Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Outer-wall insulating material and preparation method thereof

A technology of external wall insulation and granules, which is applied in the field of building materials, can solve problems such as environmental pollution, soil erosion, and destruction of ecological balance, and achieve the effects of good thermal insulation, light weight, and good fire resistance

Inactive Publication Date: 2016-12-21
合肥广能新材料科技有限公司
View PDF5 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, because excavation of clay, shale, loess, sludge, etc. will cause soil erosion, environmental pollution, and damage to ecological balance, it is not suitable for popularization and application.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] An external wall thermal insulation material, calculated in parts by weight, comprising the following components: 35 parts of polystyrene foam particles, 55 parts of Portland cement, 12 parts of slag, 5 parts of wood fiber, and 4 parts of sodium carboxymethyl cellulose , 3 parts of tetrafluoroethane and 45 parts of water. Polystyrene foam particles are lightweight, uniform particle size, surface modified and thermally insulating particles.

[0016] The preparation method includes the following steps:

[0017] First, weigh the required Portland cement, slag, wood fiber, sodium carboxymethyl cellulose and water according to the formula proportion to a uniform slurry-like substance; add tetrafluoroethane to the foaming machine for foaming, and then Inject the foam into the Portland cement slurry and stir until it is uniform; then add the polystyrene foam particles into the foamed Portland cement slurry according to the formula ratio, mix and stir evenly, and lay an alkali...

Embodiment 2

[0019] An external wall thermal insulation material, calculated in parts by weight, comprising the following components: 30 parts of polystyrene foam particles, 50 parts of Portland cement, 10 parts of slag, 6 parts of wood fiber, and 5 parts of sodium carboxymethyl cellulose , 2 parts of tetrafluoroethane, 2 parts of cyclopentane, 2 parts of carbon dioxide and 40 parts of water. Polystyrene foam particles are lightweight, uniform particle size, surface modified and thermally insulating particles.

[0020] The preparation method includes the following steps:

[0021] First, weigh the required Portland cement, slag, wood fiber, sodium carboxymethyl cellulose and water according to the formula proportion to a uniform slurry-like substance; add tetrafluoroethane, cyclopentane and carbon dioxide to foam The foam is foamed in the machine, and then the foam is injected into the Portland cement slurry and stirred until uniform; then the polystyrene foam particles are added to the fo...

Embodiment 3

[0023] An external wall thermal insulation material, calculated in parts by weight, comprising the following components: 40 parts of polystyrene foam particles, 60 parts of Portland cement, 15 parts of slag, 4 parts of wood fiber, and 3 parts of sodium carboxymethyl cellulose , 3 parts of cyclopentane and 40 to 50 parts of water; polystyrene foam particles are lightweight, uniform in particle size, surface-modified and heat-insulated.

[0024] The preparation method includes the following steps:

[0025] First, weigh the required Portland cement, slag, wood fiber, sodium carboxymethyl cellulose and water according to the formula proportion to a uniform slurry-like substance; add cyclopentane to the foaming machine for foaming, and then put the The foam is injected into the Portland cement slurry and stirred until uniform; then the polystyrene foam particles are added to the foamed Portland cement slurry according to the formula ratio, mixed and stirred evenly, and an alkali-re...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an outer-wall insulating material and a preparation method thereof. The outer-wall insulating material comprises the following components in parts by weight: 30-40 parts of polystyrene foam particles, 50-60 parts of Portland cement, 10-15 parts of mineral slag, 4-6 parts of wood fiber, 3-5 parts of sodium carboxymethylcellulose, 0-6 parts of foaming agent and 40-50 parts of water. The preparation method comprises the following steps of: firstly weighing the required Portland cement, mineral slag, wood fiber, sodium carboxymethylcellulose and water according to the proportion of a formula, stirring all the components to be uniform slurry-like substance; adding the foaming agent into a foaming machine for foaming, then injecting foam into Portland cement slurry, and stirring to be uniform; then adding the polystyrene foam particles into the Portland cement slurry in ratio, mixing and stirring to be uniform, casting, forming and then naturally curing. The outer-wall insulating material provided by the invention has the advantages that the combustion performance can meet the standard of an A-level incombustible material, the strength is higher and the heat-conductivity coefficient is low.

Description

technical field [0001] The invention belongs to the technical field of building materials, and particularly relates to an external wall thermal insulation material and a preparation method thereof. Background technique [0002] External wall thermal insulation system consists of thermal insulation layer, protective layer and fixing materials (adhesives, anchors, etc.) and is a general term for non-load-bearing thermal insulation structures installed on the surface of external walls. External thermal insulation of external walls can reduce the impact of cold bridges, and at the same time protect the main wall materials from the stress of temperature denaturation. It is also the thermal insulation practice strongly advocated by the state. [0003] At present, the external thermal insulation systems used in our country mainly have the following forms: expanded polystyrene board (EPS) thin plastered wall external thermal insulation system, large mold built-in (with mesh, no mes...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B38/10C04B38/08E04B1/78C04B16/08
CPCC04B28/04C04B16/08C04B2201/32E04B1/78C04B18/141C04B16/02C04B24/383C04B24/005C04B38/106C04B38/08C04B24/00C04B22/06
Inventor 刘涛
Owner 合肥广能新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com