the problems of limitations, poor toughness and wear resistance of binary nitride coatings, and achieve poor wear resistance, increase strength and toughness, and improve The effect of service life and cutting performance

Active Publication Date: 2018-04-13
安徽锦鹏纺织有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, with the development of cutting technology and the promotion of high-speed cutting technology, the relatively poor toughness and wear resistance of binary nitride coatings limit its application.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • tizrcraln multi-component composite wear-resistant coating tool and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A TiZrCrAlN multi-component composite wear-resistant coating tool, the tool is an ordinary milling insert, the material of the tool base 1 is: hard alloy YT15; the coating material is: Ti, Ti / Zr / Cr / Al and TiZrCrAlN; From bottom to top, the cutter is as follows: cutter base 1, Ti transition layer 2, Ti / Zr / Cr / Al transition layer 3 and TiZrCrAlN multi-component composite coating 4.

[0019] The preparation method of the TiZrCrAlN multi-component composite wear-resistant coating tool according to the present invention, the deposition method is: arc ion plating deposits a Ti transition layer on the surface of the tool substrate, and then multi-arc ion plating + unbalanced magnetron sputtering composite deposition Ti / Zr / Cr / Al transition layer, and finally deposited TiZrCrAlN multi-component composite coating (using 1 Ti arc target, 1 Zr arc target, 1 Cr unbalanced sputtering target and 1 Al unbalanced magnetron sputtering target during deposition) ), its preparation steps ar...

Embodiment 2

[0027] A TiZrCrAlN multi-component composite wear-resistant coating tool, the tool is an ordinary twist drill, the base material is: high-speed steel W18Cr4V; the coating material is: Ti, Ti / Zr / Cr / Al and TiZrCrAlN; the tool from bottom to top is : Tool substrate 1, Ti transition layer 2, Ti / Zr / Cr / Al transition layer 3 and TiZrCrAlN multi-component composite coating 4.

[0028] The preparation method of the TiZrCrAlN multi-component composite wear-resistant coating tool according to the present invention, the deposition method is: arc ion plating deposits a Ti transition layer on the surface of the tool substrate, and then multi-arc ion plating + unbalanced magnetron sputtering composite deposition Ti / Zr / Cr / Al transition layer, and finally deposited TiZrCrAlN multi-component composite coating (using 1 Ti arc target, 1 Zr arc target, 1 Cr unbalanced sputtering target and 1 Al unbalanced magnetron sputtering target during deposition) ), its preparation steps are as follows:

[...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a tool with an abrasion-resistant TiZrCrAlN multi-component compound coating and a preparation method of the tool, and belongs to the technical field of metal cutting tools. The tool comprises a tool base which is provided with the coating. The tool is provided with the tool base, a Ti transitional layer, a Ti / Zr / Cr / Al transitional layer and the TiZrCrAlN multi-component compound coating sequentially from bottom to top. The preparation method sequentially comprises the steps of pre-treatment, ion cleaning, deposition of the Ti transitional layer, deposition of the Ti / Zr / Cr / Al transitional layer, deposition of the TiZrCrAlN multi-component compound coating and post-treatment. According to the tool with the abrasion-resistant TiZrCrAlN multi-component compound coating and the preparation method of the tool, the multi-component compound coating is prepared through a multi-arc ion plating and unbalanced magnetron sputtering compound coating method, the surface layer is the TiZrCrAlN multi-component coating, and the Ti transitional layer and the Ti / Zr / Cr / Al transitional layer are arranged between the tool base and the surface coating, so that the residual stress is reduced, the strength and toughness of the coating are improved remarkably, the coating has better impact resistance and abrasion resistance, the shortcoming that an original binary coating is poor in abrasion resistance can be overcome, the service life of the tool is prolonged remarkably, and the cutting performance of the tool is improved remarkably.

Description

technical field [0001] The invention belongs to the technical field of metal cutting tools, and in particular relates to a TiZrCrAlN multi-component composite wear-resistant coating tool and a preparation method thereof. Background technique [0002] Coating the tool is one of the important ways to improve the performance of the tool. The coated tool combines the tool substrate with the coating, which greatly improves the performance of the tool. Nitride single-coated tools such as TiN and ZrN have become the most widely used coated tools since they were successfully applied to cutting tools in the 1970s. However, with the development of cutting technology and the promotion of high-speed cutting technology, the relatively poor toughness and wear resistance of binary nitride coatings limit its application. The comprehensive properties of toughness, strength and impact resistance of the coating can be significantly improved by preparing a coating with a multi-component compo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C23C14/06C23C14/16C23C14/32C23C14/35
CPCC23C14/0036C23C14/0641C23C14/16C23C14/165C23C14/325C23C14/352C23C28/322C23C28/347
Inventor 宋文龙邓建新程杰周珂王首军李小冬
Owner 安徽锦鹏纺织有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap