Polishing abrasive disc for polished crystal tiles and preparation method therefor

A technology of polishing crystal tiles and grinding discs, applied in the direction of grinding/polishing equipment, abrasives, grinding devices, etc., can solve the problem that it can only reach 15-30 degrees, it is difficult to meet the requirements, and the sharpness and glazing performance are not good. and other issues, to achieve the effect that the production cost will not be too high

Inactive Publication Date: 2016-11-09
QUANZHOU ZHONGZHI NEW MATERIAL TECH
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the commonly used grinding and polishing products for polishing crystal tiles are diamond grinding discs used for assembly line processing. The sharpness and glazing performance are not good, especially the glazing performance. The luminosity of products currently on the market can only reach 15-30 degrees. difficult to meet

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0023] The present invention also provides a preparation method for polishing the polished crystal tile, comprising the following steps:

[0024] (1) The materials taken by weight are: phenolic resin 20-30%, melamine resin 10-15%, auxiliary abrasive 25-35%, and auxiliary glazing material 25-40%, and they are mixed uniformly to obtain a tire body binding agent;

[0025] (2) Then 5-10% of the main abrasive diamond particles are added in the above-mentioned carcass binder, fully stirred to make a uniform mixture powder;

[0026] (3) Put the above-mentioned homogeneous mixture powder into a mold for heating and sintering to form.

specific Embodiment 1

[0027] A polished polishing disc for polished crystal tiles, the material composition is by weight percentage: 5% of main abrasive diamond particles, 20% of phenolic resin, 10% of melamine resin, 10% of silicon carbide, 20% of white corundum, 10% of cerium oxide, Zinc Oxide 15%, and Talc 10%.

[0028] A method for preparing a polished polishing disc for polished crystal tiles, comprising the following steps:

[0029] (1) The materials taken by weight are: phenolic resin 20%, melamine resin 10%, silicon carbide 10%, white corundum 20%, cerium oxide 10%, zinc oxide 15%, and talcum powder 10%, and they are Mix uniformly to obtain a carcass binder;

[0030] (2) Then add 5% of the main abrasive diamond particles in the above-mentioned carcass binder, fully stir to make a uniform mixture powder;

[0031] (3) Put the above-mentioned homogeneous mixture powder into a mold for heating and sintering to form.

specific Embodiment 2

[0032] A kind of polished crystal polishing disc, the material composition is by weight percentage: 10% of main abrasive diamond particles, 25% of phenolic resin, 12% of melamine resin, 10% of silicon carbide, 15% of white corundum, 10% of cerium oxide, Zinc Oxide 10%, and Talc 8%.

[0033] A method for preparing a polished polishing disc for polished crystal tiles, comprising the following steps:

[0034] (1) The materials taken by weight are: phenolic resin 25%, melamine resin 12%, silicon carbide 10%, white corundum 15%, cerium oxide 10%, zinc oxide 10%, and talcum powder 8%, and they Mix uniformly to obtain a carcass binder;

[0035] (2) Then 10% of the main abrasive diamond particles are added in the above-mentioned carcass binder, fully stirred to make a uniform mixture powder;

[0036] (3) Put the above-mentioned homogeneous mixture powder into a mold for heating and sintering to form.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a polishing abrasive disc for polished crystal tiles and a preparation method thereof. The polishing abrasive disc comprises the following materials in percentages by weight: 5-10% of main abrasive material diamond particles, 20-30% of phenolic resin, 10-15% of melamine resin, 25-35% of an auxiliary abrasive material and 25-40% of an auxiliary polishing material. The preparation method comprises the following steps: proportioning the materials to prepare a mixed powdery material; and then putting the material in a mould to be heated and sintered and moulded. According to the polishing abrasive disc for polished crystal tiles provided by the invention, two resins: phenolic resin and melamine resin which are mixed in a specific proportion are creatively adopted, so that an important breakthrough is obtained in the polishing aspect of the polished crystal tiles. The phenolic resin accounts for 20-30% and the polishing property of the phenolic resin is fully utilized; the melamine resin accounts for 10-15% and solves the problem that the sharpness of the phenolic resin is short. The two are reasonably matched in use according to the proportion, so that the polishing effect is extremely excellent. The brightness of the product in the market only reaches 15-30 degrees, but the brightness of the product disclosed by the invention can reach 30-50 degrees, and the polishing abrasive disc for polished crystal tiles is quite obvious in advantage.

Description

technical field [0001] The invention relates to the field of diamond grinding tools, in particular to a polishing grinding plate for polished crystal bricks and a preparation method thereof. Background technique [0002] Polished crystal tiles have high hardness, and the surface layer has 3mm thick glass-ceramics. During the wet grinding process of polished crystal tiles, the sharpness of grinding and polishing products is high, and products with low sharpness cannot be quickly polished and smoothed to smooth the glass-ceramic surface. In addition, the photometric characteristics of polished crystal bricks are also very important, which directly affects the product quality of polished crystal bricks. At present, the commonly used grinding and polishing products for polishing crystal tiles are diamond grinding discs used for assembly line processing. The sharpness and glazing performance are not good, especially the glazing performance. The luminosity of products currently on...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B24D3/28B24D3/34B24D18/00B24D99/00
CPCB24D3/285B24D3/28B24D3/346B24D18/00B24D99/005
Inventor 林江程赵扬张钻锋钟剑明林淑芬开万军
Owner QUANZHOU ZHONGZHI NEW MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap