Novel heat-resistant corrosion-resistant coating as well as preparation and application method thereof

A corrosion-resistant and heat-resistant technology, which is used in the preparation of new heat-resistant and corrosion-resistant coatings and corrosion-resistant coatings. It can solve the problems of poor adhesion, dry cracking and falling off of coatings, and can not withstand higher temperatures, so as to achieve stable performance. , low application cost, good heat resistance

Inactive Publication Date: 2016-10-12
SUZHOU TIANJIANHENG ELECTRONICS INFORMATION TECH CO LTD
View PDF3 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Ordinary coatings in the prior art are difficult to meet the requirements. Although general alkyd resin coatings, epoxy resin coatings, and fluorocarbon resin coatings have good heat resistance, they usually can only withstand about 200°C and cannot withs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0039] Example 1

[0040] A new type of heat-resistant and corrosion-resistant coating, based on weight components, includes the following components:

[0041] 25 parts of ethyl silicate

[0042] 50 parts of methyl triethoxy silane

[0043] Triethylamine 10 parts

[0044] 80 parts of ethanol

[0045] 0.2M hydrochloric acid 10 parts

[0046] O-cresol epoxy resin 30 parts

[0047] Xylene 15 parts

[0048] 3 parts diatomaceous earth

[0049] 0.2 part of silica

[0050] Zinc oxide 2 parts

[0051] Zeolite powder 0.2 parts

[0052] Mica 10 parts

[0053] Butyl cellosolve 5 parts

[0054] Butanol 12 parts

[0055] The preparation method of the above-mentioned novel heat-resistant and corrosion-resistant paint includes the following steps:

[0056] (1) Mix ethyl silicate, methyltriethoxysilane and ethanol, and heat to 70°C;

[0057] (2) Add hydrochloric acid and continue to keep the temperature under stirring for 10 hours;

[0058] (3) After adding triethylamine to adjust the pH value ≥7, continue to keep t...

Example Embodiment

[0063] Example 2

[0064] A new type of heat-resistant and corrosion-resistant coating, based on weight components, includes the following components:

[0065] 45 parts of ethyl silicate

[0066] 70 parts of methyltriethoxysilane

[0067] 18 parts of triethylamine

[0068] 95 parts of ethanol

[0069] 0.2M hydrochloric acid 20 parts

[0070] O-cresol epoxy resin 50 parts

[0071] 30 parts xylene

[0072] 8 parts diatomaceous earth

[0073] Silicon dioxide 0.8 parts

[0074] Zinc oxide 6 parts

[0075] Zeolite powder 3 parts

[0076] Mica 20 parts

[0077] Butyl cellosolve 12 parts

[0078] Butanol 20 parts

[0079] The preparation method of the above-mentioned novel heat-resistant and corrosion-resistant paint includes the following steps:

[0080] (1) Mix ethyl silicate, methyltriethoxysilane and ethanol, and heat to 90°C;

[0081] (2) Add hydrochloric acid and continue to keep the temperature under stirring for 12h;

[0082] (3) After adding triethylamine to adjust the pH value ≥ 7, continue to kee...

Example Embodiment

[0087] Example 3

[0088] A new type of heat-resistant and corrosion-resistant coating, based on weight components, includes the following components:

[0089] 35 parts of ethyl silicate

[0090] 55 parts of methyltriethoxysilane

[0091] 15 parts of triethylamine

[0092] 90 parts of ethanol

[0093] 0.2M hydrochloric acid 15 parts

[0094] 35 parts of o-cresol novolac epoxy resin

[0095] Xylene 20 parts

[0096] Diatomaceous earth 5 parts

[0097] 0.5 part of silica

[0098] Zinc oxide 3 parts

[0099] Zeolite powder 2 parts

[0100] Mica 15 parts

[0101] Butyl cellosolve 10 parts

[0102] Butanol 15 parts

[0103] The preparation method of the above-mentioned novel heat-resistant and corrosion-resistant paint includes the following steps:

[0104] (1) Mix ethyl silicate, methyltriethoxysilane and ethanol, and heat to 80°C;

[0105] (2) Add hydrochloric acid and continue to keep the temperature under stirring for 11 hours;

[0106] (3) After adding triethylamine to adjust the pH value ≥ 7, contin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention provides a novel heat-resistant corrosion-resistant coating as well as a preparation and application method of the novel heat-resistant corrosion-resistant coating, wherein the novel heat-resistant corrosion-resistant coating comprises ethyl silicate, methyl triethoxysilane, triethylamine, ethyl alcohol, hydrochloric acid, o-cresol formaldehyde epoxy resin, dimethylbenzene, diatomite, silica, zinc oxide, zoelite powder, mica, a butyl cellosolve solvent and butyl alcohol. The novel heat-resistant corrosion-resistant coating is reasonable in components, the stability, the corrosion resistance and the heat resistance of a product are good, and the stability is high. The preparation method of the novel heat-resistant corrosion-resistant coating is simple and feasible in process, high in production efficiency and low in application cost, the operation is easy and simple to implement, the quality of a produced product is stable, and the popularization and application values are relatively high.

Description

technical field [0001] The invention belongs to the field of paint production, and in particular relates to a novel heat-resistant and corrosion-resistant coating, a preparation method and an application method of the novel heat-resistant and corrosion-resistant coating. Background technique [0002] Generally speaking, paints and coatings are materials that can be coated on the surface of the object to be coated and form a continuous thin film that adheres firmly, whether it is a traditional coating product that uses natural substances as raw materials or a synthetic chemical product that is currently developing. The coating products of raw materials are all organic chemical polymer materials, and the formed coating film belongs to the type of polymer compound. According to the classification of modern chemical products, coatings belong to fine chemical products, and modern coatings are gradually becoming a class of multifunctional Engineering materials are an important ind...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D183/04C09D163/04C09D5/08C09D7/12C08G77/06
CPCC08G77/06C08K2201/014C08L2201/08C09D5/08C09D5/18C09D183/04C09D7/61C08L63/04C08K3/34C08K3/36C08K2003/2296
Inventor 叶晓龙
Owner SUZHOU TIANJIANHENG ELECTRONICS INFORMATION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap