A preparation method of self-cleaning antibacterial health-care physiological underwear
A self-cleaning and underwear technology, applied in biochemical fiber treatment, underwear, fiber treatment, etc., can solve the problems that affect the feel and comfort of underwear, and it is difficult to obtain antibacterial effect in the post-finishing process, so as to achieve the effect of easy cleaning
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0020] The crotch of the underwear is woven with 32S / 1 wood pulp bamboo pulp cellulose fiber (80 / 20); the belly of the underwear is woven with 40S / 2 modal fiber and pure cotton fiber (50 / 50); Solution finishing, the amount of zirconia solution is 5% of the dry cloth weight, and dried in a 140°C open-width dryer; the underwear crotch fabric is mixed with nano-silver complex antibacterial agent, zinc-doped nano-titanium oxide catalyst, Carboxylate rolling groove, the dosage of nano-silver complex antibacterial agent is 3% of dry cloth weight, the dosage of zinc-doped nano-titanium oxide catalyst is 1.5% of dry cloth weight, and the dosage of phosphate ester is 1.5% of dry cloth weight 1%, and then dried in an open-width dryer at a drying temperature of 140°C.
Embodiment 2
[0022] The crotch of the underwear is made of 40S / 2 wood pulp bamboo pulp cellulose fiber (70 / 30) blended fabric; the belly of the underwear is made of 60S / 2 cotton and mulberry silk fiber (90 / 10) blended fabric; Solution finishing, the amount of zirconia solution is 3% of the dry cloth weight, and dried in a 120°C open-width dryer; the crotch fabric of the underwear is treated with nano-iodorone antibacterial agent, zinc-doped nano-titanium oxide catalyst, polysorbate The rolling groove of ester, the consumption of nano-iodoxone antibacterial agent is 2.5% of dry cloth weight, the consumption of zinc-doped nano-titanium oxide catalyst is 1.0% of dry cloth weight, and the consumption of polysorbate is 0.8% of dry cloth weight , and then dried in an open-width dryer at a drying temperature of 135°C.
Embodiment 3
[0024] The crotch of the underwear is woven with 80S / 2 wood pulp cellulose fiber, double layer; the abdomen of the underwear is woven with 60S / 2 cotton, 60S / 2 modal, and mulberry silk fiber (70 / 20 / 10); the fabric of the underwear abdomen has passed 4000ppm nanometer level Far-infrared solution finishing, the amount of zirconia solution is 4% of the dry cloth weight, and dried in a 130°C open-width dryer; the crotch fabric of the underwear is treated with nano-iodorone antibacterial agent, silver-doped nano-titanium oxide catalyst, The rolling groove of polysorbate, the consumption of nano-iodoxorone antibacterial agent is 2% of dry cloth weight, the consumption of silver-doped nano-titanium oxide catalyst is 1.0% of dry cloth weight, and the consumption of polysorbate is 2% of dry cloth weight. 0.8%, and then dried in an open-width dryer at a drying temperature of 135°C.
[0025] See attached figure 1 , which is the antibacterial effect figure of the underwear crotch fabric m...