Environment-friendly inflaming-retarding non-cured rubber asphalt waterproof paint and preparing method thereof

A technology of asphalt waterproof coating and non-curing rubber, which is applied in the direction of asphalt coating, unspecified rubber coating, fireproof coating, etc. It can solve the problems of increasing the risk of hot melt construction, not having flame retardancy, and limiting the scope of application, etc., to achieve Good waterproof and flame retardant effects, convenient construction, and increased safety

Inactive Publication Date: 2017-01-04
天津市京建建筑防水工程有限公司
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, although the non-curing asphalt coatings currently on the market have good waterproof effects, they do not have flame-retardant properties, which limits their application range, increases the risk of hot-melt construction, and increases the risk of building fires. Sexuality, causing huge losses to human material property, but also destroying the surrounding environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly inflaming-retarding non-cured rubber asphalt waterproof paint and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] An environmentally friendly flame-retardant non-curing rubber asphalt waterproof coating, comprising the following components in parts by weight: 80 parts of natural asphalt, 60 parts of rubber powder, 60 parts of rosin resin, 60 parts of acrylic polymer, and 30 parts of thermoplastic styrene-butadiene rubber , Solvent: 25 parts of colloidal oil, 25 parts of soybean oil, 20 parts of paraffin oil, 30 parts of attapulgite, 30 parts of cellulose, adhesion promoter: 5 parts of aldehyde and ketone resin, 5 parts of polystyrene butadiene rubber , 5 parts of neoprene, binder: 5 parts of modified polyacrylate, 5 parts of acrylonitrile polymer, 5 parts of polystyrene-acrylate, light stabilizer: 7.5 parts of benzophenone, methyl salicylate 7.5 parts of ester, composite flame retardant: 10 parts of triphenyl phosphate, 10 parts of ammonium polyphosphate, 10 parts of decabromodiphenylethane, 10 parts of zinc borate.

[0022] The present invention also provides a preparation method ...

Embodiment 2

[0027] An environmentally friendly flame-retardant non-curing rubber asphalt waterproof coating, comprising the following components in parts by weight: 70 parts of natural asphalt, 70 parts of rubber powder, 50 parts of rosin resin, 50 parts of acrylic polymer, and 40 parts of thermoplastic styrene-butadiene rubber , Solvent: 30 parts of colloidal oil, 30 parts of soybean oil, 40 parts of attapulgite, 20 parts of cellulose, adhesion promoter: 10 parts of polystyrene butadiene rubber, 10 parts of neoprene, binder: 10 parts of polystyrene-acrylate, 10 parts of polyvinyl butyral resin, light stabilizer: 10 parts of benzophenone, 10 parts of methyl salicylate, composite flame retardant: 10 parts of ammonium polyphosphate, ten parts Bromodiphenylethane 10 parts, zinc borate 10 parts.

[0028] The present invention also provides a preparation method of the above-mentioned environmentally friendly flame-retardant non-curing rubber asphalt waterproof coating, comprising the following...

Embodiment 3

[0033] An environmentally friendly flame-retardant non-curing rubber asphalt waterproof coating, comprising the following components in parts by weight: 90 parts of natural asphalt, 50 parts of rubber powder, 60 parts of rosin resin, 70 parts of acrylic polymer, and 40 parts of thermoplastic styrene-butadiene rubber , Solvent: 45 parts of soybean oil, 45 parts of paraffin oil, 20 parts of attapulgite, 20 parts of cellulose, adhesion promoter: 10 parts of aldehyde and ketone resin, binder: 10 parts of modified polyacrylate, acrylonitrile polymer 5 parts, light stabilizer: 10 parts of benzophenone, 10 parts of methyl salicylate, composite flame retardant: 20 parts of ammonium polyphosphate, 20 parts of decabromodiphenylethane.

[0034] The present invention also provides a preparation method of the above-mentioned environmentally friendly flame-retardant non-curing rubber asphalt waterproof coating, comprising the following steps:

[0035] (1) Weigh each component by parts by we...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides environment-friendly inflaming-retarding non-cured rubber asphalt waterproof paint and belongs to the technical field of waterproofing of building. The paint is prepared from, by weight, 60-100 parts of natural asphalt, 20-80 parts of rubber powder, 20-80 parts of rosin resin, 20-80 parts of acrylic polymer, 10-40 parts of thermoplastic styrene-butadiene rubber, 40-100 parts of solvent, 10-40 parts of attapulgite, 10-40 parts of cellulose, 5-20 parts of adhesion promoter, 5-20 parts of binder, 5-20 parts of light stabilizer and 20-60 parts of composite flame retardant. The paint will never be solidified, and the content of condensate is higher than 99.9%; volatile matter can hardly be generated, and environment friendliness is realized; durability, fatigue resistance and extensibility are high; the paint can be bonded with any foreign matter; flexibility is high, automatic restoration can be achieved after building deformation, and self-healing property is high; adhesive force is high, cracking is avoided, and peeling is avoided; construction is convenient; the paint can be used independently and can also be used by being mixed with other types of solvent and paint; waterproof and inflaming-retarding effects are good; using safety of the paint is improved.

Description

technical field [0001] The invention relates to the technical field of building waterproofing, in particular to an environmentally friendly flame-retardant non-curing rubber asphalt waterproof coating. Background technique [0002] Non-curing rubber asphalt waterproof coating has the characteristics of low temperature resistance, high temperature non-dripping, never curing, excellent creep performance, etc., especially when dealing with defects such as building deformation joints and displacement joints, it has a good waterproof effect. Therefore, non-curing rubber asphalt waterproof coatings have been widely promoted and applied in the field of building waterproofing in recent years. However, although the non-curing asphalt coatings currently on the market have good waterproof effects, they do not have flame-retardant properties, which limits their application range, increases the risk of hot-melt construction, and increases the risk of building fires. Sex, causing huge lo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D195/00C09D121/00C09D193/04C09D133/00C09D153/02C09D101/02C09D5/18C09D7/12
CPCC08L2201/02C08L2205/035C09D5/18C09D121/00C09D195/00C08L21/00C08L93/04C08L33/00C08L53/02C08L1/02C08K13/02C08K3/346C08K5/523C08K2003/323C08K5/03C08K2003/387C08L95/00
Inventor 卢杏哲
Owner 天津市京建建筑防水工程有限公司