A technology of flame-retardant composite and urea-formaldehyde resin, which is applied in applications, household components, household appliances, etc., can solve the problems of inferior bonding strength and flame retardancy, and achieve improved aging resistance, good film-forming properties, and good freeze-thaw resistance. Effect

Inactive Publication Date: 2017-01-18
广西横县正林木业有限公司
View PDF13 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In the above-mentioned patent, the adhesive used in the production process of the cabinet board is a urea-formaldehyde resin adhesive modified by hydroxyacrylate resin (the purpose is to reduce the formaldehyde content), and a PPU flame retardant

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for producing cabinet board by adopting flame-retardant composite urea resin

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0066] Example 1

[0067] The method of using flame-retardant composite urea-formaldehyde resin to produce cabinet board, the cabinet board structure from top to bottom is: decorative paper, fir veneer, particle board, back board; the cabinet board is surrounded by aluminum alloy; The particleboard is coated with a flame-retardant composite urea-formaldehyde resin adhesive, the particleboard and the backboard are coated with a flame-retardant composite urea-formaldehyde resin adhesive, and the particleboard in the cabinet board also uses a flame-retardant composite urea-formaldehyde resin adhesive; the specific steps include :The preparation of particleboard, the process of applying glue and covering particleboard to the veneer of fir and backboard, and decorating.

[0068] The preparation process of the particle board is:

[0069] 1) The waste material that cannot be used in the process of making multi-layer eucalyptus boards after the peeling of eucalyptus boards is simply screene...

Example Embodiment

[0096] Example 2

[0097] The method of using flame-retardant composite urea-formaldehyde resin to produce cabinet board, the cabinet board structure from top to bottom is: decorative paper, fir veneer, particle board, back board; the cabinet board is surrounded by aluminum alloy; The particleboard is coated with a flame-retardant composite urea-formaldehyde resin adhesive, the particleboard and the backboard are coated with a flame-retardant composite urea-formaldehyde resin adhesive, and the particleboard in the cabinet board also uses a flame-retardant composite urea-formaldehyde resin adhesive; the specific steps include :The preparation of particleboard, the process of applying glue and covering particleboard to the veneer of fir and backboard, and decorating.

[0098] The preparation process of the particle board is:

[0099] 1) The waste material that cannot be used in the process of making multi-layer eucalyptus boards after the peeling of eucalyptus boards is simply screene...

Example Embodiment

[0126] Example 3

[0127] The method of using flame-retardant composite urea-formaldehyde resin to produce cabinet board, the cabinet board structure from top to bottom is: decorative paper, fir veneer, particle board, back board; the cabinet board is surrounded by aluminum alloy; The particleboard is coated with a flame-retardant composite urea-formaldehyde resin adhesive, the particleboard and the backboard are coated with a flame-retardant composite urea-formaldehyde resin adhesive, and the particleboard in the cabinet board also uses a flame-retardant composite urea-formaldehyde resin adhesive; the specific steps include :The preparation of particleboard, the process of applying glue and covering particleboard to the veneer of fir and backboard, and decorating.

[0128] The preparation process of the particle board is:

[0129] 1) The waste material that cannot be used in the process of making multi-layer eucalyptus boards after the peeling of eucalyptus boards is simply screene...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to home building materials, in particular to a method for producing a cabinet board by adopting flame-retardant composite urea resin. The cabinet board structurally comprises decorative paper, a cunninghamia lanceolata veneer, a shaving board and a back board from top to bottom, wherein the periphery of the cabinet board is edged with aluminium alloy; a flame-retardant composite urea resin adhesive is applied between the cunninghamia lanceolata veneer and the shaving board; a flame-retardant composite urea resin adhesive is applied between the shaving board and the back board; a flame-retardant composite urea resin adhesive is also adopted for the shaving board in the cabinet board. The cabinet board manufactured by the method has the advantages of strong water resistance, high bonding strength, low formaldehyde residue and a flame-retardant function. The shaving board in production of the cabinet board is made of waste materials and leftover materials which can not be utilized in the process of manufacturing a multilayered eucalyptus board after rotary cutting of eucalyptus boards, and the leftover materials are utilized, so that the woods can be saved and the production cost of an enterprise can be reduced.

Description

technical field [0001] The invention relates to a home building material, in particular to a method for producing a cabinet board by using a flame-retardant composite urea-formaldehyde resin. Background technique [0002] As the saying goes, "Poor is better than a living room, richer than a kitchen". As the "finishing touch" of kitchen decoration, cabinet boards are paid more attention to. At present, the cabinet boards on the market also use particleboard as the core board, and particleboard is an important board type in wood-based panels. Compared with other board types, its production investment is relatively small, energy consumption is small, and cost is low. The requirements are not high, and the three leftovers, fast-growing wood, recycled waste wood and some non-wood materials can be used as raw materials for particleboard. Therefore, the development of particleboard industry in China, which is scarce in wood resources, has its unique advantages. The interior of th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A47B96/20C09J161/32C09J103/10C09J11/08C09J11/06B27N3/02B27N3/14B27N3/10
CPCA47B96/206A47B2220/0091B27N3/02B27N3/10B27N3/143C08L2201/02C08L2201/10C08L2205/035C09J11/06C09J11/08C09J161/32C08L3/10C08L71/02C08L93/04C08L29/04C08L97/005
Inventor 陈姗姗
Owner 广西横县正林木业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap