A tile adhesive and fast technology, applied in the direction of solid waste management, sustainable waste treatment, climate sustainability, etc., can solve problems such as unfavorable construction workers, indoor environmental pollution, affecting people's health, etc., to shorten the construction period , short setting time, enhance the toughness of the glue

Active Publication Date: 2017-01-04
山东汉诺宝嘉新材料科技有限公司
View PDF5 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing polymer-based tile adhesives have a long curing time, which is not conducive to construction by construction personnel and reduces work efficiency.
In addition, the existing tile adhesives are relatively expensive in materials, and mostly use toxic low-molecular organic matter as the main component, which will undoubtedly lead to greater indoor environmental pollution and affect people's health.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Quickly-solidified tile adhesive

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A fast-setting tile adhesive, consisting of the following raw materials: 20kg of rapid hardening cement, 40kg of quartz sand, 10kg of fly ash, 10kg of heavy calcium, 2kg of redispersible latex powder, 0.2kg of cellulose ether, and starch ether 0.1kg, water repellent 0.2kg, retarder 0.1kg, early strength agent 1kg. The water-repellent agent is composed of the following raw materials in parts by weight: 60 parts of organosilane water-repellent agent, 10 parts of calcium stearate, 10 parts of stearic acid, and 5 parts of silane coupling agent. The retarder is composed of the following raw materials in parts by weight: 15 parts of citric acid, 20 parts of boric acid, 15 parts of calcium gluconate, and 5 parts of sodium phosphate. The early strengthening agent is composed of the following raw materials in parts by weight: 40 parts of aluminum sulfate, 15 parts of calcium formate, 5 parts of sodium metaaluminate, 5 parts of calcium oxide, and 5 parts of copper sulfate. The p...

Embodiment 2

[0041] A fast-setting tile adhesive, consisting of the following raw materials in kilograms: rapid hardening cement 25kg, quartz sand 45kg, fly ash 15kg, heavy calcium 15kg, redispersible latex powder 3kg , 0.35kg of cellulose ether, 0.2kg of starch ether, 0.35kg of water repellent, 0.25kg of retarder, and 3kg of early strength agent. The water repellent is composed of the following raw materials in parts by weight: 65 parts of organosilane water repellent, 15 parts of calcium stearate, 15 parts of stearic acid and 8 parts of silane coupling agent. The retarder is composed of the following raw materials in parts by weight: 20 parts of citric acid, 30 parts of boric acid, 20 parts of calcium gluconate, and 10 parts of sodium phosphate. The early strengthening agent is composed of the following raw materials in parts by weight: 50 parts of aluminum sulfate, 20 parts of calcium formate, 10 parts of sodium metaaluminate, 10 parts of calcium oxide and 10 parts of copper sulfate. T...

Embodiment 3

[0044] A fast-setting tile adhesive, composed of the following raw materials: 40kg of rapid hardening cement, 50kg of quartz sand, 20kg of fly ash, 20kg of heavy calcium, 4kg of redispersible latex powder, 0.5kg of cellulose ether, and starch ether 0.3kg, water repellent 0.5kg, retarder 0.4kg, early strength agent 5kg. The water-repellent agent is composed of the following raw materials in parts by weight: 70 parts of organosilane water-repellent agent, 20 parts of calcium stearate, 20 parts of stearic acid, and 10 parts of silane coupling agent. The retarder is composed of the following raw materials in parts by weight: 25 parts of citric acid, 40 parts of boric acid, 25 parts of calcium gluconate, and 15 parts of sodium phosphate. The early strengthening agent is composed of the following raw materials in parts by weight: 60 parts of aluminum sulfate, 25 parts of calcium formate, 15 parts of sodium metaaluminate, 15 parts of calcium oxide and 15 parts of copper sulfate. The...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to view more

Abstract

A quickly-solidified tile adhesive comprises the raw materials in parts by weight: 20-40 parts of quick-hardening cement, 40-50 parts of quartz sand, 10-20 parts of fly ash, 10-20 parts of calcium carbonate, 2-4 parts of redispersible latex powder, 0.2-0.5 part of cellulose ether, 0.1-0.3 part of starch ether, 0.2-0.5 part of water repellent, 0.1-0.4 part of retarder and 1-5 parts of early strength agent. The quick-hardening cement, the quartz sand and the fly ash are used as raw materials to prepare the quickly-solidified tile adhesive, the adhesive is short and adjustable in initial setting time, the strength growth is fast, the fixed waste fly ash generated by thermal power plants is effectively utilized, the adhesive also contains organic high-molecular polymer capable of being compounded with the ceramic tile and the indoor environment pollution cannot be caused.

Description

[0001] Technical field: [0002] The invention relates to a fast-setting tile adhesive. [0003] Background technique: [0004] Tile adhesives are mainly used to paste ceramic tiles, facing tiles, floor tiles and other materials. Because tile adhesives can make up for the defects of cement and ordinary polymer mortar, they are widely used in interior and exterior walls, floors, bathrooms, kitchens and other building decorations. At present, cement and sand mixed on site are often used as tile adhesives, and the traditional thick-layer bonding method is used to bond tiles. The annual consumption of yellow sand and cement is as high as more than 1 trillion tons, and there are still problems such as Inadequate bonding, hollowing, cracking, falling off, water seepage and other disadvantages. The polymer-based tile adhesives that are now popularized and used overcome the shortcomings of ordinary tile adhesives due to their waterproof, cohesive and durable properties. However, the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B14/06C04B18/08
CPCC04B14/06C04B18/08C04B28/00C04B2111/00637C04B14/28C04B2103/0057C04B24/383C04B24/38C04B2103/65C04B2103/22C04B2103/0068Y02W30/91
Inventor 魏永强陈强李太胜乔媛李景山
Owner 山东汉诺宝嘉新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap