Air cylinder liner used for Stirling engine and processing process for air cylinder liner

A Stirling engine and processing technology, which is used in machines/engines, hot gas varicap engine devices, metal material coating processes, etc. problems, to achieve the effect of shortening the processing cycle, improving corrosion resistance, and improving cavitation

Active Publication Date: 2016-11-09
无锡市锡达电子科技有限公司
View PDF2 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] 1. There are many processes, and a variety of mechanical equipment is required, such as lathes, boring machines, internal grinding, external grinding and honing machines, so the production cycle is long and the manufacturing cost is high;
[0006] 2. The corrosion resistance of materials such as cast iron or structural steel is poor, and the surface layer of the cooling medium is easily corroded, fatigued and cracked, so the service life is short;

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0026] Specific embodiment one: a cylinder liner for a Stirling engine, in terms of mass percentage, the composition of the cylinder liner is: C: 0.03%, Ni: 4.5%, Mo: 3.0%, Cr: 22%, P : 0.03%, S: 0.02%, Mn: 2.00%, Si: 1.00%, N: 0.14%, and the balance is Fe.

[0027] The above-mentioned production process for the cylinder liner of Stirling engine comprises the following steps:

[0028] Step 1, carry out batching according to the above-mentioned component mass percentage that is used for the cylinder liner of Stirling engine;

[0029] Step 2, casting the ingredients in step 1 to produce steel pipe raw materials;

[0030] Step 3, cutting the steel pipe raw material in step 2 into a cylinder liner blank by a sawing machine;

[0031] Step a, carry out semi-finished turning on the outer circle and inner hole of the cylinder liner blank obtained in step 3 by a numerically controlled lathe;

[0032] Step b. Perform aging treatment on the cylinder liner blank obtained in step a in a...

specific Embodiment 2

[0041] Specific embodiment two: a cylinder liner for a Stirling engine, in terms of mass percentage, the composition of the cylinder liner is: C: 0.02%, Ni: 5%, Mo: 3.1%, Cr: 23%, P : 0.02%, S: 0.01%, Mn: 1.9%, Si: 0.9%, N: 0.15%, and the balance is Fe.

[0042] The above-mentioned production process for the cylinder liner of Stirling engine comprises the following steps:

[0043] Step 1, carry out batching according to the above-mentioned component mass percentage that is used for the cylinder liner of Stirling engine;

[0044] Step 2, casting the ingredients in step 1 to produce steel pipe raw materials;

[0045] Step 3, cutting the steel pipe raw material in step 2 into a cylinder liner blank by a sawing machine;

[0046] Step a, carry out semi-finished turning on the outer circle and inner hole of the cylinder liner blank obtained in step 3 by a numerically controlled lathe;

[0047] Step b. Perform aging treatment on the cylinder liner blank obtained in step a in a vac...

specific Embodiment 3

[0056] Specific embodiment three: a cylinder liner for a Stirling engine, in terms of mass percentage, the composition of the cylinder liner is: C: 0.025%, Ni: 5.5%, Mo: 3.3%, Cr: 23%, P : 0.02%, S: 0.02%, Mn: 1.8%, Si: 0.8%, N: 0.16%, and the balance is Fe.

[0057] The above-mentioned production process for the cylinder liner of Stirling engine comprises the following steps:

[0058] Step 1, carry out batching according to the above-mentioned component mass percentage that is used for the cylinder liner of Stirling engine;

[0059] Step 2, casting the ingredients in step 1 to produce steel pipe raw materials;

[0060] Step 3, cutting the steel pipe raw material in step 2 into a cylinder liner blank by a sawing machine;

[0061] Step a, carry out semi-finished turning on the outer circle and inner hole of the cylinder liner blank obtained in step 3 by a numerically controlled lathe;

[0062] Step b. Perform aging treatment on the cylinder liner blank obtained in step a in ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides an air cylinder liner used for a Stirling engine, and performance of an air cylinder body is greatly improved. The air cylinder liner consists of the following components in percentage by mass: less than or equal to 0.03% of C, 4.5-6.5% of Ni, 3.0-3.5% of Mo, 22-23% of Cr, less than or equal to 0.03% of P, less than or equal to 0.02% of S, less than or equal to 2.00% of Mn, less than or equal to 1.00% of Si, 0.14-0.20% of N and the balance Fe. Meanwhile, the invention further provides a processing process for the air cylinder liner; and the process is simple, and equipment investment is less, so that manufacturing cost is reduced and a processing period is shortened.

Description

technical field [0001] The invention relates to the technical field of a Stirling engine, in particular to a cylinder liner for a Stirling engine and a processing technology thereof. Background technique [0002] The Stirling engine is a closed-cycle piston engine with external heating. The closed cylinder of the Stirling engine is filled with a certain volume of working fluid. The upper part of the piston in the cylinder is a hot chamber, and the lower part of the piston in the cylinder is a cold chamber. The hot chamber mainly plays the role of expansion, and the cold chamber mainly plays the role of compression, driving the piston to do work. [0003] The cylinder liner, the cylinder head and the piston together constitute the working space of the cylinder, which is the lead of the reciprocating motion of the piston, and is cooled by cooling water outside. destroy. [0004] Existing cylinder liners are generally produced and processed using wear-resistant alloy cast iro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/44C22C38/58C22C38/02C22C38/04C21D9/00C23C8/38B23P15/00F02G1/053
CPCB23P15/00C21D9/0068C22C38/001C22C38/02C22C38/04C22C38/44C22C38/58C23C8/38F02G1/053
Inventor 朱锡良过宏鸣朱雯婷沈惠春
Owner 无锡市锡达电子科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products