Preparation method of conductive polyester fiber

A technology of polyester fiber and preparation steps, which is applied in the field of preparation of conductive polyester fiber, can solve the problems of poor conductive durability, poor fiber conductive durability, poor hand feeling, etc., and achieve the problems of difficult uniform distribution, improved conductive durability, and simple preparation steps Effect

Inactive Publication Date: 2016-09-28
郭舒洋
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention: the conductive fiber prepared by the current coating method is coated with carbon black on the surface of the fiber, the carbon black is easy to fall off, the hand feel is poor, and the carbon black is not easy to be evenly distributed on the fiber surface, resulting in poor conductive durability. Provides a kind of conductive carbon black powder made from waste rubber, which is compounded and modified with garcinia cambogia rich in hydroxyl and Pichia submembranesis, compounded with polyester fiber and mixed with phenol Conductive coating solution, a method for preparing conductive polyester fibers by applying a dissolution coating method to the surface of polyester fibers
The preparation steps of the present invention are simple, the obtained product has a good hand feeling, and the coating liquid is evenly distributed on the surface of the fiber, effectively solving the problems that the carbon black is easy to fall off and the durability of the fiber is poor.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0017] First, weigh 800g of waste rubber, crush it into particles with a particle size of 1mm with a rubber grinder, rinse the rubber particles with absolute ethanol for 20 minutes, and then dry them. Put the dried rubber particles into a thermal cracking furnace and heat up to 500 Treat at ℃ for 20 minutes, filter and separate the mixed oil to obtain the crude carbon black; then grind the crude carbon black obtained above with a mortar for 30 minutes, and then disperse it in a methanol solution with a mass concentration of 90% according to a solid-to-liquid ratio of 1:5. Use a high-speed shear pulverizer to grind at a speed of 18000r / min for 40 minutes, then transfer it to a horizontal centrifuge and centrifuge at a speed of 20000r / min for 10 minutes, remove the supernatant to obtain a lower layer of sediment, and dry it in an oven to obtain nano-scale conductive carbon black powder Then take 2kg Garcinia Cambogia and peel, remove the seeds and cut into pieces, put the Garcini...

example 2

[0020]First weigh 850g of waste rubber, crush it into particles with a particle size of 2mm with a rubber grinder, rinse the rubber particles with absolute ethanol for 25 minutes, and then dry them. Put the dried rubber particles into a thermal cracking furnace and heat up to 550 Treat at ℃ for 25 minutes, filter and remove the mixed oil to obtain crude carbon black; then grind the crude carbon black obtained above with a mortar for 35 minutes, and disperse it in a methanol solution with a mass concentration of 90% according to a solid-to-liquid ratio of 1:5. Use a high-speed shear pulverizer to grind at a speed of 18500r / min for 45 minutes, then transfer it to a horizontal centrifuge and centrifuge at a speed of 20500r / min for 13 minutes, remove the supernatant to obtain a lower layer of sediment, and dry it in an oven to obtain nano-scale conductive carbon black powder ; Then take 3kg Garcinia Cambogia and peel, remove the seeds and cut into pieces, put the Garcinia Cambogia ...

example 3

[0022] First, weigh 900g of waste rubber, crush it into particles with a particle size of 3mm with a rubber grinder, rinse the rubber particles with absolute ethanol for 30 minutes, and then dry them. Put the dried rubber particles into a thermal cracking furnace and heat up to 600 Treat at ℃ for 30 minutes, filter and separate the mixed oil to obtain crude carbon black; then grind the crude carbon black obtained above with a mortar for 40 minutes, and then disperse it in a methanol solution with a mass concentration of 90% according to a solid-to-liquid ratio of 1:5. Use a high-speed shear pulverizer to grind at a speed of 19000r / min for 50 minutes, then transfer it to a horizontal centrifuge and centrifuge at a speed of 21000r / min for 15 minutes, remove the supernatant to obtain a lower layer of sediment, and dry it in an oven to obtain nano-scale conductive carbon black powder ; Then take 3kg Garcinia Cambogia and peel, remove the seeds and cut into pieces, put the Garcinia ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
electrical conductivityaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of conductive polyester fiber, which belongs to the technical field of conductive fiber preparation. The invention uses waste rubber to prepare conductive carbon black powder, carries out dispersive composite modification on it through garcinia cambogia juice rich in hydroxyl and Pichia submembraneus, and mixes it with polyester fiber to prepare conductive carbon black powder. The coating solution is applied to the surface of the polyester fiber by a dissolution coating method to obtain a conductive polyester fiber. The beneficial effects of the present invention are: the preparation steps of the present invention are simple, and the dispersive composite modification of the carbon black is carried out by fully utilizing the garcinia cambogia juice rich in hydroxyl groups and Pichia submembranesis, which effectively solves the problem that the carbon black is not easy to be uniform on the fiber surface The problem of distribution, the obtained product feels good, the carbon black on the surface of the fiber does not fall off, and the conductive durability is improved by 28-29%.

Description

technical field [0001] The invention relates to a preparation method of conductive polyester fiber, which belongs to the technical field of conductive fiber preparation. Background technique [0002] Conductive fiber is a new fiber variety that appeared in the 1960s. This type of fiber has good electrical conductivity and durability, especially in low humidity and still has good durable antistatic properties. Therefore, it is used in industrial and civil fields. Has a great use. The antistatic mechanism of conductive fibers is to generate corona discharge between conductive fibers. Corona discharge is a very gentle form of discharge. When the static voltage reaches a certain value, a sparkless corona discharge is generated to eliminate static electricity. This phenomenon is generally considered to be that the conductive fibers in the fabric, under the action of the electrostatic field, ionize the surrounding air to form positive and negative ions. One of the positive and n...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M23/00D06M11/74D06M101/32
CPCD06M23/00D06M11/74D06M2101/32
Inventor 郭舒洋盛海丰林茂平
Owner 郭舒洋
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com