A kind of oily anti-adhesive titanium coating and its application

An oily, anti-stick technology, applied in epoxy resin coatings, coatings, etc., can solve the problems of poor film formation and adhesion, long preparation time, complex preparation process, etc., to improve product accuracy, size and surface quality, improve Yield and production efficiency, the effect of simple production and use processes

Active Publication Date: 2018-06-12
PANGANG GROUP RESEARCH INSTITUTE CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In the rolling process of titanium tubes, due to the deformation of titanium ingots, the effect of spraying the coating on the surface of titanium ingots to prevent titanium-steel bonding is not good
If the paint is directly sprayed on the surface of the rolling capstan, due to the different materials of the capstan and the titanium ingot, the film forming and adhesion effects are poor, and it cannot prevent titanium-steel bonding well
In addition, the use of this coating requires spraying treatment on the surface of each titanium ingot, and the coating needs a certain period of time to dry after spraying, so the preparation process becomes complicated, the preparation time is long, and continuous and efficient production is not possible.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of oily anti-adhesive titanium coating and its application
  • A kind of oily anti-adhesive titanium coating and its application
  • A kind of oily anti-adhesive titanium coating and its application

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0031] The preparation method of the oil-based anti-sticking titanium coating of the present invention has no special requirements, and various methods commonly used in the field can be used, as long as the components are mixed evenly, and it can be prepared immediately for use. However, the inventors of the present invention have found in their research that the following method is used to prepare the oil-based anti-sticking titanium coating, which can make the components mix more uniformly. The specific method is: first mix the oily film-forming agent with the diluent to dilute, then slowly add copper powder, iron sesquioxide powder and aluminum sesquioxide powder under stirring, then add the curing agent, stir evenly, and then add Dispersant, just stir until it becomes a uniform and stable phase.

[0032] The oily anti-sticking titanium coating of the present invention can be used in high-temperature rolling titanium pipes.

[0033] Before the titanium tube is rolled, the ...

Embodiment 1～5

[0039] Under normal temperature and pressure, weigh epoxy resin (solid content 50%) and place it in a container for use; add diluent and stir evenly for use; measure Cu powder, Fe 2 o 3 Powder, Al 2 o 3 powder, slowly add to the container, stirring continuously during the adding process, and stir evenly; then measure the curing agent SiO 2 powder, put it into the container, and stir evenly; then measure and add polyvinyl alcohol 200 as a dispersant, add it into the container, and stir until the solution is in a uniform and stable phase, and the oily anti-sticking titanium coating of the present invention is obtained. The consumption of each raw material is shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an oil-based anti-bonding titanium coating and application thereof, and belongs to the technical field of titanium-steel anti-bonding coatings. The oil-based anti-bonding titanium coating is used in titanium tube rolling. The coating is prepared from, by weight, 50-150 parts of oil-based film-forming agent, 0-50 parts of copper powder, 300-400 parts of iron sesquioxide powder and 400-450 parts of aluminum oxide powder. Steel equipment, roller beds and winches are coated with the oil-based anti-bonding titanium coating, a very good isolation layer is formed, it can be guaranteed that a titanium ingot and steel equipment rollers or the winches are not subjected to a bonding reaction in the rolling or piercing process at the temperature of 900 DEG C, the precision size and surface quality of the product are improved, the yield of titanium material machining is increased, the production efficiency of titanium material machining is improved, and the production cost is reduced.

Description

technical field [0001] The invention relates to an oily anti-adhesion titanium coating and its application, belonging to the technical field of titanium-steel anti-adhesion coatings. Background technique [0002] At present, the domestic use of titanium ingot round blanks to produce titanium tubes is to directly heat the titanium ingot round billets in a heating furnace at 900 ° C for more than 4 hours, and then push out the heating furnace for high-temperature rolling of titanium tubes. Due to the high temperature, titanium and titanium alloys tend to "stick to titanium" with steel rolling equipment, roller tables and rolling winches, which makes the surface of titanium tubes appear "lack of meat" at different depths. It is rotating piercing and rolling. The titanium billet is pierced and rolled during high-speed rotation. Due to the high temperature characteristics of the titanium-based titanium alloy, it is easy to stick to iron, and even form a TiFe phase. If the TiFe p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D163/00C09D7/61
CPCC08L2201/08C09D7/61C09D163/00C08L29/04C08K3/00C08K2003/085C08K2003/2272C08K2003/2227
Inventor 郑昊青许哲峰徐权肖聪李军
Owner PANGANG GROUP RESEARCH INSTITUTE CO LTD