Self-cleaning beauty towel and making method thereof
A self-cleaning, towel technology, applied in textiles, biochemical fiber treatment, fabrics, etc., can solve the problems of not being washable, affecting the hand feeling and the hydrophilicity of towels, etc., and achieve the effect of easy cleaning
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0025] The double-sided interweaving method is adopted, the plain gauze is woven with 32S / 2 pure cotton yarn on one side, the base of the loop side is 32S pure cotton yarn, and the loop part is woven with 21S / 1 pure bamboo pulp fiber.
[0026] Prepare nano-zirconia by the following method, dissolve zirconium oxychloride in 2000mL water to make a solution with a concentration of 0.1M, add 0.01M sodium phytate, 0.01M lecithin, 0.05 M polyvinylpyrrolidone, 0.05 M polyethylene glycol , add 50mL of ethanol after ultrasonic mixing, add the above mixed solution into a thermal reaction kettle, react at a high temperature of 180°C for 6h, cool down to room temperature and age for 10h, and centrifuge to obtain a milky white slurry, which is nano-zirconia dispersed liquid.
[0027] According to the preparation method of a nano-silver halide colloid disclosed in Chinese invention patent CN101659439B, the nano-silver antibacterial agent is prepared according to the method disclosed in Exam...
Embodiment 2
[0033] Double-sided interweaving method is adopted, plain gauze is woven with 32S / 2 cotton modal blended yarn (70 / 30) on one side, cotton modal blended yarn (70 / 30) is used at the base of the loop side, and 32S / 2 pure Bamboo pulp fiber weaving; nano far-infrared zirconia, nano-silver antibacterial agent preparation method is the same as in Example 1, by spraying the nano-scale far-infrared zirconia solution with particle size between 5-10nm sprayed on the plain weave side, zirconia The amount of the solution is 6% of the dry weight of the towel, and it is dried in a 120°C open-width dryer; the dried towels are respectively passed through rolling grooves equipped with nano-silver antibacterial agent and lecithin, and the amount of the antibacterial agent solution is The weight of the dry cloth is 4%, and the amount of carboxylate is 1.5% of the weight of the towel dry cloth; dry in a loose dryer at a drying temperature of 135°C.
Embodiment 3
[0035] Double-sided interweaving method is adopted, plain gauze is woven with 21S / 1 cotton and linen (80 / 20) yarn on one side, 32S pure cotton yarn is used on one side of the loop, and 21S bamboo pulp and wood pulp fiber (80 / 20) is used to weave the loop part The preparation method of nano far-infrared zirconia and nano-silver antibacterial agent is the same as embodiment 1, and the nano-scale far-infrared zirconia solution between 5~10nm is sprayed on plain weave side by spraying method, and the consumption of zirconia solution is 5% of the dry cloth weight of the towel is dried in a 130°C open-width dryer; the dried towels are respectively passed through rolling grooves equipped with nano-silver antibacterial agent and polysorbate, and the amount of antibacterial agent solution is the dry cloth weight of the towel. The amount of polysorbate is 1% of the weight of the towel dry cloth; it is dried in a loose dryer at a drying temperature of 145°C.
PUM
| Property | Measurement | Unit |
|---|---|---|
| particle diameter | aaaaa | aaaaa |
| particle diameter | aaaaa | aaaaa |