Composite resin film with good shallow screen printing effect and preparation method thereof

A technology of shallow screen printing and composite resin, which is applied in the direction of synthetic resin layered products, chemical instruments and methods, temperature recording methods, etc., can solve the problems of poor shallow screen printing effect, poor polarity of the substrate film, etc., and achieve no residue of waste products, Effect of eliminating induced charge and good sealing

Active Publication Date: 2018-01-05
石狮市炎英塑胶制品有限公司 +1
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this patent does not modify the polypropylene film, and there is still the problem of poor polarity of the base film, and the effect of shallow screen printing is poor.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite resin film with good shallow screen printing effect and preparation method thereof
  • Composite resin film with good shallow screen printing effect and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A composite resin film with good shallow screen printing effect, comprising a three-layer structure of a shallow screen printing layer, a core layer, and a heat-sealing layer;

[0030] The raw materials forming the shallow screen printing layer include 60% isotactic polypropylene, 10% aliphatic polyimide, 10% polyurethane, 10% polyarylsulfone and 10% polycaprolactam in weight percentage. The thickness of the shallow screen printing layer is: 0.1 μm.

[0031] Wherein the raw materials forming the core layer include by weight percentage: isotactic polypropylene 65%, polyphenylene ether 10%, polyethylene naphthalate 15%, sodium lauryl polyoxyethylene ether sulfate 6% , Tetradecyltrimethylammonium bromide 4%. The thickness of the core layer is: 16 μm.

[0032] The raw materials forming the heat-sealing layer include by weight percentage: 40% polycarbonate, 30% amino resin, 15% polyhydroxybutyrate-valerate, 10% polyvinyl chloride, phthalimide 2%, bistrifluoromethanesulfon...

Embodiment 2

[0035] A composite resin film with good shallow screen printing effect, comprising a three-layer structure of a shallow screen printing layer, a core layer, and a heat-sealing layer;

[0036] The raw materials forming the shallow screen printing layer include 80% isotactic polypropylene, 5% aliphatic polyimide, 5% polyurethane, 5% polyarylsulfone and 5% polycaprolactam in weight percentage. The thickness of the shallow screen printing layer is: 0.7 μm.

[0037] Wherein the raw materials forming the core layer include by weight percentage: 85% isotactic polypropylene, 5% polyphenylene ether, 8% polyethylene naphthalate, 1% tetradecyl sulfopropyl betaine, Sodium dodecylbenzenesulfonate 1%. The thickness of the core layer is: 20 μm.

[0038] Wherein the raw materials forming the heat-sealing layer include by weight percentage: polycarbonate 60%, amino resin 20%, polyhydroxybutyrate-valerate 10%, polyvinyl chloride 8%, methylene succinic anhydride 0.5% %, adipic anhydride 1.5%....

Embodiment 3

[0041] A composite resin film with good shallow screen printing effect, comprising a three-layer structure of a shallow screen printing layer, a core layer, and a heat-sealing layer;

[0042] The raw materials forming the shallow screen printing layer include 70% isotactic polypropylene, 7% aliphatic polyimide, 8% polyurethane, 7% polyarylsulfone and 8% polycaprolactam in weight percentage. The thickness of the shallow screen printing layer is: 0.4 μm.

[0043] The raw materials forming the core layer include 75% of isotactic polypropylene, 8% of polyphenylene ether, 11% of polyethylene naphthalate, and 6% of tetradecyl sulfopropyl betaine by weight percentage. The thickness of the core layer is: 18 μm.

[0044] The raw materials forming the heat-sealing layer include by weight percentage: 50% polycarbonate, 25% amino resin, 13% polyhydroxybutyrate-valerate, 8% polyvinyl chloride, phthalimide 4%. The thickness of the heat-sealing layer is: 0.4 μm.

[0045] The proportions of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a composite resin film with good light screen printing effect and a preparation method thereof. The film comprises a light screen-printed layer, a core layer and a heat-sealing layer. The light screen-printed layer comprises the following raw materials: isotactic polypropylene, aliphatic polyimide, polyurethane, polyarylsulfone and polycaprolactam. The core layer comprises the following raw materials: isotactic polypropylene, polyphenyl ether, polyethylene naphthalate and an antistatic agent. The heat-sealing layer comprises the following raw materials: polycarbonate, amino resin, polyhydroxybutyrate-pentanoate, polyvinyl chloride and a slipping agent. According to the preparation method, a three-layer co-extrusion process is employed; production speed and screw speed are controlled; the light screen-printed layer is extruded from an auxiliary extruder 1 at a temperature of 225 DEG C; the core layer is extruded from a main extruder at a temperature of 250 DEG C; and the heat-sealing layer is extruded from an auxiliary extruder 2 at a temperature of 225 DEG C. The light screen-printed film prepared in the invention has improved polarity and anti-static property and presents better light screen printing effect in printing.

Description

technical field [0001] The invention relates to the field of layered products, in particular to a composite resin film with good shallow screen printing effect and a preparation method thereof. Background technique [0002] Shallow screen printing technology has outstanding advantages such as good formability, rich colors, and high combination precision, and is especially suitable for application in exquisite printed products with strict quality requirements and high control levels. Shallow screen printing technology overcomes the problems of fading and blurring of printed products produced by flat film printing technology, and promotes the quality of printed products to a higher level. Nevertheless, shallow screen printing technology often degrades the quality of printed products due to problems such as uneven coloring, board blocking, and dry board during actual operation. Therefore, it is necessary to optimize and improve the properties of the substrate film used in shal...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B27/32B32B27/18B32B27/16B32B27/08B32B27/36B32B33/00B41M5/40B29C47/06C08L23/12C08L79/08C08L75/04C08L81/06C08L77/02C08L71/12C08L67/02C08L69/00C08L61/20C08L67/04C08L27/06
CPCB29C48/18B32B27/08B32B27/16B32B27/18B32B27/32B32B27/365B32B33/00B32B2250/24B32B2307/21B32B2307/51B32B2307/7163B41M5/40C08L23/12C08L69/00C08L2201/04C08L2201/06C08L2203/16C08L2205/03C08L2205/035C08L2207/10C08L79/08C08L75/04C08L81/06C08L77/02C08L71/12C08L67/02C08L61/20C08L67/04C08L27/06
Inventor 何则鍏
Owner 石狮市炎英塑胶制品有限公司
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog