Wear resistant paint mortar and preparing method thereof

Abstract

The invention claims wear resistant paint mortar and a preparing method thereof. The wear resistant paint mortar is prepared from, by weight, 30- 40 parts of refined raw lacquer, 25- 35 parts of glass powder, 20- 25 parts of ox horn powder,15- 22 parts of pebble powder, 5- 12 parts of sand powder, 5- 8 parts of laminated rock powder, and 8- 12 parts of adhesive;The preparing procedures are as follows:(1) the preparing of mixed powder; (2) mixing. The wear resistant paint mortar adopts fungal enzyme for refining processing of raw lacquer, and the rheological property of the raw lacquer can be effectively adjusted. The produced paint mortar has strong adhesion and high hardness together with corrosion-resistant and wear-resistant.It is easy to be smeared on the wood embryo to effectively improve the hardness and strength of wood and to fill the holes as well as the gaps on the board also improves the wear resistantce of the board.

Description

technical field [0001] The invention relates to the field of lacquer painting production, in particular to a wear-resistant paint mortar and a preparation method thereof. Background technique [0002] In the process of making lacquer paintings, lacquer painting boards are one of the basic raw materials for making lacquer paintings. Lacquer painting boards, commonly known as lacquer boards, are the fetal bones of lacquer paintings. Metal plates and fiberboards can be used instead, while tire boards can only be used after being treated with cloth, paint scraping, painting and other processes. Scraping paint ash is a very important step, because paint ash can not only cover holes, cracks, scratches, etc. on the surface of the lacquer carcass, fill up the defects, but also enhance the adhesion of the paint film to achieve The purpose of saving labor and materials, and the paint ash layer is also conducive to the subsequent molding processes such as grinding and scraping, which ...

AI Technical Summary

Problems solved by technology

This kind of paint ash generally has the general lack of adhesion, and the composition is single, the preparation process is simple, and the finished paint ash prepared has low adhesion and cannot well fill and smooth the holes and gaps on the wooden board. Most of the lacquer ash has poor wear resistance, which is not conducive to the subsequent production of lacquer paintings