A kind of hole making method of carbon fiber reinforced pantograph carbon slide carbon strip

A pantograph carbon slide, carbon slide technology, applied in carbon fiber reinforced pantograph carbon slide carbon strip hole making field, carbon fiber reinforced carbon slide carbon strip hole making field, can solve the problem of reducing the resistivity of carbon strip, can not be achieved, etc. problems, to achieve low cost, long service life, and good lubricating performance

Active Publication Date: 2019-02-01
SUZHOU DONEKA NEW MATERIALS CORP LTD
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The metal-impregnated carbon slide is to fill a large number of pores in the carbon strip substrate with metal to form a practical condensate. In the past, the pores on the carbon strip were naturally formed during the production process of the carbon strip. These pores were scattered in the form of points. In the carbon strip, the impregnated metal is also scattered in the carbon strip in dots, which cannot achieve the best effect of reducing the resistivity of the carbon strip

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of hole making method of carbon fiber reinforced pantograph carbon slide carbon strip
  • A kind of hole making method of carbon fiber reinforced pantograph carbon slide carbon strip
  • A kind of hole making method of carbon fiber reinforced pantograph carbon slide carbon strip

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0074] 1. Prepare raw materials according to the following weight ratio

[0075]

[0076] 2. Raw material mixing

[0077] (1) Add carbon black, pitch coke, carbon fiber, graphite, and sulfur into the mixer and stir for 30 minutes, and mix evenly to obtain the first mixture;

[0078] (2) Heating the first mixture to 130°C, then adding molten asphalt into the first mixture, stirring for 200 minutes, and mixing evenly to obtain the second mixture;

[0079] (3) The second mixture is placed in the roll machine for the first roll treatment to obtain a sheet material; the sheet material is placed in a pulverizer for crushing to obtain a crushed material; the crushed material is placed in a roll machine Carrying out the second roll treatment to obtain a sheet-like third mixture with a thickness of 1-3mm; wherein the treatment temperature of the roll machine is 100°C;

[0080] (4) placing the third mixture in a pulverizer for pulverization to obtain a fourth mixture with a particl...

Embodiment 2

[0097] 1. Prepare raw materials according to the following weight ratio

[0098]

[0099] 2. Raw material mixing

[0100] (1) Add carbon black, pitch coke, carbon fiber, graphite, and sulfur into the blender and stir for 200 minutes, and mix evenly to obtain the first mixture;

[0101] (2) Heating the first mixture to 210°C, then adding molten asphalt to the first mixture, stirring for 30 minutes, and mixing evenly to obtain the second mixture;

[0102] (3) The second mixture is placed in the roll machine for the first roll treatment to obtain a sheet material; the sheet material is placed in a pulverizer for crushing to obtain a crushed material; the crushed material is placed in a roll machine Carrying out the second roll treatment to obtain a third flake mixture with a thickness of 1-3mm; wherein the treatment temperature of the roll machine is 180°C;

[0103] (4) placing the third mixture in a pulverizer for pulverization to obtain a fourth mixture with a particle siz...

Embodiment 3

[0120] 1. Prepare raw materials according to the following weight ratio

[0121]

[0122] 2. Raw material mixing

[0123] (1) Add carbon black, pitch coke, carbon fiber, graphite, and sulfur into the mixer and stir for 60 minutes, and mix evenly to obtain the first mixture;

[0124] (2) Heating the first mixture to 145°C, then adding molten asphalt to the first mixture, stirring for 90 minutes, and mixing evenly to obtain the second mixture;

[0125](3) The second mixture is placed in the roll machine for the first roll treatment to obtain a sheet material; the sheet material is placed in a pulverizer for crushing to obtain a crushed material; the crushed material is placed in a roll machine Carrying out the second roll treatment to obtain the third flake mixture with a thickness of 1-3mm; wherein the treatment temperature of the roll machine is 110°C;

[0126] (4) placing the third mixture in a pulverizer for pulverization to obtain a fourth mixture with a particle size ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides a method for making pores on a carbon-fiber-reinforced pantograph carbon slide plate carbon strip, and the method comprises the following steps: uniformly mixing a pantograph carbon slide plate carbon strip raw material and a pore forming agent to obtain a mixture; pressing the mixture to obtain a carbon slide plate carbon strip initial blank containing the pore forming agent; calcining the carbon slide plate carbon strip initial blank to burn out the pore forming agent in the carbon slide plate carbon strip initial blank to form pores in uniform distribution in the carbon slide plate carbon strip so as to obtain a carbon slide plate carbon strip with a pore structure. The prepared carbon strip has the advantages of high porosity, low resistivity, strong electric conductivity, high strength and long service life by addition of the pore-forming agent to control the number and shape of the pores in the carbon strip.

Description

technical field [0001] The invention relates to a pore-making method for a carbon fiber-reinforced pantograph carbon strip, in particular to a pore-making method for a carbon fiber-reinforced carbon strip with high porosity and uniform distribution, and belongs to the technical field of electric locomotives. Background technique [0002] An electric locomotive is a locomotive that obtains electric energy from the catenary and is driven by a traction motor. With the development of electrified railways, electric locomotives have also developed rapidly, from DC motor locomotives to AC drive electric locomotives. In 1979, the first high-power AC drive locomotive was born in Germany, ushering in a new era of development of electric locomotives. In order to obtain large capacity and high speed, the power of electric locomotives is increasing. In 1961, the Baoji-Fengzhou line, China's first electrified line, was completed. The power of electric locomotives has grown from 4740kw t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline