Low-cost high-strength dolomite earthen-ware green body and preparation method thereof
A white cloud ceramic green body and high-strength technology, applied in the field of ceramic products, can solve the problems of energy saving and emission reduction of white cloud pottery, reduce the degradation function of white cloud pottery, and reduce the strength of white cloud pottery, so as to promote sustainable development and expand firing The temperature range can be improved to improve the firing pass rate
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0020] Example one:
[0021] In this embodiment, the base material includes the following raw materials by weight percentage: 28wt% of elutriation mud, 12wt% of black clay, 1wt% of bentonite, 5wt% of pyrophyllite, 12wt% of low temperature sand, 4wt% of lithium porcelain stone, 10wt% of dolomite %, black talc 6wt%, limestone 8wt%, diopside 9wt%, Yongchun coarse soil 2wt%, waste porcelain powder 3wt%; the weight percentage of the additive relative to the base material is 1%. The additive is an organic silicon nano-liquid, and its weight percentage relative to the base material is 1%.
[0022] The preparation method of the low-cost high-strength dolomite ceramic body of this embodiment includes the following specific steps:
[0023] (1) The inferior raw materials are milled, washed, sieved, and iron removed to prepare the washing slurry;
[0024] (2) The elutriation slurry prepared in step (1) and the other raw materials in the base material are respectively ball-milled into a mill unti...
Example Embodiment
[0027] Embodiment two:
[0028] In this embodiment, the base material includes the following raw materials by weight percentage: 30wt% of elutriation mud, 15wt% of black clay, 6wt% of pyrophyllite, 13wt% of low temperature sand, 5wt% of lithium porcelain stone, 7wt% of dolomite, black talc 6wt%, limestone 7wt%, diopside 10wt%, Yongchun coarse soil 1wt%. The additive is organic silicon nano-liquid, and its weight percentage relative to the base material is 2%.
[0029] The preparation method of the low-cost high-strength dolomite ceramic body of this embodiment includes the following specific steps:
[0030] (1) The inferior raw materials are milled, washed, sieved, and iron removed to prepare the washing slurry;
[0031] (2) The elutriation slurry prepared in step (1) and the other raw materials in the base material are respectively ball-milled into a mill until the mixture particles pass a 200-250 mesh sieve, and then the slurry is discharged for use;
[0032] (3) Mix the mud prepare...
Example Embodiment
[0034] Embodiment three:
[0035] In this embodiment, the base material includes the following raw materials by weight percentage: elutriation mud 32wt%, black clay 15wt%, bentonite 1wt%, pyrophyllite 5wt%, low temperature sand 13wt%, lithium porcelain stone 5wt%, dolomite 10wt% %, black talc 7wt%, limestone 7wt%, diopside 8wt%; the weight percentage of the additive relative to the base material is 1%. The additive is an organic silicon nano-liquid, and its weight percentage relative to the base material is 1%.
[0036] The preparation method of the low-cost high-strength dolomite ceramic body of this embodiment includes the following specific steps:
[0037] (1) The inferior raw materials are milled, washed, sieved, and iron removed to prepare the washing slurry;
[0038] (2) The elutriation slurry prepared in step (1) and the other raw materials in the base material are respectively ball-milled into a mill until the mixture particles pass a 200-250 mesh sieve, and then the slurry i...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap