High-shielding flame-retardant FPI release paper and preparation method thereof

A technology of release paper and shielding layer, applied in the field of release paper, can solve the problems that the coating layer is easy to reach the melting point and ignition point, the use of release paper is limited, and the characteristics of the release paper are single, so as to prevent high temperature melting and burning , good shielding performance, and the effect of improving safety

Inactive Publication Date: 2016-12-07
JIXIANGBAO TAICANG RELEASE MATERIAL TECH CO LTD
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Release paper has a wide range of applications, such as electronics, medical and other fields. The existing release paper has single characteristics, and the use of release paper is limited due to its special working environment.
Such as external electromagnetic signal shielding, and the stability of the release paper in an environment with high air humidity; for example, in a high temperature environment, the coating layer on the release paper can easily reach the melting point and ignition point, thus causing safety hazards

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A kind of high shielding, flame retardant FPI release paper, including base paper, shielding layer, coating layer and release agent layer, described base paper is white kraft paper, both sides of described white kraft paper are all sprayed with shielding layer, the coating layer is evenly coated on the shielding layer, and the release agent layer is an organic silicon layer, which is evenly coated on the coating layer;

[0022] The shielding layer is composed of the following components in parts by weight: 35 parts of conductive polypropylene resin, 20 parts of conductive powder, 1 part of silane coupling agent, 3 parts of dispersant, and 20 parts of alcohol solvent;

[0023] The coating layer is composed of the following components by weight: 35 parts of low-density PE, 10 parts of high-density PE, 7 parts of polyolefin halogen-free flame retardant, 10 parts of high-fluidity polyamide, 1 part of stabilizer, aluminum oxide 2.5 parts, 2.5 parts of magnesium oxide, 1 part...

Embodiment 2

[0030] A kind of high shielding, flame retardant FPI release paper, including base paper, shielding layer, coating layer and release agent layer, described base paper is white kraft paper, both sides of described white kraft paper are all sprayed with shielding layer, the coating layer is evenly coated on the shielding layer, and the release agent layer is an organic silicon layer, which is evenly coated on the coating layer;

[0031] The shielding layer is composed of the following components by weight: 55 parts of conductive polypropylene resin, 40 parts of conductive powder, 3 parts of silane coupling agent, 5 parts of dispersant, and 45 parts of alcohol solvent;

[0032] The coating layer is composed of the following components by weight: 45 parts of low-density PE, 20 parts of high-density PE, 9 parts of melamine pyrophosphate flame retardant, 20 parts of high-fluidity polyamide, 2 parts of stabilizer, aluminum oxide 3.5 parts, 3.5 parts of magnesium oxide, 3 parts of par...

Embodiment 3

[0039] A kind of high shielding, flame retardant FPI release paper, including base paper, shielding layer, coating layer and release agent layer, described base paper is white kraft paper, both sides of described white kraft paper are all sprayed with shielding layer, the coating layer is evenly coated on the shielding layer, and the release agent layer is an organic silicon layer, which is evenly coated on the coating layer;

[0040] The shielding layer is composed of the following components by weight: 40 parts of conductive polypropylene resin, 25 parts of conductive powder, 2 parts of silane coupling agent, 4 parts of dispersant, and 30 parts of alcohol solvent;

[0041] The coating layer is composed of the following components by weight: 38 parts of low-density PE, 13 parts of high-density PE, 8 parts of melamine pyrophosphate flame retardant, 12 parts of high-fluidity polyamide, 1.5 parts of stabilizer, aluminum oxide 3 parts, 3 parts of magnesium oxide, 1 part of steari...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides high-shielding flame-retardant FPI release paper and a preparation method thereof. The high-shielding flame-retardant release paper comprises base paper, shielding layers, coating layers and release agent layers, wherein the base paper is white kraft paper; two sides of the white kraftpaper are coated with the shielding layers; the coating layers uniformly coat the corresponding shielding layers; the release agent layers are organic silicon layers and uniformly coat the corresponding coating layers. The shielding layers of the release paper provided by the invention have good shielding performance and are well applied in the electric field; the coating layers of the release paper have a flame retardant function, protect the integral release paper, and have a high-temperature resisting effect; by using the coating layers, the phenomena of high-temperature melting and burning are prevented, and the safety of production is improved; meanwhile, the release paper prepared by the preparation method provided by the invention has a dense structure and does not absorb water, so that the safety of FPI is further guaranteed.

Description

technical field [0001] The invention relates to the technical field of release paper, in particular to a high-shielding, flame-retardant FPI release paper and a preparation method thereof. Background technique [0002] Release paper, also known as release paper and anti-adhesive paper, is mainly used to stick the adhesive layer on the surface of the tape to protect the surface of the tape. The existing release paper is generally coated with a film layer (the material used is mainly polyethylene) on the surface of the bottom paper layer of the release paper, and then coated with a layer of release agent on the surface of the film layer ( The material used is mainly silicone oil) to obtain release paper. Release paper has a wide range of applications, such as electronics, medical and other fields. The existing release paper has single characteristics, and the use of release paper is limited due to its special working environment. Such as external electromagnetic signal shiel...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D5/24C09D7/12C08L23/06C08L23/02C08L77/00C08K3/22D21H27/30D21H23/50
CPCC09D133/00C08K5/54C08K2201/001C08L23/06C08L2201/02C08L2201/08C08L2203/20C08L2205/02C08L2205/025C08L2205/035C08L2207/062C08L2207/066C09D5/24C09D7/61D21H23/50D21H27/30C08L23/02C08L77/00C08K2003/2227C08K2003/222
Inventor 於险峰
Owner JIXIANGBAO TAICANG RELEASE MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com