Bio-based diatom mud coating material preparation method

A technology based on diatom mud and paint, applied in the field of diatom mud paint preparation, can solve the problems of harming the environment and human health, and the paint is prone to produce harmful substances, and achieves the effects of reducing the preparation cost, strengthening the self-cleaning function and simple process

Inactive Publication Date: 2016-11-30
张静
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The main technical problem to be solved by the present invention is to provide a kind of bio-based diatom mud for the diatom mud coating currently on the market, in which a large amount of artificial synthetic additives are added, which makes the coating easy to produce harmful substances and endanger the environment and human health. The preparation method of the paint comprises pretreatment of bamboo chips to make bamboo chip powder, and calcining the powder in sections to make bamboo charcoal fiber; then ultrasonically extracting Coptis chinensis, Radix Astragali, and tea leaves, collecting filtrate and filter residue, and then making the filter residue Boil, then filter, combine the filtrates to obtain a mixed extract, then mix with bamboo charcoal fiber and add nano-diatomaceous earth, sepiolite powder, nano-activated carbon, shell powder, chitin, fish gelatin, and shake. Get a Bio-Based Diatom Mud Paint

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0019] First weigh 100g of bamboo slices, cut the bamboo slices into 5cm pieces, dry the cut bamboo slices in a 95°C oven until the moisture content of the bamboo slices is 20%, and place the dried bamboo slices in a 25KHz plasma processor , under normal temperature and pressure for 20 minutes to obtain pretreated bamboo chips; then add the pretreated bamboo chips to pulverizer, sieve to obtain 100 mesh bamboo chip powder, and add the bamboo chip powder to the muffle furnace, Control the temperature at 300°C, calcining for 6 hours, raising the temperature to 600°C, calcining for 5 hours, continuing to raise the temperature to 1000°C, and calcining for 8 hours to obtain bamboo charcoal fibers for later use; In the beaker, add 200mL deionized water into the beaker, place the beaker on a 3000W ultrasonic extraction machine, ultrasonically extract for 20min, filter, collect the filtrate and filter residue respectively, put the filter residue in the beaker, add 100mL deionized water...

example 2

[0022] First weigh 150g of bamboo slices, cut the bamboo slices into 8cm pieces, dry the cut bamboo slices in an oven at 100°C until the moisture content of the bamboo slices is 25%, and place the dried bamboo slices in a 28KHz plasma processor , under normal temperature and pressure for 25min to obtain pretreated bamboo chips; then add the pretreated bamboo chips to pulverize in a pulverizer, and sieve to obtain 110 mesh bamboo chip powders, and add the bamboo chip powders to the muffle furnace, Control the temperature at 350°C, calcined for 7 hours, raise the temperature to 700°C, calcined for 5.5 hours, continue to raise the temperature to 1100°C, and calcined for 9 hours to obtain bamboo charcoal fibers for later use; into the beaker, add 250mL deionized water to the beaker, place the beaker on a 3100W ultrasonic extraction machine, ultrasonically extract for 25min, filter, collect the filtrate and filter residue respectively, put the filter residue in the beaker, add 150mL...

example 3

[0025]First weigh 200g of bamboo slices, cut the bamboo slices into 10cm pieces, dry the cut bamboo slices in an oven at 105°C until the moisture content of the bamboo slices is 30%, and place the dried bamboo slices in a 30KHz plasma processor , treated under normal temperature and pressure for 30min to obtain pretreated bamboo chips; then add the pretreated bamboo chips to pulverizer, sieve to obtain 120 mesh bamboo chip powder, and add the bamboo chip powder to the muffle furnace, Control the temperature at 400°C, calcining for 8 hours, raising the temperature to 800°C, calcining for 6 hours, continuing to raise the temperature to 1200°C, and calcining for 10 hours to obtain bamboo charcoal fibers for later use; In the beaker, add 300mL deionized water into the beaker, place the beaker on a 3200W ultrasonic extraction machine, ultrasonically extract for 30min, filter, collect the filtrate and filter residue respectively, put the filter residue in the beaker, add 200mL deioni...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a bio-based diatom mud coating, which belongs to the technical field of diatom mud coating preparation. In the present invention, bamboo chips are pretreated to make bamboo chip powder, and the powder is calcined in sections to make bamboo charcoal fiber; then Coptidis Rhizoma, Radix Astragali, and tea leaves are subjected to ultrasonic extraction, filtrate and filter residue are collected, and then the filter residue is boiled, and then Filtrate, combine the filtrates to obtain a mixed extract, then mix with bamboo charcoal fiber and add nano-diatomaceous earth, sepiolite powder, nano-activated carbon, shell powder, chitin, fish gelatin, and shake to obtain a bio-based Diatom mud coating. The invention is easy to operate, and the prepared diatom mud paint is natural and safe in raw materials without adding any artificially synthesized additives and will not produce harmful substances. The paint itself has a self-cleaning function, can be used for a long time, and has broad market prospects.

Description

technical field [0001] The invention discloses a bio-based diatom mud coating, which belongs to the technical field of diatom mud coating preparation. Background technique [0002] Diatom mud is a kind of interior decoration wall material with diatomite as the main raw material. It has the functions of eliminating formaldehyde, purifying air, adjusting humidity, releasing negative oxygen ions, fire retardant, self-cleaning of walls, sterilization and deodorization, etc. It is used to replace wallpaper and latex paint. It is suitable for interior wall decoration in villas, apartments, hotels, homes, hospitals, etc. Therefore, diatom mud coating is a new type of environmentally friendly coating. Diatom mud has the functions of eliminating formaldehyde and releasing negative oxygen ions. , calling it "breathable environmentally friendly functional wall material". [0003] The main raw material of diatom mud is diatomaceous earth, a diatom mineral formed by marine seaweed plant...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B30/02C04B14/38
CPCC04B30/02C04B14/386C04B2111/00017C04B2111/00482C04B14/08C04B20/008C04B14/042C04B14/022C04B14/28C04B24/38C04B24/14C04B2103/0068
Inventor 张静孟浩影薛蕾
Owner 张静
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com