A kind of preparation method of chitosan microsphere

A technology of chitosan microspheres and chitosan solutions, which is applied in the field of preparation of chitosan microspheres, can solve the problems of insufficient therapeutic effect, reduction, and increase of drug levels, and achieve high deacetylation degree and enzymatic hydrolysis efficiency High, reduce degradation effect

Active Publication Date: 2018-10-02
上海丽珠制药有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Through the traditional way of administration, most of the drug ingredients are released very quickly, causing the drug level in the body to rise rapidly, reach the peak and then decrease rapidly
For drugs, their effects are closely related to the concentration of the drug in the serum, and the drastic fluctuations often cause unacceptable side effects at the peak, and then insufficient therapeutic effect due to the low concentration of the drug in the serum

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] (1) Decalcification: After crushing 10g of insect carapaces, place them in 200g of dilute acid with a mass concentration of 10% and soak for 4 hours at 50°C, filter, wash the filter cake with water for 3-5 times and dry to obtain 7.2g of decalcified Product A;

[0034] (2) Deproteinization: put 7.2g decalcification product A, 0.09g trypsin, 0.09g papain, 0.18g alkaline lipase and 144g water in a three-necked flask, control the pH of the reaction solution to 7.5, and stir at 40°C After hydrolysis for 3 hours, filter, wash and dry the filter cake to obtain 4.3 g of deproteinized product B;

[0035] (3) Purification: 4.3g of deproteinized product B, 28g of hexanoic acid, 22g of oxalic acid, 14g of pyridine and 0.43g of NaCl were stirred and dissolved at 60°C for 3 hours, then filtered, and the filtrate was dried under reduced pressure to remove the solvent, and then passed through NaCl was removed by washing with water, and 3.2 g of chitin was obtained by drying. The HPLC...

Embodiment 2

[0042] (1) Decalcification: after crushing 10g insect carapace, place it in 250g of dilute acid with a mass concentration of 15% and immerse it at 30°C for 6 hours, filter, take the filter cake and wash it with water for 3-5 times to obtain 7.8g of decalcification. product A;

[0043] (2) Deproteinization: put 7.8g of decalcified product A, 0.12g of trypsin, 0.12g of papain, 0.24g of alkaline lipase and 78g of water in a three-necked flask, control the pH of the reaction solution to 8, and stir at 50°C After being hydrolyzed for 2.5 hours, filtered, the filter cake was washed with water and dried to obtain 5.1 g of deproteinized product B;

[0044] (3) Purification: 5.1 g of deproteinized product B, 40 g of hexanoic acid, 32 g of oxalic acid, 20 g of pyridine and 1 g of MgSO 4 After stirring and dissolving at 70 °C for 2 hours, the filtrate was filtered, and the filtrate was dried under reduced pressure to remove the solvent, and then washed with water to remove MgSO 4 , 3.8...

Embodiment 3

[0050] (1) Decalcification: After crushing 10g insect carapace, place it in 300g of dilute acid with a mass concentration of 20% and immerse it at 40°C for 5 hours, filter, wash the filter cake with water for 3-5 times and dry to obtain 6.9g of decalcification product A;

[0051] (2) Deproteinization: Place 6.9g of decalcified product A, 0.14g of trypsin, 0.14g of papain, 0.28g of alkaline lipase and water in a three-necked flask, control the pH of the reaction solution to be 8.5, and stir and hydrolyze at 55°C After 2 hours, filter, wash and dry the filter cake to obtain 4.6 g of deproteinized product B;

[0052] (3) Purification: 4.6 g of deproteinized product B, 40 g of hexanoic acid, 32 g of oxalic acid, 20 g of pyridine and 1.4 g of Na 2 SO 4 After stirring and dissolving at 80 °C for 1 hour, the filtrate was filtered, and the filtrate was dried under reduced pressure to remove the solvent, and then washed with water to remove Na 2 SO 4 , 3.5g of chitin was obtained b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention provides a preparation method of chitosan microspheres. The preparation method comprises steps as follows: calcium removal with insect carapace diluted acid, deproteinization through compound enzymes, dissolution and purification of a mixed solvent, deacetylation of weak base through ultraviolet light and emulsification crosslinking, and the chitosan microspheres are prepared with the method. Chitosan prepared with the method has high purity, high degree of deacetylation and large molecular weight, the size of the chitosan microspheres prepared from chitosan ranges from 210 mu m to 400 mu m, the deviation is lower than 15%, and the application requirement of the chitosan microspheres in interventional therapy is met.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and in particular relates to a preparation method of chitosan microspheres. Background technique [0002] Chitosan, also known as deacetylated chitin, soluble chitin and polyglucosamine, its chemical name is β-(1→4)-2-amino-2-deoxy-D-glucose, after chitin is treated with concentrated alkali The product obtained by removing the acetyl group. Chitosan has excellent biocompatibility and low toxicity, and can be dissolved and metabolized by lytic enzymes in the human body. [0003] Through the traditional way of administration, most of the drug ingredients are released very quickly, causing the drug level in the body to rise rapidly, reach a peak and then decrease rapidly. As for the drug, its effect is closely related to the concentration of the drug in the serum, and violent fluctuations often cause unacceptable side effects at the peak, and then insufficient therapeutic effect due to t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08J3/24C08J3/12C08J3/16C08B37/08A61K47/36C08L5/08
CPCA61K47/36C08B37/0003C08B37/003C08J3/12C08J3/16C08J3/24C08J2305/08
Inventor 倪协照
Owner 上海丽珠制药有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap