Foam material

A foaming material and foaming agent technology, applied in the field of foaming materials, can solve the problems of poor impact resistance and poor durability, and achieve the effects of good wind pressure resistance, excellent thermal insulation and high compressive strength

Inactive Publication Date: 2016-11-16
张莘蔓
View PDF1 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to provide a foaming material to s

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Foam material
  • Foam material
  • Foam material

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0030] The preparation method of the novel insulating brick comprises the following steps:

[0031] S1: Preparation of hollow bricks

[0032] Mix cement, shale ore, ceramsite, lime, and pumice, and stir evenly at a speed of 200-400r / min to make hollow bricks;

[0033] S2: Preparation of foamed material

[0034] S21: Stir cement, glyoxal and water evenly at a speed of 100-300r / min to prepare a slurry;

[0035] S22: Calcium carbonate, barium sulfate, bentonite, magnesium borate, rice straw powder, AR glass fiber, carboxymethyl cellulose, water reducer, foaming agent, foam regulator, catalyst, crosslinking agent and stabilizer The foaming agent is stirred for 2-3 hours at a speed of 60-100r / min to obtain a foam liquid;

[0036] S23: Add the foam liquid prepared in step S22 to the slurry prepared in step S21, and stir evenly at a rotating speed of 150-200r / min to obtain a foaming material;

[0037] S3: Preparation of insulation bricks

[0038] Fill the foam material prepared ...

Embodiment 1

[0041] A new type of thermal insulation brick, comprising a hollow brick as a brick body shell and a foaming material filled in the cavity of the brick body, the hollow brick includes the following raw materials in parts by weight: 55 parts of cement, 40 parts of shale ore, pottery 25 parts of grains, 6 parts of lime, 9 parts of pumice; the foaming material is in parts by weight, including the following raw materials: 36 parts of cement, 3 parts of calcium carbonate, 2 parts of barium sulfate, 2 parts of bentonite, 2 parts of magnesium borate 2 parts, rice straw powder 2 parts, AR glass fiber 0.8 parts, carboxymethyl cellulose 0.6 parts, water reducer 2 parts, foaming agent 0.6 parts, foam regulator 0.4 parts, catalyst 0.2 parts, crosslinking agent 0.5 parts , 0.3 parts of foam stabilizer, 25 parts of glyoxal, and 280 parts of water.

[0042] The particle size of the rice straw powder is ≤300 μm, and the moisture content is ≤14%.

[0043] The water reducer is a polycarboxylat...

Embodiment 2

[0061]A new type of thermal insulation brick, comprising a hollow brick as a brick body shell and a foaming material filled in the cavity of the brick body, the hollow brick includes the following raw materials in parts by weight: 45 parts of cement, 35 parts of shale ore, pottery 20 parts of grains, 4 parts of lime, 6 parts of pumice; the foaming material is in parts by weight, including the following raw materials: 28 parts of cement, 3 parts of calcium carbonate, 2 parts of barium sulfate, 2 parts of bentonite, 1 part of magnesium borate 1 part, rice straw powder 1 part, AR glass fiber 0.6 part, carboxymethyl cellulose 0.4 part, water reducing agent 1.5 part, foaming agent 0.2 part, foam regulator 0.2 part, catalyst 0.1 part, crosslinking agent 0.3 part , 0.1 parts of foam stabilizer, 20 parts of glyoxal, and 240 parts of water.

[0062] The particle size of the rice straw powder is ≤300 μm, and the moisture content is ≤14%.

[0063] The water reducer is a polycarboxylate ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a foam material. The foam material is prepared from, by weight, 28-45 parts of cement, 3-4 parts of calcium carbonate, 2-3 parts of barium sulfate, 2-3 parts of bentonite, 1-2 parts of magnesium borate, 1-2 parts of rice straw powder, 0.6-1 part of AR glass fibers, 0.4-0.8 part of carboxymethylcellulose, 1.5-2.5 parts of a water reducing agent, 0.2-0.8 part of a foaming agent, 0.2-0.6 part of a foaming regulator, 0.1-0.3 part of a catalyst, 0.3-0.6 part of a crosslinking agent, 0.1-0.5 part of foam stabilizer, 20-30 parts of glyoxal and 240-300 parts of water. An environment-friendly concrete brick made of the foam material has the advantages of being good in heat preservation and heat insulation performance and sound insulation effect, light, resistant to pressure and the like.

Description

technical field [0001] The invention belongs to the technical field of building material preparation, and in particular relates to a foaming material. Background technique [0002] With the popularization of building energy saving and the continuous improvement of people's demand for the comfort of living environment, thermal insulation materials have been paid more and more attention by people. Existing thermal insulation composite bricks or blocks mainly include multiple forms such as inlaying thermal insulation materials, setting thermal insulation interlayers, thermal insulation holes, and trenches. As one of the thermal insulation materials for houses, non-fired foamed bricks at room temperature are more and more popular because of their thermal insulation, sound insulation, fire prevention, and strength superior to traditional thermal insulation materials. However, the foaming materials currently on the market have disadvantages such as poor impact resistance and rela...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/00C04B38/02
CPCC04B28/00C04B2201/20C04B2201/32C04B2201/50C04B14/108C04B18/023C04B22/064C04B14/16C04B14/28C04B14/368C04B14/104C04B22/0013C04B18/248C04B14/42C04B24/008C04B24/124C04B24/045C04B24/40C04B24/42C04B2103/302C04B2103/0068C04B2103/48C04B38/02
Inventor 张莘蔓
Owner 张莘蔓
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap