A reinforced bone china for daily use and a preparing method thereof

A daily-use porcelain and bone technology, applied in the field of ceramics, can solve the problems of poor thermal shock resistance of products, difficult quality of bone china products, high lead and cadmium dissolution, and achieve improved thermal shock resistance, phospho-silicate The effect of complete glass phase network and uniform crystal growth and development

Active Publication Date: 2016-12-21
GUANGDONG BENING CERAMICS IND CO LTD
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the quality of existing bone china products is difficult to control. The main problems are low strength, poor thermal shock resistance, high lead and cadmium dissolution, and insufficient smoothness of the glaze.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A reinforced bone china for daily use and a preparing method thereof
  • A reinforced bone china for daily use and a preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] The preparation of embodiment 1 additive ZL

[0043] The additive ZL is obtained by grinding the following components into a ball mill, sieving, dehydrating, pre-firing, and superfine grinding with zirconium corundum grinding media (on the order of 1000g).

[0044] In terms of parts by mass, there are 70 parts of zirconia; 6 parts of feldspar; 3 parts of rare earth; and 5 parts of clay.

[0045] The fine pulverization is pulverization to a particle size range of 250-350 mesh.

[0046] The main technical conditions of the pre-firing are: firing with an oxidizing flame, and the key condition is to keep warm at about 1250° C. for 2 hours. Others refer to existing routines.

Embodiment 2

[0047] The preparation of embodiment 2 additive ZL

[0048] The additive ZL is obtained by using the following components to be finely pulverized by a ball mill, sieved, dehydrated, pre-fired, and superfinely pulverized by a zirconium corundum grinding medium.

[0049] In terms of parts by mass, there are 85 parts of zirconium silicate; 10 parts of feldspar; 5 parts of rare earth; and 2 parts of clay.

[0050] The fine pulverization is pulverization to a particle size range of 250-350 mesh.

[0051] The main technical conditions of the pre-firing are: firing with an oxidizing flame, and the key condition is to keep warm at about 1350° C. for 1.5 hours.

Embodiment 3

[0052] The preparation of embodiment 3 additive ZL

[0053] The additive ZL is obtained by using the following components to be finely pulverized by a ball mill, sieved, dehydrated, pre-fired, and superfinely pulverized by a zirconium corundum grinding medium.

[0054] In terms of parts by mass, there are 75 parts of zirconia; 8 parts of feldspar; 2 parts of rare earth; and 10 parts of clay.

[0055] The fine pulverization is pulverization to a particle size range of 250-350 mesh.

[0056]The main technical conditions of the pre-firing are: firing with an oxidizing flame, and the key condition is to keep the temperature at 1280° C. for 1 hour.

[0057] Art conditions are with reference to prior art routine.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A reinforced bone china for daily use and a preparing method thereof are disclosed. The bone china for daily use is prepared from, by mass, 1-3 parts of an additive ZL, 40-45 parts of bone char, 10-12 parts of quartz, 10-12 parts of feldspar, 24-28 parts of kaolin, 48-52 parts of water, 1-3 parts of a crystal form improving agent, 1-2 parts of a mineralizer and 1-3 parts of a phosphosilicate targeting fluxing agent. Through scientifically introducing the phosphosilicate targeting fluxing agent, introduction of potassium-containing and sodium-containing mineral raw materials is significantly reduced, and the sintering temperature and the expansion coefficient of a blank are controlled well. Through introducing the additive ZL, the crystal form improving agent and the mineralizer into bone china pug, uniform crystal growth in a stage of vitrification to form the china is ensured, a phosphosilicate glass phase network is further complete, and mechanical strength and thermal shock resistance of the bone china are finally improved. The bone china for daily use is high in mechanical strength, smooth in glaze, easy to clean, significantly reduced in lead and cadmium dissolving-out amounts, and good in thermal shock resistance.

Description

technical field [0001] The invention relates to the technical field of ceramics, in particular to a daily-use porcelain for strengthening bone and a preparation method thereof. Background technique [0002] Bone china porcelain is fine and smooth, with smooth glaze and soft luster. It looks like fat and jade. , the quality requirements for daily-use ceramics are getting higher and higher, and the application of bone china is becoming more and more extensive. It is recognized as the highest-grade porcelain in the world today, and is deeply loved by consumers. market expectation. [0003] However, the quality of existing bone china products is difficult to control. The main problems are low strength, poor thermal shock resistance, high lead and cadmium dissolution, and insufficient glaze. With the improvement of people's living standards, consumers have higher and higher requirements for daily-use porcelain, not only for its appearance, such as shape, decoration, etc., but a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B33/13C04B33/132C04B33/32
CPCC04B33/131C04B33/132C04B33/32C04B2235/3208C04B2235/3225C04B2235/3227C04B2235/3244C04B2235/3409C04B2235/3418C04B2235/3427C04B2235/3472C04B2235/443C04B2235/447Y02P40/60
Inventor 林秋杰
Owner GUANGDONG BENING CERAMICS IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com