A preparation method of fluorescent transparent magnetic wood

A magnetic wood and transparent technology, applied in wood treatment, wood heating, impregnating wood, etc., can solve the problems of non-magnetism, non-fluorescent performance, wood opacity, etc., and achieve the effect of suitable magnetic properties, excellent fluorescent performance, and simple operation

Inactive Publication Date: 2017-10-10
NORTHEAST FORESTRY UNIVERSITY
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention solves the problems of opaque, non-magnetic and non-fluorescent properties of existing wood, and provides a preparation method of fluorescent transparent magnetic wood

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A preparation method of fluorescent transparent magnetic wood
  • A preparation method of fluorescent transparent magnetic wood
  • A preparation method of fluorescent transparent magnetic wood

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0032] Specific embodiment 1: The method for preparing fluorescent transparent magnetic wood described in this embodiment is specifically carried out according to the following steps:

[0033] 1. Lignin removal from wood:

[0034] The wood with a thickness of 0.1mm-20mm is immersed in a reactor containing a sodium hypochlorite solution with a concentration of 0.1mol / L-10mol / L to obtain a reaction system, and then glacial acetic acid is added to adjust the pH of the reaction system to 1-7, and the reaction is sealed Place the reactor at a temperature of 70℃~200℃, cook for 1h~52h, cool to room temperature, and then add hydrogen peroxide with a concentration of 0.1mol / L~10mol / L to the reactor at a temperature of 70 Under the condition of ℃~200℃, continue to cook for 1h~52h, cool to room temperature, take out the reacted wood, under the condition of 50℃~200℃, vacuum dry the reacted wood for 1h~52h to get stripped Lignin wood

[0035] The volume ratio of the hydrogen peroxide solution w...

specific Embodiment approach 2

[0055] Specific embodiment two: this embodiment is different from specific embodiment one in that the wood described in step one is coniferous or hardwood. Others are the same as the first embodiment.

specific Embodiment approach 3

[0056] Specific embodiment three: The difference between this embodiment and specific embodiment one or two is: the content of Fe described in step two ④ 3+ The salt is ferric chloride, ferric sulfate or ferric nitrate; the step 2 ④ contains Fe 2+ The salt is ferrous chloride, ferrous sulfate or ferrous nitrate. Others are the same as the first or second embodiment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
transmittivityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a manufacturing method for fluorescent transparent magnetic wood. The manufacturing method for the fluorescent transparent magnetic wood aims to solve the problems that existing wood is not transparent and does not have magnetism or the fluorescence property. The manufacturing method for the fluorescent transparent magnetic wood comprises the steps that firstly, lignin of wood is eliminated; secondly, fluorescent magnetic nanoparticles are prepared; and thirdly, the fluorescent transparent magnetic wood is manufactured and obtained. The method is used for manufacturing the fluorescent transparent magnetic wood.

Description

Technical field [0001] The invention relates to a preparation method of fluorescent transparent magnetic wood. Background technique [0002] As a material for industry and life, wood is closely related to the construction of the national economy and human life, and has many excellent qualities. However, as a biomass material, wood does not have transparency, magnetism, and fluorescence properties. Nowadays, with the development of materials science, materials with a single function can no longer meet the requirements of social production, and multi-functional and new-type biomass materials have increasingly shown broad application prospects, and are concerned by scientific researchers worldwide. Summary of the invention [0003] The invention aims to solve the problems of opaque, non-magnetic, and non-fluorescent properties of existing wood, and provides a method for preparing fluorescent transparent magnetic wood. [0004] A method for preparing fluorescent transparent magnetic w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B27K3/02B27K3/50B27K3/32B27K3/08B27K5/04B27K5/00
CPCB27K3/02B27K3/08B27K3/32B27K3/50B27K5/001B27K5/0075B27K5/04
Inventor 李坚甘文涛高丽坤詹先旭肖少良高汝楠
Owner NORTHEAST FORESTRY UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com