UV curing coating for PVC material coating process and preparation method for UV curing material

A technology of PVC material and coating process, which is applied in the direction of epoxy resin coating, polyurea/polyurethane coating, coating, etc., which can solve the problems of high equipment requirements, many coating processes and high cost of curtain coating process

Inactive Publication Date: 2016-08-03
HUNAN JINHAI SCI & TECH
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The surface flatness and coating fullness of the roller coating process are not ideal; the flow coating process has many coa

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • UV curing coating for PVC material coating process and preparation method for UV curing material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Modified epoxy acrylate: 25%

[0032] Special functional group acrylate: 35%

[0033] Aliphatic urethane acrylate: 8%

[0034] HDDA: 20%

[0035] TM: 5%

[0036] Photoinitiator: 6.5%

[0037] Additives: 0.5%

[0038] The above-mentioned modified epoxy acrylate resin adopts JS-217 produced by the company;

[0039] The above-mentioned aliphatic polyurethane acrylate resin adopts Changxing Chemical Industry 5104D;

[0040] The above-mentioned special functional group acrylate resin adopts JS-402 produced by the company itself;

[0041] The above-mentioned photoinitiator adopts 1-hydroxy-cyclohexylbenzophenone (184), macromolecular methyl benzoylformate photoinitiator Doublecure200, Taiwan double bond 1104 and 200 series products;

[0042] The above additives are BYK358N and BYK1790.

Embodiment 2

[0044] Modified epoxy acrylate: 20%

[0045] Special functional group acrylate: 35%

[0046] Aliphatic urethane acrylate: 12%

[0047] HDDA: 20%

[0048] TM: 6%

[0049]Photoinitiator: 6.5%

[0050] Additives: 0.5%

[0051] The above-mentioned modified epoxy acrylate resin adopts JS-217 produced by the company;

[0052] The above-mentioned aliphatic polyurethane acrylate resin adopts Changxing Chemical Industry 5104D;

[0053] The above-mentioned special functional group acrylate resin adopts JS-402 produced by the company itself;

[0054] The above-mentioned photoinitiator adopts 1-hydroxy-cyclohexylbenzophenone (184), macromolecular methyl benzoylformate photoinitiator Doublecure200, Taiwan double bond 1104 and 200 series products;

[0055] The above additives are BYK358N and BYK1790.

Embodiment 3

[0057] Modified epoxy acrylate: 20%

[0058] Special functional group acrylate: 35%

[0059] Aliphatic urethane acrylate: 15%

[0060] HDDA: 18%

[0061] TM: 5%

[0062] Photoinitiator: 6.7%

[0063] Additives: 0.3%

[0064] The above-mentioned modified epoxy acrylate resin adopts JS-217 produced by the company;

[0065] The above-mentioned aliphatic polyurethane acrylate resin adopts Changxing Chemical Industry 5104D;

[0066] The above-mentioned special functional group acrylate resin adopts JS-402 produced by the company itself;

[0067] The above-mentioned photoinitiator adopts 1-hydroxy-cyclohexylbenzophenone (184), macromolecular methyl benzoylformate photoinitiator Doublecure200, Taiwan double bond 1104 and 200 series products;

[0068] The above additives are BYK358N and BYK1790.

[0069] The preparation method of above-mentioned a kind of PVC material laminating coating process with UV coating is as follows:

[0070] Put modified epoxy acrylate, special funct...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an ultraviolet (UV) curing coating for a PVC material coating process and a preparation method for the UV curing material. The UV curing coating for the PVC material coating process is composed of the following raw materials in percentage by mass: 20-30% of modified epoxy acrylate, 35-40% of special functional group acrylate, 8-15% of aliphatic polyurethane acrylate, 20-30% of a reactive diluent, 6-10% of a photoinitiator and 0.3-1% of an additive. The UV curing coating for the PVC material coating process finishes coating only by one coating process and is quickly cured to form a film under UV-irradiation; the coating forming the film is good in adhesion, high in hardness, controllable in luster, good in scratch resistance, excellent in yellowing resistance and excellent in water resistance; and compared with a conventional process, the process has the advantages that the efficiency is high, intermittent production can be realized, the finished product defect rate is low and the like.

Description

technical field [0001] The invention mainly relates to the field of ultraviolet curing materials, in particular to an ultraviolet (UV) curing coating for PVC material film coating process and a preparation method thereof. Background technique [0002] Traditional non-UV coatings have a slow curing speed, seriously affecting production efficiency, and traditional non-UV coatings contain a large amount of volatile organic solvents, which are not only extremely harmful to human health, but also cause serious environmental problems due to volatilization into the atmosphere after use. pollution. UV coatings are composed of UV-curable resins, reactive diluents, photoinitiators, additives and other components, which can avoid the use of volatile organic solvents, and are an important development direction of environmentally friendly coatings. With the improvement of people's awareness of environmental protection, the application field and market demand of UV paint will continue to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D163/10C09D175/14C09D7/12
CPCC09D163/10C08L75/14
Inventor 刘立新王石青李祥郝茜
Owner HUNAN JINHAI SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap